In this study, the removal of nickel (Ni(II)) by adsorption from synthetically prepared solutions using natural bentonites (Lieskovec (L), Hliník nad Hronom (S), Jelšový Potok (JP), and Stará Kremnička (SK)) was investigated. All experiments were carried out under batch processing conditions, with the concentration of Ni(II), temperature, and time as the variables. The adsorption process was fast, approaching equilibrium within 30 min. The Langmuir maximum adsorption capacities of the four bentonite samples used were found to be 8.41, 12.24, 21.79, and 21.93 mg g^–1, respectively. The results best fitted the pseudo-second-order kinetic model, with constant rates in a range of 0.0948–0.3153 g mg^–1 min. The effect of temperature was investigated at temperatures of 20, 30, and 40 °C. Thermodynamic parameters, including standard enthalpy (ΔH⁰), Gibbs energy (ΔG⁰), and standard entropy (ΔS⁰), were calculated. The adsorption of Ni(II) by bentonite samples was an endothermic and spontaneous process. These results indicated that, of the bentonite samples used, the natural bentonites from JP and SK were most suitable for the removal of nickel from synthetically prepared solutions.

In the present research, the removal of zinc from concentrated galvanic wastewater (pH 3.1, conductivity 20.31 mS/cm, salinity, 10.16 g/L, Chemical Oxygen Demand (COD) 2900 mg O₂/L, Total Organic Carbon (TOC) 985 mg/L, zinc (Zn) 1534 mg/L and ethylenediaminetetraacetic acid (EDTA) 70 mg/L) by combination of lime (Ca(OH)₂) and sodium trithiocarbonate (Na₂CS₃) as precipitation agents is studied. Central Composite Design (CCD) and response surface methodology (RSM) were applied for modelling and optimizing the designed wastewater treatment process. Analysis of Variance (ANOVA) and the experimental verification of the model confirmed the consistency of the experimental and estimated data calculated from the model (R² = 0.9173, R²_adj. = 0.8622). The use of Ca(OH)₂ and Na₂CS₃ in the optimal condition calculated from the model (pH = 10.75 ± 0.10, V Na₂CS₃ dose 0.043 mL/L and time = 5 min) resulted in a decrease in the concentration of Zn in treated wastewater by 99.99%. Other physicochemical parameters of wastewater also improved. Simultaneously, the application of Ca(OH)₂ and Na₂CS₃ reduced the inhibition of activated sludge dehydrogenase from total inhibition (for raw wastewater) to −70% (for treated wastewater). Under the same conditions the phytotoxicity tests revealed that the seed germination index for the raw and treated wastewater increased from 10% to 50% and from 90% to 100% for white mustard (Sinapis alba) and garden cress (Lepidium sativum L.), respectively. The parameters of root and shoot growth showed a statistically significant improvement. Treated wastewater (1:10) showed a stimulating effect (shoot growth) compared to the control sample (GI = −116.7 and −57.9 for S. alba and L. sativum L., respectively). Thus, the use of Na₂CS₃ is a viable option for the treatment of concentrated galvanic wastewater containing zinc.

The purpose of this investigation is to investigate the hydrophobicity of geopolymers, new alumino-silicate materials and the influence of Si/Al ratio on their surface properties. Contact angle measurement (CAM) as reliable indicator of hydrophobicity was determined for synthesized geopolymers using water and ethylene-glycol as reference liquids. Geopolymers were synthesized from various precursors: kaolin, bentonite and diatomite. Characterization of phase structure and microstructure was performed by XRD, FTIR, SEM/EDX methods. Contact angle measurements confirmed that the geopolymers synthesized from metakaolin are the most porous, which can be explained by the smallest Si/Al ratio. The maximum value of contact angle and free surface energy (110.2 mJ/m2) has been achieved for geopolymer synthesized by diatoms (GPMD). SEM micrograph of GPMD shows a homogeneous surface with some longitudinal cavities in the gel and is significantly different from the micrographs of other two geopolymer samples, GPMB and GPMK.

Geopolymers (GP) were successfully synthesized from metabentonite (MB), metadiatomite (MD) and metakaolinite (MK). Characterization of their phase structure and microstructure was performed by XRD, FTIR, SEM/EDX methods. A SEM micrograph of GPMD shows a homogeneous surface with some longitudinal cavities in the gel, and it is significantly different from the micrographs of the other two geopolymer samples, GPMB and GPMK. A considerable amount of unreacted particles, as well as the presence of pores in the geopolymer matrix of GPMK and GPMD, indicate an incomplete reaction in the system. Aluminosilicate inorganic polymers, geopolymers, are quasi solid electrolytes which possess a high electrical conductivity at room temperature in relation to materials of similar chemical composition. The highest conductivity was found for the sample obtained from GPMK, amounting to 2.14 × 10–2 Ω–1cm–1at 700 ºC. The corresponding activation energies of conductivity for this sample amounted to 0.33 eV in the temperature range of 500–700 ºC. The geopolymer synthesized from metakaolin has good ionic conductivity values, which recommends it for use as an alternative material for an SOFC (Solid Oxide Fuel Cell).