Natural fibre-reinforced polymer matrix composites are gaining increased attention among the researchers due to their low density, biodegradability, abundance, good mechanical properties, etc. Significant amount of research works can be found on the material characterisation of natural fibres like hemp, flax, sisal, kenaf, coir and jute and their composites based on the polymer matrices. Natural fibres are hydrophilic in nature and exhibit poor interfacial adhesion between fibre and matrix. Modification of the fibre surface by chemical methods, such as alkalisation, benzoylation and acetylation, has been used by researchers to improve the above-mentioned shortcomings. This review paper focuses on the effect of alkali treatment on the material properties of various natural fibres and their composites along with their water absorption behaviour.

Fused Deposition Modeling (FDM) is capable of producing complicated geometries and a variety of thermoplastic or composite products. Thus, it is critical to carry out the relationship between the process parameters, the finished part’s quality, and the part’s mechanical performance. In this study, the optimum printing parameters of FDM using oil palm fiber reinforced thermoplastic composites were investigated. The layer thickness, orientation, infill density, and printing speed were selected as optimization parameters. The mechanical properties of printed specimens were examined using tensile and flexural tests. The experiments were designed using a Taguchi experimental design using a L₉ orthogonal array with four factors, and three levels. Analysis of variance (ANOVA) was used to determine the significant parameter or factor that influences the responses, including tensile strength, Young’s modulus, and flexural strength. The fractured surface of printed parts was investigate using scanning electron microscopy (SEM). The results show the tensile strength of the printed specimens ranged from 0.95 to 35.38 MPa, the Young’s modulus from 0.11 to 1.88 GPa, and the flexural strength from 2.50 to 31.98 MPa. In addition, build orientation had the largest influence on tensile strength, Young’s modulus, and flexural strength. The optimum printing parameter for FDM using oil palm fiber composite was 0.4 mm layer thickness, flat (0 degree) of orientation, 50% infill density, and 10 mm/s printing speed. The results of SEM images demonstrate that the number of voids seems to be much bigger when the layer thickness is increased, and the flat orientation has a considerable influence on the bead structure becoming tougher. In a nutshell, these findings will be a valuable 3D printing dataset for other researchers who utilize this material.

Today, additive manufacturing (AM) is the most recent technology used to produce detailed and complexly built parts for a variety of applications. The most emphasis has been given to fused deposition modeling (FDM) in the development and manufacturing fields. Natural fibers have received attention in the area of 3D printing to be employed as bio-filters with thermoplastics, which have prompted an effort for more ecologically acceptable methods of manufacturing. The development of natural fiber composite filaments for FDM requires meticulous methods and in-depth knowledge of the properties of natural fibers and their matrices. Thus, this paper reviews natural fiber-based 3D printing filaments. It covers the fabrication method and characterization of thermoplastic materials blended with natural fiber-produced wire filament. The characterization of wire filament includes the mechanical properties, dimension stability, morphological study, and surface quality. There is also a discussion of the difficulties in developing a natural fiber composite filament. Last but not least, the prospects of natural fiber-based filaments for FDM 3D printing are also discussed. It is hoped that, after reading this article, readers will have enough knowledge regarding how natural fiber composite filament for FDM is created.

Physical, mechanical, chemical, and thermal properties of sugar palm (Arenga pinnata) fiber were investigated for specimens obtained from three different locations: Kuala Jempol (Peninsular Malaysia), Tawau (West Malaysia), and Tasik Malaya (Indonesia). The morphology of the fiber were observed through scanning electron microscopy (SEM), the thermal properties by thermogravimetric analysis (TGA), tensile properties according to ASTM D3379, and chemical analysis by using neutral detergent fiber (NDF) and acid detergent fiber (ADF). This study confirmed that in sugar palm fiber, the highest chemical content of cellulose resulted in the highest strength and thermal stability of the fiber. Fiber originating from Kuala Jempol had the highest cellulose content of 44.53%, followed by Indonesia (44.47%) and Tawau (43.75%). Kuala Jempol fiber (233.28 MPa) also had the highest tensile strength, followed by Indonesia (211.03 MPa) and Tawau (201.30 MPa), which was affected by the cellulose content in the fiber. Thus, fiber originating from Kuala Jempol had better quality than the others as a reinforcement material in manufacturing of polymer composites.

Fiber composites are known to have poor through-thickness mechanical properties due to the absence of a Z-direction binder. This issue is more critical with the use of natural fibers due to their low strength compared to synthetic fibers. Stitching is a through-thickness toughening method that is used to introduce fibers in the Z-direction, which will result in better through-thickness mechanical properties. This research was carried out to determine the mechanical properties of unstitched and silk fiber-stitched woven kenaf-reinforced epoxy composites. The woven kenaf mat was stitched with silk fiber using a commercial sewing machine. The specimens were fabricated using a hand lay-up method. Three specimens were fabricated, one unstitched and two silk-stitched with deferent stitching orientations. The results show that the stitched specimens have comparable in-plane mechanical properties to the unstitched specimens. For the tensile mechanical test, stitched specimens show similar and 17.1% higher tensile strength compared to the unstitched specimens. The flexural mechanical test results show around a 9% decrease in the flexural strength for the stitched specimens. On the other hand, the Izod impact mechanical test results show a significant improvement of 33% for the stitched specimens, which means that stitching has successfully improved the out-of-plane mechanical properties. The outcome of this research indicates that the stitched specimens have better mechanical performance compared to the unstitched specimens and that the decrease in the flexural strength is insignificant in contrast with the remarkable enhancement in the impact strength.