The European parliament has declared a global “climate and environmental emergency” on 28 November 2019. Given that, climate change is a clear strategic issue all around the world. Then, greenhouse gas emissions are reported by each country to the United Nations Framework Convention on Climate Change (UNFCCC) every year. In addition, The Intergovernmental Panel on Climate Change (IPCC) in the “2006 IPCC Guidelines for National Greenhouse Gas Inventories” give the procedure to calculate and manage the national greenhouse gases (GHG) emissions. However, these guidelines do not provide any method to consider the net carbon dioxide emissions to the atmosphere (released in clinker fabrication minus those due to concrete carbonation) by the Portland cement clinker industry. This topic should be implemented in the climatic models of the next IPCC assessment report. This paper provides an easy procedure of estimating net CO₂ emissions proposed in the “recarbonation project” (simplified method); that is to say, carbon dioxide uptake during the service-life stage is considered as the 20% of the CO₂ released by the calcination (process emissions), whereas the end-of-life and secondary usage is only the 3% of the CO₂ released by calcination. The outcome of this study reveals that 31,290.753 tons of carbon dioxide will be absorbed by the cement-based materials produced in Spain with the cements manufactured from 2005 to 2015.

The fabrication of cement clinker releases CO₂ due to the calcination of the limestone used as raw material, which contributes to the greenhouse effect. The industry is involved in a process of reducing this amount liberated to the atmosphere by mainly lowering the amount of clinker in the cements. The cement-based materials, such as concrete and mortars, combine part of this CO₂ by a process called “carbonation”. Carbonation has been studied lately mainly due to the fact that it induces the corrosion of steel reinforcement when bringing the CO₂ front to the surface of the reinforcing bars. Thus, the “rate of carbonation” of the concrete cover is characterized by and linked to the length of service life of concrete structures. The studies on how much CO₂ is fixed by the hydrated phases are scarce and even less has been studied the influence of the type of cement. In present work, 15 cements were used to fabricate paste and concrete specimens withwater/cement (w/c) ratios of 0.6 and 0.45 which reproduce typical concretes for buildings and infrastructures. The amount of carbon dioxide uptake was measured through thermal gravimetry. The degree of carbonation, (DoC) is defined as the CO₂ fixed with respect to the total theoretical maximum and the carbon storage capacity (CSC) as the carbonation uptake by a concrete element, a family or the whole inventory of a region or country. The results in the pastes where analyzed with respect to the uptake by concretes and indicated that: (a) the humidity of the pores is a critical parameter that favours the carbonation reaction as higher is the humidity (within the normal atmospheric values), (b) all types of cement uptake CO₂ in function of the CaO of the clinker except the binders having slags, which can uptake additional CO₂ giving aDoC near or above 100%. The CSC of Spain has been updated with respect to a previous publication resulting in proportions of 10.8–11.2% of the calcination emissions, through considering a ratio of “surface exposed/volume of the element” of 3 as an average of the whole Spanish asset of building and infrastructures.

Because of industrialization growth, the amount of coal power plant wastes has increased very rapidly. Particularly, the disposal of coal bottom ash (CBA) is becoming an increasing concern for many countries because of the increasing volume generated, the costs of operating landfill sites, and its potential hazardous effects. Therefore, new applications of coal bottom ash (CBA) have become an interesting alternative to disposal. For instance, it could be used as a Portland cement constituent leading to more sustainable cement production by lowering energy consumption and raw material extracted from quarries. Coal fly and bottom ashes are formed together in the same boiler; however, the size and shape of these ashes are very different, and hence their effect on the chemical composition as well as on the mineralogical phases must be studied. Coal bottom ash was ground. Later, both ashes were compared from a physical, mechanical, and chemical point of view to evaluate the potential use of coal bottom ash as a new Portland cement constituent. Both ashes, produced by the same electrical power plant, generally present similar chemical composition and compressive strength and contribute to the refill of mortar capillary pores with the reaction products leading to a redistribution of the pore size.

The European Green Deal and its endeavors will make rapid and far-reaching decisions with major implications for the European cement industry in the short- and longer-term. Accordingly, new measures should be dealt with quickly and effectively to minimize the adverse impact on global warming and global climate change by this sector. The aim of this study is to show and assess the measures to be undertaken to reach carbon neutrality by the Spanish cement industry by 2050. They may be categorized into three broad types based on the main materials: clinker, cement, and concrete. The cement sector must implement breakthrough initiatives, inventions, and technologies regarding the clinker and cement production processes. Furthermore, carbon dioxide uptake by cement-based materials must be considered to achieve the carbon neutrality objective. Accordingly, two methodologies named simplified and advanced, consistent with Guidelines for National Greenhouse Gas Inventories elaborated by the Intergovernmental Panel on Climate Change (IPCC), were selected to model the carbon offsetting by mortars and concretes. Finally, the existing climate change mitigation technologies available in Spain are insufficient to reach the net zero carbon footprint. Therefore, breakthrough technologies such as novel and efficient carbon dioxide capture, utilization, and storage (CCUS) technologies should be implemented by the Spanish cement industry to achieve zero carbon dioxide emissions in 2050.