ZnO particles were synthetized by the sol–gel method and subsequent heat treatment of 400, 500 and 600 °C was applied. The nano ZnO particles were incorporated to the unsaturated polyester resin by solution blending at 0.05 wt % concentration. X-ray diffraction detected the formation of a wurtzite-like structure. Viscoelastic behavior of neat polyester and nanocomposites revealed the nano ZnO particles does not promote better mechanical properties because of a weak interaction and the glass transition temperature of the polyester was favored by the presence of a higher quantity of nano-size ZnO particles. Thermogravimetric analysis at 5, 10 and 20 °C/min allowed determining the degradation kinetic parameters based on the Friedman and Kissinger models for neat polyester and nanocomposites. Heating rates promoted an increase in the temperature degradation and the addition of ZnO particles promoted a catalyst effect that reduce the amount of thermal energy needed to start the thermal degradation.

Amorphous carbon nitride films with N/C ratios ranging from 2.24 to 3.26 were deposited by reactive sputtering at room temperature on corning glass, silicon, and quartz as substrates. The average chemical composition of the films was obtained from the semiquantitative energy dispersive spectroscopy analysis. Photoluminescence measurements were performed to determine the optical band gap of the films. The photoluminescence spectra displayed two peaks: one associated with the substrate and the other associated withCNxfilms located at ≈2.13±0.02 eV. Results show an increase in the optical band gap from 2.11 to 2.15 eV associated with the increase in the N/C ratio. Raman spectroscopy measurements showed a dominantDband.ID/IGratio reaches a maximum value for N/C ≈ 3.03 when the optical band gap is 2.12 eV. Features observed by the photoluminescence and Raman studies have been associated with the increase in the carbon sp²/sp³ratio due to presence of high nitrogen content.