In this study, aligned zinc oxide (ZnO) nanorods (NRs) with various lengths (1.5–5 µm) were deposited on ZnO:Al (AZO)-coated glass substrates by using a solution phase deposition method; these NRs were prepared for application as working electrodes to increase the photovoltaic conversion efficiency of solar cells. The results were observed in detail by using X-ray diffraction, field-emission scanning electron microscopy, UV-visible spectrophotometry, electrochemical impedance spectroscopy, incident photo-to-current conversion efficiency, and solar simulation. The results indicated that when the lengths of the ZnO NRs increased, the adsorption of D-719 dyes through the ZnO NRs increased along with enhancing the short-circuit photocurrent and open-circuit voltage of the cell. An optimal power conversion efficiency of 0.64% was obtained in a dye-sensitized solar cell (DSSC) containing the ZnO NR with a length of 5 µm. The objective of this study was to facilitate the development of a ZnO-based DSSC.

In Cu₂ZnSnS₄ (CZTS) solar cells, it is crucial to suppress the generation of and remove the SnS₂ secondary phase to improve the solar cell characteristics, as the SnS₂ secondary phase affects the barrier for carrier collection and diode characteristics of the device. In this study, the nano-metallic precursor was modified to effectively suppress the generation of the SnS₂ secondary phase on the surface and simultaneously improve the uniformity and quality of the thin film. The CZTS bifacial solar cells prepared via the proposed method exhibited significantly improved junction-rectifying characteristics, as the efficiency was improved to 1.59%. The proposed method to figurremove SnS₂ is effective, simple, and environmentally friendly.