Co-torrefaction of microalgae and lignocellulosic biomass was evaluated as a method to process microalgae sludge produced from various effluents and to obtain biochars with suitable properties for energy or material valorization. The influence of four independent variables on biochar yield and properties was evaluated by a set of experiments defined by response surface methodology (RSM). The biochars were characterized for proximate and ultimate composition, HHV, and methylene blue adsorption capacity. HHV of the biochars was positively correlated with carbonization temperature, residence time, and lignocellulosic biomass content in the feed. Co-torrefaction conditions that led to a higher yield of biochar (76.5%) with good calorific value (17.4 MJ Kg⁻¹) were 250 °C, 60 min of residence time, 5% feed moisture, and 50% lignocellulosic biomass. The energy efficiency of the process was higher for lower temperatures (92.6%) but decreased abruptly with the increase of the moisture content of the feed mixture (16.9 to 57.3% for 70% moisture). Biochars produced using algal biomass grown in contaminated effluents presented high ash content and low calorific value. Dye removal efficiency by the produced biochars was tested, reaching 95% methylene blue adsorption capacity for the biochars produced with the least severe torrefaction conditions.

Acacia spp. are widespread all over the Portuguese territory, representing a threat to local biodiversity and to the productivity of the forest sector. The measures adopted in some countries for their eradication or to control their propagation are expensive, have been considered unfeasible from practical and economical perspectives, and have generated large amounts of residue that must be valorized in a sustainable way. This review brings together information on the valorization of bark, wood, leaves, flowers, pods, seeds, roots, and exudates from Acacia spp., through the production of high-value bioactive extracts (e.g., antioxidant, antimicrobial, anti-inflammatory, antidiabetic, antiviral, anthelmintic, or pesticidal agents, suitable to be explored by pharmaceutical, nutraceutical, cosmetics, and food and feed industries), its incorporation in innovative materials (e.g., polymers and composites, nanomaterials, low-cost adsorbents), as well as through the application of advanced thermochemical processes (e.g., flash pyrolysis) and pre-treatments to decompose biomass in its structural components, regarding the production of biofuels along with valuable chemicals derived from cellulose, hemicellulose, and lignin. The knowledge of this research is important to encourage an efficient and sustainable valorization of Acacia spp. within a biorefinery concept, which can bring a significant economic return from the valorization of these residues, simultaneously contributing to forest cleaning and management, to reduce the risk of fires, and to improve the social-economic development of rural areas.

The purpose of this work was to evaluate the recovery of bioactive extracts from Acacia dealbata leaves and twigs and to characterize their chemical composition and functional properties. Fresh and air-dried samples were extracted by maceration at room temperature and by hot extraction at 60 °C using aqueous solutions of acetone, ethanol, and methanol. The highest extraction yields (14.8 and 12.0% for dried leaves and twigs, respectively) were obtained with 70% acetone, for both extraction procedures. Extracts were characterized for total phenolics content (TPC), total flavonoid content (TFC) and total proanthocyanidin content (TPrAC). Bioactive extracts with high TPC (526.4 mg GAE/g extract), TFC (198.4 mg CatE/g extract), and TPrAC (631.3 mg PycE/g extract) were obtained using maceration, a technically simple and low-energy process. The non-polar fraction of selected extracts was characterized using gas chromatography and time of flight mass spectrometry (GC-TOFMS). The main components detected were phytol, squalene, α-tocopherol, lupenone, and lupeol. The antioxidant activity of the extracts was characterized through DPPH and FRAP assays. Antimicrobial activity of the extracts against different bacteria was also determined. The highest DPPH and FRAP activities were obtained from dried twigs from Alcobaça (1068.3 mg TE/g extract and 9194.6 mmol Fe²⁺/g extract, respectively). Extracts from both leaves and twigs showed antimicrobial properties against Staphylococcus aureus, Staphylococcus epidermidis, methicillin resistant Staphylococcus aureus (MRSA), Enterococcus faecalis, Bacillus cereus, Streptococcus mutans, and Streptococcus mitis. The results obtained demonstrate the feasibility of recovering valuable components from these biomass fractions that may be further valorized for energy production in a biorefinery concept.

In recent decades, interest in the eco-efficiency of building materials has led to numerous research projects focused on the replacement of raw materials with mineral and biomass wastes, and on the production of mortars with low-energy-consuming binders, such as gypsum. In this context, five different fractions (bark, wood, branchlets, leaves, and flowers) of Acacia dealbata—an invasive species—were evaluated as fillers for premixed gypsum mortars, at 5% and 10% (vol.) addition levels and fixed water content. Although these biomass fractions had different bulk densities (>50% of variation), all the mortars were workable, although presenting different consistencies. As expected, dry density decreased with biomass addition, but, while mortars with addition at 5% presented a slight shrinkage, a slight expansion occurred with those with 10% addition. Generally, the mechanical properties decreased with the biomass additions even if this was not always proportional to the added content. The wood fraction showed the most positive mechanical results but flexural and compressive strengths of all the tested mortars were found to be higher than the lower standard limit, justifying further studies.