The European Green Deal and its endeavors will make rapid and far-reaching decisions with major implications for the European cement industry in the short- and longer-term. Accordingly, new measures should be dealt with quickly and effectively to minimize the adverse impact on global warming and global climate change by this sector. The aim of this study is to show and assess the measures to be undertaken to reach carbon neutrality by the Spanish cement industry by 2050. They may be categorized into three broad types based on the main materials: clinker, cement, and concrete. The cement sector must implement breakthrough initiatives, inventions, and technologies regarding the clinker and cement production processes. Furthermore, carbon dioxide uptake by cement-based materials must be considered to achieve the carbon neutrality objective. Accordingly, two methodologies named simplified and advanced, consistent with Guidelines for National Greenhouse Gas Inventories elaborated by the Intergovernmental Panel on Climate Change (IPCC), were selected to model the carbon offsetting by mortars and concretes. Finally, the existing climate change mitigation technologies available in Spain are insufficient to reach the net zero carbon footprint. Therefore, breakthrough technologies such as novel and efficient carbon dioxide capture, utilization, and storage (CCUS) technologies should be implemented by the Spanish cement industry to achieve zero carbon dioxide emissions in 2050.

The purpose of this paper is to establish some correlations between the main technical parameter with regard to the cement-based materials technology, the 28-day compressive strength, and ultrasonic pulse velocity of standard mortar samples cured at three different conditions—(i) under water at 22 °C; (ii) climatic chamber at 95% RH and 22 °C; (iii) lab ambient, 50% RH, and 22 °C—and after five curing periods of 1, 2, 7, 14, and 28 days. Good correlations for each curing conditions were obtained. All the positive linear relationships showed better R2 than exponential ones. These findings may promote the use of ultrasonic pulse velocity for the estimation of the 28-day compressive strength of standard Portland cement samples within the factory internal quality control.

The increased use of industrial wastes and by-products to produce concretes and blended cements is a lever to achieve carbon neutrality. Furthermore, they could improve their durability. Some pozzolanic additions can minimize the alkali-silica reaction (ASR), which is a well-known deleterious process that occurs between some reactive aggregates and the alkaline pore solution found in mortars and concretes. This work quantifies the efficiency of four pozzolanic materials (natural pozzolan, P, siliceous coal fly ash, V, silica fume, D, and blast-furnace slag, S) assessed by means of compressive strength testing, open porosity, ASR-expansion measurements, and SEM microscopy. Accelerated expansion tests were performed in mortar bars with a cement/sand ratio of 1/2.25 and a water/cement ratio of 0.47, two reactive aggregates and a non-reactive one. The major contributions of this paper are: (i) The more aggregate reactivity is, the higher ASR mitigation level was found when additions were added and (ii) The best additions for ASR inhibition are silica fume and fly ash.