Rice husk biochar was utilized to reinforce high-density polyethylene (HDPE) and to prepare biochar/plastic composites (BPC) by the extrusion method. Morphologies, non-isothermal crystallization behavior, and mechanical properties of the composites were investigated. The SEM (scanning electron microscope) showed that HDPE was embedded into the holes of the rice husk biochar. The DSC (differential scanning calorimeter) showed that biochar could reduce the crystallization rate and the higher the content of rice husk biochar, the slower the crystallization rate. Significantly, the bending and tensile strength of BPC could reach 53.7 and 20 MPa, far beyond WPC (wood plastic composites). With the increase of filler content, BPC were still stronger than WPC, although the impact strength of BPC and WPC all showed a general decline in the trend. The strong interaction was achieved by the utilization of rice husk biochar to reinforce HDPE.

In this study, rice husk biochar/high-density polyethylene (HDPE) composites were prepared via melt mixing followed by extrusion. Effects of biochar content and testing temperature on the dynamic mechanical analysis (DMA) of the composites were studied. Morphological analysis of the rice husk biochar and composites were evaluated by scanning electron microscopy (SEM). The results showed that biochar had a positive effect on dynamic viscoelasticity, creep resistance and stress relaxation properties of the composites, but the creep resistance and stress relaxation of the composites decreased with the increase of temperature. SEM analysis showed that HDPE components were embedded in the holes of the rice husk biochar, and it is believed that strong interaction was achieved.

Three dimensional (3D) printing materials were manufactured with polylactic acid (PLA) and poplar powder using the twin screw extruder and 3D printing consumables extruder. Lubricant (TPW604) and toughening agent polyolefin elastomer (POE) were utilized to improve the fluidity and toughness of the materials. 3D printing materials were tested by infrared spectroscopy, X-ray diffraction, melt flow rate, rheology behavior, impact and scanning electron microscope. The results show that the poplar powder could decrease impact strength of PLA, the same as TPW604. Unlike poplar powder, TPW604 can improve the fluidity of 3D printing materials. And POE can fill the voids formed by poplar powder in PLA, enhance interface compatibility between poplar powder and PLA, and effectively improve the fluidity and impact strength of 3D printing materials.

In this study, activated carbon microsphere (SLACM) was prepared from powdered sodium lignosulfonate (SL) and polystyrene by the Mannich reaction and ZnCl₂ activation, which can be used to remove Cr(VI) from the aqueous solution without adding any binder. The SLACM was characterized and the batch experiments were conducted under different initial pH values, initial concentrations, contact time durations and temperatures to investigate the adsorption performance of Cr(VI) onto SLACM. The results indicated that the SLACM surface area and average pore size were 769.37 m²/g and 2.46 nm (the mesoporous material), respectively. It was found that the reduced initial pH value, the increased temperature and initial Cr(VI) concentration were beneficial to Cr(VI) adsorption. The maximum adsorption capacity of Cr(VI) on SLACM was 227.7 mg/g at an initial pH value of 2 and the temperature of 40 °C. The adsorption of SLACM for Cr(VI) mainly occurred during the initial stages of the adsorption process. The adsorption kinetic and isotherm experimental data were thoroughly described by Elovich and Langmuir models, respectively. SL could be considered as a potential raw material for the production of activated carbon, which had a considerable potential for the Cr(VI) removal from wastewater.