Oil palm shell (OPS) is an agricultural solid waste from the extraction process of palm oil. All these wastes from industry pose serious disposal issues for the environment. This research aims to promote the replacement of conventional coarse aggregates with eco-friendly OPS aggregate which offers several advantages, such as being lightweight, renewable, and domestically available. This paper evaluates the mechanical and thermal performances of renewable OPS lightweight concrete (LWC) reinforced with various type of synthetic polypropylene (SPP) fibers. Monofilament polypropylene (MPS) and barchip polypropylene straight (BPS) were added to concrete at different volume fractions (singly and hybrid) of 0%, 0.1%, 0.3% and 0.4%. All specimens were mixed by using a new mixing method with a time saving of up to 14.3% compared to conventional mixing methods. The effects of SPP fibers on the mechanical properties were investigated by compressive strength, splitting tensile strength and residual strength. The strength of the oil palm shell lightweight concrete hybrid 0.4% (OPSLWC–HYB–0.4%) mixture achieved the highest compressive strength of 29 MPa at 28 days. The inclusion of 0.3% of BPS showed a positive outcome with the lowest thermal conductivity value at 0.55 W/m °C. Therefore, the results revealed that incorporation of BPS fiber enhanced the performance of thermal conductivity tests as compared to inclusion of MPS fiber. Hence, renewable OPS LWC was proven to be a highly recommended environmentally friendly aggregate as an alternative solution to replace natural aggregates used in the concrete industry.

The use of cement as a soil stabilization agent is one of the common solutions to enhancing the engineering properties of soil. However, the impact and cost of using cement have raised environmental concerns, generating much interest in the search for alternative materials to reduce the use of cement as a stabilizing agent in soil treatment. This study looked into limiting cement content in peat soil stabilization by using fly ash waste and polypropylene fiber (PPF). It focused on soil mechanical mediation for stabilization of peat with fly ash cement and PPF cement by comparing the mechanical properties, using unconfined compressive strength (UCS) and California bearing ratio (CBR) tests. The control (untreated) peat specimen and specimens with either fly ash (10%, 20% and 30%) and PPF (0.1%, 0.15% and 0.2%) were studied. Test results showed that 30% of fly ash and cement content displays the highest UCS and CBR values and gives the most reliable compressibility properties. On the other hand, UCS and CBR test results indicate optimum values of PPF–cement stabilizing agent content in the specimen of 0.15% PPF and 30% cement. Selected specimens were analyzed using scanning electron microscopy (SEM), and PPF threads were found to be well surrounded by cement-stabilized peat matrices. It was also observed that the specimen with 30% fly ash generated more hydration products when compared to the specimen with 100% cement content. It is concluded that the use of fly ash cement and PPF cement as stabilizing agents to limit the cement usage in peat soil treatment is potentially viable.

This research investigates the effect of pre-soaking treatment on plant-based aggregate using a wet grout binder to formulate a high-strength lightweight concrete (HSLWC). Surface modification utilising a novel grout soaking technique with various water-to-cement (w/c) ratios has indicated a new method of approach for the recent development of lightweight plant-based aggregate (LWPA). In this experiment, the fresh and hardened properties of modified LWPA lightweight concrete were assessed by verifying their workability, densities, compressive and split tensile strengths towards the modulus of elasticity. The results showed that pre-soaking plant-based lightweight aggregate (w/c: 0.6, 0.8, 1.0 and 1.2) slightly increased the density of the samples compared to untreated LWPA. The oven-dry density of treated and untreated LWPA is controlled in the range of HSLWC. The outcomes indicated that the workability of the surface-modified LWPA is significantly improved: up to 40% in 6 min for the (TDS)/0.6 sample compared to the original LWPA. The mechanical properties of the LWPA concrete with the surface modification method exhibit a substantial increment of compressive strength, split tensile strength and the modulus of elasticity; recorded at 22%, 26% and 34%, respectively. Significantly, the findings from this experiment reveal that the pre-soaking treatment method on LWPA is shown to be a highly recommended technique in improving interfacial bonding while maintaining its performance as one of the most promising solutions to improve the properties of lightweight concrete.

Conventional compressive strength test of concrete involves the destruction of concrete samples or existing structures. Thus, the focus of this research is to ascertain a more effective method to assess the compressive strength of concrete, especially during the hardening process. One of the prevalent non-destructive test (NDT) methods that involves the employment of elastic wave has been proposed to forecast the compressive strength development of air-entrained rubberized concrete. The change of the properties, such as wave amplitude, velocity and dominant frequency of the wave that propagates within the concrete is investigated. These wave parameters are then correlated with the compressive strength data, obtained using the conventional compressive strength test. It has been certified that both correlation between wave amplitude and concrete compressive strength, as well as the correlation between velocity and concrete compressive strength, have high regression degrees, which are 0.9404 and 0.8788, respectively. On the contrary, dominant wave frequency has been proved imprecise to be used to correlate with the concrete compressive strength development, as a low correlation coefficient of 0.2677 is reported. In a nutshell, the correlation data of wave amplitude and velocity could be used to forecast the compressive strength development of an air-entrained rubberized concrete in the future.

This study aims to investigate a new shear reinforcement method which utilizes thin mild steel (TMS) plates as shear reinforcement in deep beams to replace conventional reinforcement. Thirteen reinforced concrete deep beam specimens with three different plate thicknesses and four varying perforated hole arrangements on the TMS plates were experimentally tested to determine the load-carrying capacity and crack pattern. The experimental results indicate that the 2.0 mm thick TMS plate has the highest load-carrying capacity. Among the four different hole arrangements on the TMS plates, the perforated plates with a three-column hole arrangement show the best performance in terms of load-carrying capacity, with a 2.9% increment against the control beam specimen. The specimens also demonstrated compatible elastic stiffness with the control beam that used conventional shear links. This shows that TMS plates have the potential to replace conventional shear links in deep beams. This proposed method also changed the failure mode from conventional diagonal shear tension failure to a combination of flexural failure and shear deformation. A numerical model was developed and was found to have a good correlation with the experimental results, demonstrating potential for use in future parametric investigations on deep beams and cost reduction in future experimental work.

The ever-present environmental crises are current research hotspots. Nature-based solutions have been shown to have multiple co-benefits toward solving these crises. Plant-based coagulants are known to be a cost-effective and environmentally friendly approach for coagulation and flocculation processes for drinking-water treatment. In this study, a natural coagulant was extracted from Annona diversifolia seed, and its effectiveness was investigated for turbidity reduction using jar test in kaolin suspension, river water, and evaluation of factors for sludge dewatering. The characterisation studies of Annona diversifolia seed extract were carried out using techniques including Fourier-transform infrared spectroscopy (FTIR), zeta potential analyser, and transmission electron microscopy (TEM). Response surface methodology (RSM) was also performed for the optimisation study. The results from FTIR showed that Annona diversifolia seed extract contains carboxyl and hydroxyl functional groups. The charge density was found to be negative. A web-like structure surface morphology was observed from TEM. The optimum treatment settings were found to be at pH 3 and a dosage of 25 mg/L for water treatment, and 50 mg/L for sludge dewatering, which were comparable to the metal–salts coagulants. Annona diversifolia seed extract has been shown to be a good natural coagulant. Further research can be conducted to modify and enhance its performance.