This study shows mechanochemical synthesis as an alternative method to the traditional green synthesis of silver nanoparticles in a comparative manner by comparing the products obtained using both methodologies and different characterization methods. As a silver precursor, the most commonly used silver nitrate was applied and the easily accessible lavender (Lavandula angustofolia L.) plant was used as a reducing agent. Both syntheses were performed using 7 different lavender:AgNO₃ mass ratios. The synthesis time was limited to 8 and 15 min in the case of green and mechanochemical synthesis, respectively, although a significant amount of unreacted silver nitrate was detected in both crude reaction mixtures at low lavender:AgNO₃ ratios. This finding is of particular interest mainly for green synthesis, as the potential presence of silver nitrate in the produced nanosuspension is often overlooked. Unreacted AgNO₃ has been removed from the mechanochemically synthesized samples by washing. The nanocrystalline character of the products has been confirmed by both X-ray diffraction (Rietveld refinement) and transmission electron microscopy. The latter has shown bimodal size distribution with larger particles in tens of nanometers and the smaller ones below 10 nm in size. In the case of green synthesis, the used lavender:AgNO₃ ratio was found to have a decisive role on the crystallite size. Silver chloride has been detected as a side-product, mainly at high lavender:AgNO₃ ratios. Both products have shown a strong antibacterial activity, being higher in the case of green synthesis, but this can be ascribed to the presence of unreacted AgNO₃. Thus, one-step mechanochemical synthesis (without the need to prepare extract and performing the synthesis as separate steps) can be applied as a sustainable alternative to the traditional green synthesis of Ag nanoparticles using plants.

CdS nanoparticles were successfully synthesized using cadmium acetate and sodium sulfide as Cd and S precursors, respectively. The effect of using sodium thiosulfate as an additional sulfur precursor was also investigated (combined milling). The samples were characterized by XRD, Raman spectroscopy, XPS, UV-Vis spectroscopy, PL spectroscopy, DLS, and TEM. Photocatalytic activities of both CdS samples were compared. The photocatalytic activity of CdS, which is produced by combined milling, was superior to that of CdS, and was obtained by an acetate route in the degradation of Orange II under visible light irradiation. Better results for CdS prepared using a combined approach were also evidenced in photocatalytic experiments on hydrogen generation. The antibacterial potential of mechanochemically prepared CdS nanocrystals was also tested on reference strains of E. coli and S. aureus. Susceptibility tests included a 24-h toxicity test, a disk diffusion assay, and respiration monitoring. Bacterial growth was not completely inhibited by the presence of neither nanomaterial in the growth environment. However, the experiments have confirmed that the nanoparticles have some capability to inhibit bacterial growth during the logarithmic growth phase, with a more substantial effect coming from CdS nanoparticles prepared in the absence of sodium thiosulfate. The present research demonstrated the solvent-free, facile, and sustainable character of mechanochemical synthesis to produce semiconductor nanocrystals with multidisciplinary application.

In this study, a high entropy composite coating was synthesized by oxidizing a high entropy alloy, AlCrFeCoNi, at elevated temperatures in a pure oxygen atmosphere. X-Ray diffraction (XRD) analysis revealed that the prepared material was a dual-phase composite material consisting of a spinel-structured high entropy oxide and a metallic phase with a face-centered cubic structure. The metallic phase can improve the electrical conductivity of the oxide phase, resulting in improved electrochemical performance. Scanning electron microscopy with energy dispersive spectroscopy (SEM/EDS) analysis unveiled the compositional homogeneity of the composite material. The prepared material was utilized as an anode active material in lithium-ion batteries. Cyclic voltammetry (CV) revealed the oxidation and reduction regions, while the electrochemical impedance spectroscopy (EIS) measurements showed a decrease in the charge transfer resistance during the cycling process. A long-term rate capability test was conducted at various current densities: 100, 200, 500, 1000, and 2000 mA g⁻¹. During this test, a notable phenomenon was observed in the regeneration process, where the capacity approached the initial discharge capacity. Remarkably, a high regeneration efficiency of 98% was achieved compared with the initial discharge capacity. This phenomenon is typically observed in composite nanomaterials. At a medium current density of 500 mA g⁻¹, an incredible discharge capacity of 543 mAh g⁻¹ was obtained after 1000 cycles. Based on the results, the prepared material shows great potential for use as an anode active material in lithium-ion batteries.