This research was set out to explore the development of arrowroot starch (AS) films using glycerol (G) as plasticizer at the ratio of 15, 30, and 45% (w/w, starch basis) using solution casting technique. The developed films were analyzed in terms of physical, structural, mechanical, thermal, environmental, and barrier properties. The incorporation of glycerol to AS film-making solution reduced the brittleness and fragility of films. An increment in glycerol concentration caused an increment in film thickness, moisture content, and solubility in water, whereas density and water absorption were reduced. The tensile strength and modulus of G-plasticized AS films were reduced significantly from 9.34 to 1.95 MPa and 620.79 to 36.08 MPa, respectively, while elongation at break was enhanced from 2.41 to 57.33%. FTIR analysis revealed that intermolecular hydrogen bonding occurred between glycerol and AS in plasticized films compared to control films. The G-plasticized films showed higher thermal stability than control films. The cross-sectional micrographs revealed that the films containing 45% glycerol concentration had higher homogeneity than 15% and 30%. Water vapour permeability of plasticized films increased by an increase in glycerol concentrations. The findings of this research provide insights into the development of bio-degradable food packaging.

Over recent years, enthusiasm towards the manufacturing of biopolymers has attracted considerable attention due to the rising concern about depleting resources and worsening pollution. Among the biopolymers available in the world, polylactic acid (PLA) is one of the highest biopolymers produced globally and thus, making it suitable for product commercialisation. Therefore, the effectiveness of natural fibre reinforced PLA composite as an alternative material to substitute the non-renewable petroleum-based materials has been examined by researchers. The type of fibre used in fibre/matrix adhesion is very important because it influences the biocomposites’ mechanical properties. Besides that, an outline of the present circumstance of natural fibre-reinforced PLA 3D printing, as well as its functions in 4D printing for applications of stimuli-responsive polymers were also discussed. This research paper aims to present the development and conducted studies on PLA-based natural fibre bio-composites over the last decade. This work reviews recent PLA-derived bio-composite research related to PLA synthesis and biodegradation, its properties, processes, challenges and prospects.

In the field of hybrid natural fiber polymer composites, there has been a recent surge in research and innovation for structural applications. To expand the strengths and applications of this category of materials, significant effort was put into improving their mechanical properties. Hybridization is a designed technique for fiber-reinforced composite materials that involves combining two or more fibers of different groups within a single matrix to manipulate the desired properties. They may be made from a mix of natural and synthetic fibers, synthetic and synthetic fibers, or natural fiber and carbonaceous materials. Owing to their diverse properties, hybrid natural fiber composite materials are manufactured from a variety of materials, including rubber, elastomer, metal, ceramics, glasses, and plants, which come in composite, sandwich laminate, lattice, and segmented shapes. Hybrid composites have a wide range of uses, including in aerospace interiors, naval, civil building, industrial, and sporting goods. This study intends to provide a summary of the factors that contribute to natural fiber-reinforced polymer composites’ mechanical and structural failure as well as overview the details and developments that have been achieved with the composites.

The use of starch based films as a potential alternative choice to petroleum derived plastics is imperative for environmental waste management. This study presents a new biopolymer (sugar palm starch) for the preparation of biodegradable packaging films using a solution casting technique. The effect of different plasticizer types (glycerol (G), sorbitol (S) and glycerol-sorbitol (GS) combination) with varying concentrations (0, 15, 30 and 45, w/w%) on the tensile, thermal and barrier properties of sugar palm starch (SPS) films was evaluated. Regardless of plasticizer types, the tensile strength of plasticized SPS films decreased, whereas their elongation at break (E%) increased as the plasticizer concentrations were raised. However, the E% for G and GS-plasticized films significantly decreased at a higher plasticizer concentration (45% w/w) due to the anti-plasticization effect of plasticizers. Change in plasticizer concentration showed an insignificant effect on the thermal properties of S-plasticized films. The glass transition temperature of SPS films slightly decreased as the plasticizer concentration increased from 15% to 45%. The plasticized films exhibited increased water vapor permeability values from 4.855 × 10⁻¹⁰ to 8.70 × 10⁻¹⁰ g·m⁻¹·s⁻¹·Pa⁻¹, irrespective of plasticizer types. Overall, the current study manifested that plasticized sugar palm starch can be regarded as a promising biopolymer for biodegradable films.