The scope of additive manufacturing, particularly fused deposition modelling (FDM), can indeed be explored with the fabrication of multi-material composite laminates using this technology. Laminar composite structures made up of two distinct materials, namely acrylonitrile butadiene styrene (ABS) and carbon fiber reinforced polylactic acid (CF-PLA), were produced using the FDM process. The current study analyzes the effect of various printing parameters on the interfacial bond strength (IFBS) of the ABS/CF-PLA laminar composite by employing response surface methodology. The physical examination of the tested specimens revealed two failure modes, where failure mode 1 possessed high IFBS owing to the phenomenon of material patch transfer. Contrarily, failure mode 2 yielded low IFBS, while no patch transfer was observed. The analysis of variance (ANOVA) revealed that printing parameters were highly interactive in nature. After extensive experimentation, it was revealed that good quality of IFBS is attributed to the medium range of printing speed, high infill density, and low layer height. At the same time, a maximum IFBS of 20.5 MPa was achieved. The study presented an empirical relation between printing parameters and IFBS that can help in forecasting IFBS at any given printing parameters. Finally, the optimized printing conditions were also determined with the aim to maximize IFBS.

AISI 316L stainless steel (SS) is one of the extensively used biomaterials to produce implants and medical devices. It provides a low-cost solution with ample mechanical properties, corrosion resistance, and biocompatibility compared to its counterpart materials. However, the implants made of this material are subjected to a short life span in human physiological conditions leading to the leaching of metal ions, thus limiting its use as a biomaterial. In this research, the addition of boron, titanium, and niobium with varying concentrations in the SS matrix has been explored. This paper explores the impact of material composition on modified SS alloy’s physical and mechanical properties. The study’s outcomes specify that the microhardness increases for all the alloy compositions, with a maximum increase of 64.68% for the 2 wt.% niobium added SS alloy. On the other hand, the tensile strength decreased to 297.40 MPa for the alloy containing 0.25 wt.% boron and 2 wt.% titanium additions compared to a tensile strength of 572.50 MPa for pure SS. The compression strength increased from 776 MPa for pure SS to 1408 MPa for the alloy containing niobium and titanium additions in equal concentrations.

Together, 316L steel, magnesium-alloy, Ni-Ti, titanium-alloy, and cobalt-alloy are commonly employed biomaterials for biomedical applications due to their excellent mechanical characteristics and resistance to corrosion, even though at times they can be incompatible with the body. This is attributed to their poor biofunction, whereby they tend to release contaminants from their attenuated surfaces. Coating of the surface is therefore required to mitigate the release of contaminants. The coating of biomaterials can be achieved through either physical or chemical deposition techniques. However, a newly developed manufacturing process, known as powder mixed-electro discharge machining (PM-EDM), is enabling these biomaterials to be concurrently machined and coated. Thermoelectrical processes allow the migration and removal of the materials from the machined surface caused by melting and chemical reactions during the machining. Hydroxyapatite powder (HAp), yielding Ca, P, and O, is widely used to form biocompatible coatings. The HAp added-EDM process has been reported to significantly improve the coating properties, corrosion, and wear resistance, and biofunctions of biomaterials. This article extensively explores the current development of bio-coatings and the wear and corrosion characteristics of biomaterials through the HAp mixed-EDM process, including the importance of these for biomaterial performance. This review presents a comparative analysis of machined surface properties using the existing deposition methods and the EDM technique employing HAp. The dominance of the process factors over the performance is discussed thoroughly. This study also discusses challenges and areas for future research.

This article investigates the impact of manufacturing technology on the structure, mechanical, and tribological properties of new antifriction composite materials based on R6M5 high-speed tool steel grinding waste. The characteristics of the new composite’s structure formation and its impact on properties after use of the established technological modes, including grinding waste regeneration, were illustrated. It was demonstrated that such technology is capable of ensuring microheterogeneous structure. The material’s structure consists of the metal matrix based on R6M5 high-speed tool steel waste and uniformly distributed CaF₂ solid lubricant in the steel matrix. As compared to known iron-based composites, this structure promotes a high degree of mechanical and tribological properties. During tribological tests, anti-seize thin films of 15–20 μm are formed on the contacting surfaces. These constantly renewable films contribute to the high antifriction properties of the composite under the studied friction conditions and provide a self-lubricating effect. Such films fully cover both the material’s surface and the counterface. The formation of antifriction films results in the self-lubrication mode. The findings of the study open up the possibility of predicting the friction behavior of a composite at high temperatures by selecting the initial metal grinding waste to ensure the appropriate level of properties. The extensive use of various alloy steel-based industrial grinding waste in the re-production cycle would significantly contribute to resolving the global environmental problem of protecting the environment from pollution.

This study attempts to simultaneously machine and synthesize a biomimetic nanoporous hydroxyapatite coating on the Zr₆₇Cu₁₁Ni₁₀Ti₉Be₃ bulk metallic glass (BMG) surface. The aim is to investigate and optimize the hydroxyapatite deposition rate and the surface roughness during the electro-discharge coating of Zr₆₇Cu₁₁Ni₁₀Ti₉Be₃ BMG. Scanning Electron Microscopy (SEM), X-ray powder Diffraction (XRD) and Energy-dispersive X-ray Spectroscopy (EDS) were employed to characterize and analyze the results. Response Surface Methodology using D-optimum custom design approach was utilized to generate the models and optimize the input parameters. A globule nanostructured and nanoporous coating of about 25.2 µm thick, containing mainly Ca, O, and K were ascertained. Further XRD analysis confirmed the deposition of biocompatible oxides (HA, CaZrO₃, and ZrO₂) and hard ZrC coating on the Zr₆₇Cu₁₁Ni₁₀Ti₉Be₃ BMG surface. A significant improvement in cell viability was observed in the HA electro-discharge coated BMG specimens. The numerical models for the Hydroxyapatite Deposition Rate (HDR) and Surface Roughness (SR) were developed and experimentally validated using the optimized parameters setting suggested by the software. The achieved average predicted error of 4.94 and 5.09% for the HDR and SR respectively confirmed the excellent reproducibility of the developed models.

The powder metallurgy (PM) technique has been widely used for producing different alloy compositions by the addition of suitable reinforcements. PM is also capable of producing desireable mechanical and physical properties of the material by varying process parameters. This research investigates the addition of titanium and niobium in a 316L stainless steel matrix for potential use in the biomedical field. The increase of sintering dwell time resulted in simultaneous sintering and surface nitriding of compositions, using nitrogen as the sintering atmosphere. The developed alloy compositions were characterized using OM, FESEM, XRD and XPS techniques for quantification of the surface nitride layer and the nitrogen absorbed during sintering. The corrosion resistance and cytotoxicity assessments of the developed compositions were carried out in artificial saliva solution and human oral fibroblast cell culture, respectively. The results indicated that the nitride layer produced during sintering increased the corrosion resistance of the alloy and the developed compositions are non-cytotoxic. This newly developed alloy composition and processing technique is expected to provide a low-cost solution to implant manufacturing.