Variations in Moisture Content Affect the Shrinkage of Gigantochloa scortechinii and Bambusa vulgaris at Different Heights of the Bamboo Culm

In this study, the effect of superheated steam (SHS) treatment on the changes of the chemical composition and biological properties of two tropical hardwoods was investigated. SHS was carried out on light red meranti (Shorea spp.) and kedondong (Canarium spp.) wood with dimensions of 410 × 25 × 25 mm, using superheated steam as the heating medium. Wood samples were heat-treated at nine treatment levels, ranging from 172 to 228 °C and 95 to 265 min, respectively. The chemical constituents and resistance against white rot fungus (Pycnoporus sanguineus) and subterranean termite (Coptotermus curvignathus) of the treated wood were evaluated. A significant reduction in holocellulose content and increment in lignin was observed after SHS treatment. Consequently, the resistance against white rot fungus and termites improved. The biological durability improved with an increasing treatment temperature and time. A regression analysis revealed that the reduced equilibrium moisture content imparted superior biological resistance to the treated wood. Weight loss caused by the thermal degradation also served as a good indicator for fungal decay, as the loss of weight was directly proportional to the improvement in fungal resistance. However, this did not apply to termite resistance, as a very weak relationship was found between the two variables.

Eucalyptus hybrid has been planted rigorously in wet tropical regions including Malaysia. Recently, there was a report on the occurrence of stem canker on these trees. However, the extent of the infections by this stem canker is unknown. The aim of this study was to evaluate the influence of stem canker disease, Chrysoporthe deuterocubensis, on the physical and mechanical properties of 11-year-old E. urophylla × E. grandis or also known as E. urograndis. The samples were taken from infected and healthy trees that were segregated into different classes based on the severity of the attack, i.e., healthy (class 1), moderately infected (class 2), severely infected (class 3) and very severely infected (class 4). A total of 1440 samples from four infection classes were used in this study. The physical and mechanical properties were determined according to the standard test procedures specified by the International Organization for Standardization (ISO) 13061:2014 (Parts 1 to 4, 13, 14 and 17) and British Standard (BS 373: 1957). From the result, a significant effect by the infection classes was observed on physical and mechanical properties of E. urograndis. All infected wood experienced less shrinkage compared to that of a healthy one, particularly the volumetric (Vol_sh) and radial shrinkage (R_sh). Wood from class 2 and class 3 was less affected by the infection while the majority of wood from class 4 had significantly lower density and poorer strength. Based on the strength data, wood from infection class 2 can be considered to be used for non-structural applications such as furniture, interior finishing, window frames and doors since reduction in mechanical properties was observed. Wood from class 3 would need further investigation to examine its suitability for structural applications.

Oil palm wood (OPW) extracted from the oil palm trunks and subjected to a four-step compreg method consisted of drying, impregnation, re-drying and hot-pressing densification process. For the densification process, four different pressing cycles (involving 1–3 cycles) were proposed and conducted with three pressing durations (30, 35 and 40 min). Properties of the compreg OPW were evaluated. The results revealed that the samples compressed using the pressing process with more than 1 cycle displayed significantly better water absorption and thickness swelling. OPW samples that compressed with longer pressing durations also reported better performance and the formaldehyde emission decreased along with extending pressing durations. However, the improvement was not statistically significant, therefore, 30 min pressing duration is sufficient to achieve satisfied properties.

This study assessed the machining properties of 11-year-old Eucalyptus urophylla × E. grandis, known as E. urograndis wood, that was infected by stem canker disease, Chrysoporthe deuterocubensis. Instead of being discarded directly, the study aimed to explore the possibility of infected trees being used in other applications such as furniture. Sawing, planing, and boring properties as well as the surface roughness of the healthy and infected trees were evaluated. The samples were collected from infected and healthy trees and classified according to the severity of the attack: healthy (class 1), moderately infected (class 2), severely infected (class 3), and very severely infected (class 4). Prior to sawing, planing, and boring, the samples were prepared according to ASTM D 1666-11 Standard Test Methods for Conducting Machining Tests of Wood and Wood-Base Materials. All samples were sawn, planed, and bored and were evaluated for their respective machining quality. The surface roughness of the machined samples was also assessed. Overall, E. urograndis of different infection severity has very good machining properties ranging from Grade I to III. Fuzzy grain, chip grain, chip mark, and tear out are the most commonly seen physical defects. As for surface roughness, healthy trees have lower surface roughness compared to that of infected trees, which indicates a better surface quality. The findings of this study suggested that infected E. urograndis can still be used in many applications. The results of this study will provide us with better knowledge about the machining performance of disease-infected E. urograndis wood and its possibilities to be used as raw material for the wood products industry.