The article deals with determining of fatigue lifetime of structural materials during by multiaxial cyclic loading. The theoretical part focuses on fatigue and criterions for evaluation of the multiaxial fatigue lifetime. The experimental part deals with modeling of combined bending -torsion loading and determining the number of cycles to fracture in region low-cycle fatigue and also during of the loading with the sinusoidal wave form under in phase φ = 0°. Based on the experimental results the fatigue design curves are compared to fatigue data from base metal and weldments

Secondary-cast aluminum alloys have increasing industrial applications. Their biggest deficiency is their impurity content, especially Fe, which has low solubility in Al and almost all the content creates intermetallic phases. This work examines the effect of higher Fe content on the microstructure and properties of A356.0 alloy. At the same time, no other possibility existed to affecting the brittleness of the formation of the β phases. The calculation of Fe_crit, ratio of Mn/Fe, quantitative and computed tomography analysis of porosity and Fe plate-like phases, measurement of mechanical and fatigue properties, and fractography analysis were performed in this study. The results show that gravity die casting into a sand mold, and the non-usage of Mn addition or heat treatment, do not have a negative effect on increasing the size of the Fe-rich plate-like phases. The longest Fe-rich phases have limited the pore growth and ratios, but their higher thickness led to greater porosity formation. The mechanical and fatigue properties correlate with the Fe_crit level and the highest were for the experimental alloy with 0.454 wt.% of Fe. The experimental results confirmed the fact that if the Fe plate-like phases have a length of up to 50 µm, the fatigue properties depend more on the size of porosity. If the length of the Fe needles is more than 50 µm, then the properties are mainly affected by the length of these Fe phases.

Corrosion resistance of sensitized austenitic stainless steel (SS) in chloride environments is currently the subject of numerous studies. Most of them are focused on neutral chloride solutions at room temperature and the experiments are carried out on ground stainless steels surfaces. This paper deals with the corrosion behavior of sensitized AISI 304 stainless steel in acid 1 M chloride solution (pH = 1.1) at the temperatures of 20 ± 3 °C and 50 °C. The specimens after sensitization are tested as covered by high-temperature surface oxides (“heat tinted”), and also after their chemical removal to assess the impact of the surface state on corrosion resistance. Potentiodynamic polarization (PP) and exposure immersion test are used as the independent corrosion tests. Microstructure before/after exposure immersion test is evaluated by optical microscopy (OM) and SEM. The results obtained showed that sensitization significantly conditions corrosion regardless of the removal of high-temperature oxides, and the elevated temperature mainly acts as its accelerating factor.

Due to the combination of high corrosion resistance and suitable mechanical properties, AISI 316L stainless steel is extensively used as the biomaterial for surgical implants. However, heat exposure in inappropriate temperatures can cause its sensitization accompanied by chromium depletion along the grain boundaries. This study deals with an assessment of the susceptibility of sensitized AISI 316L biomaterial to pitting under conditions simulating the internal environment of the human body (Hank’s balanced salt solution, 37 ± 0.5 °C). The resistance to pitting corrosion is tested by the potentiodynamic polarization and by the 50-day exposure immersion test. Corrosion damage after the exposure immersion test is evaluated in the specimens’ cross-sections by optical microscope and SEM. Despite passive behavior in potentiodynamic polarization and shallow, slight corrosion damage observed after exposure, the sensitized AISI 316L biomaterial could represent a risk, especially in long-term implantation even after the chemical removal of high-temperature oxides.

Concerning the use of modern technologies and manufacturing systems in the production of high-stress components from Ni-base superalloys and the optimization of the production process, knowledge of the microstructure–mechanical properties relationship is very important. The microstructure of Ni-base superalloys is very closely related to the chemical composition. With the high number of alloying elements, various phases are presented in the structure of Ni-base superalloys, which have a predominantly positive effect on the mechanical properties, but also phases that reduce, in particular, the heat resistance of these materials. The aim of the presented paper is the quantification of structural parameters of two types of cast alloys, ZhS6K and IN738, where the effect of dwell at 10 and 15 h at 800 °C on the change in morphology and volume fraction of the γ′-phase precipitate was studied. The detected changes were verified by the Vickers hardness test. The IN718 superalloy was chosen as a representative of the wrought superalloy. This alloy was also annealed for 72 h at a temperature of 800 °C, and the quantification of structural parameters was performed by EDS mapping and TEM analysis. Another partial goal was to assess the effect of changes in the volume fraction of the γ′-phase and δ-phase on the change in the high-cycle fatigue life of superalloy IN 718. This superalloy was tested by dynamic cyclic loading with cycle asymmetry parameter R = −1 at an ambient temperature of 22 ± 5 °C and at a temperature of 700 ± 5 °C and with cycle asymmetry parameter R < 1 (three-point bending load) after annealing at 700 °C/72 h. The results of the quantitative analyses and fatigue tests will be further used in optimizing the design of Ni-base superalloy components by modern technologies such as additive technologies for the production of turbine blades and implemented within the philosophy of Industry 4.0.