Biomass-based carbon nanofibers (CNF) were synthesized using lignin extracted from sawdust and polyacrylonitrile (PAN) (30:70) with the help of the electrospinning method and subsequent stabilization at 220 °C and carbonization at 800, 900, and 1000 °C. The synthesized CNFs were studied by scanning electron microscopy, energy-dispersive X-ray analysis, Raman spectroscopy, and the Brunauer–Emmett–Teller method. The temperature effect shows that CNF carbonized at 800 °C has excellent stability at different current densities and high capacitance. CNF 800 in the first test cycle at a current density of 100 mA/g shows an initial capacity of 798 mAh/g and an initial coulomb efficiency of 69.5%. The CNF 900 and 1000 show an initial capacity of 668 mAh/g and 594 mAh/g, and an initial Coulomb efficiency of 52% and 51%. With a long cycle (for 500 cycles), all three samples at a current density of 500 mA/g show stable cycling in different capacities (CNF 800 in the region of 300–400 mAh/g, CNF 900 and 1000 in the region of 100–200 mAh/g).

Activated carbons (ACs) have been the most widespread carbon materials used in supercapacitors (SCs) due to their easy processing methods, good electrical conductivity, and abundant porosity. For the manufacture of electrodes, the obtained activated carbon based on sawdust (karagash and pine) was mixed with conductive carbon and polyvinylidene fluoride as a binder, in ratios of 75% activated carbon, 10% conductive carbon black, and 15% polyvinylidene fluoride (PVDF) in an N-methyl pyrrolidinone solution, to form a slurry and applied to a titanium foil. The total mass of each electrode was limited to vary from 2.0 to 4.0 mg. After that, the electrodes fitted with the separator and electrolyte solution were symmetrically assembled into sandwich-type cell construction. The carbon’s electrochemical properties were evaluated using cyclic voltammetry (CV) and galvanostatic charge–discharge (CGD) studies in a two-electrode cell in 6M KOH. The CV and CGD measurements were realized at different scan rates (5–160 mV s⁻¹) and current densities (0.1–2.0 A g⁻¹) in the potential window of 1 V. ACs from KOH activation showed a high specific capacitance of 202 F g⁻¹ for karagash sawdust and 161 F g⁻¹ for pine sawdust at low mass loading of 1.15 mg cm⁻² and scan rate of 5 mV s⁻¹ in cyclic voltammetry test and 193 and 159 F g⁻¹ at a gravimetric current density of 0.1 A g⁻¹ in the galvanostatic charge–discharge test. The specific discharge capacitance is 177 and 131 F g⁻¹ at a current density of 2 A g⁻¹. Even at a relatively high scan rate of 160 mV s⁻¹, a decent specific capacitance of 147 F g⁻¹ and 114 F g⁻¹ was obtained, leading to high energy densities of 26.0 and 22.1 W h kg⁻¹ based on averaged electrode mass. Surface properties and the porous structure of the ACs were studied by scanning electron microscopy, energy-dispersive X-ray analysis, Raman spectroscopy, and the Brunauer–Emmett–Teller method.

Biowaste conversion into activated carbon is a sustainable and inexpensive approach that relieves the pressure on its disposal. Here, we prepared micro-mesoporous activated carbons (ACs) from cucumber peels through carbonization at 600 °C followed by thermal activation at different temperatures. The ACs were tested as supercapacitors for the first time. The carbon activated at 800 °C (ACP-800) showed a high specific capacitance value of 300 F/g at a scan rate of 5 mV/s in the cyclic voltammetry and 331 F/g at the current density of 0.1 A/g in the galvanostatic charge–discharge analysis. At the current density of 1 A/g, the specific discharge capacitance was 286 F/g and retained 100% capacity after 2000 cycles. Their properties were analyzed by scanning electron microscopy, energy-dispersive X-ray analysis, porosity, thermal analysis, and Fourier-transform infrared spectroscopy. The specific surface area of this sample was calculated to be 2333 m² g⁻¹ using the Brunauer–Emmett–Teller method. The excellent performance of ACP-800 is mainly attributed to its hierarchical porosity, as the mesopores provide connectivity between the micropores and improve the capacitive performance. These electrochemical properties enable this carbon material prepared from cucumber peels to be a potential source for supercapacitor materials.

Co₃O₄ nanoparticles synthesized by solution combustion synthesis present a versatile platform for the development of porous nanostructures with tunable morphology and physicochemical properties. Synthesis conditions and parameters such as fuel type; fuel-to-oxidizer ratio and temperature control lead yielding; and Co₃O₄ NPs with fine particle size, surface area, and porosity result in enhancing their electrochemical and catalytic capabilities. This review evaluates present studies about SCS Co₃O₄ NPs to study how synthesis parameter modifications affect both surface morphology and material structure characteristics including porosity features, which make their improved performance ideal for lithium-ion batteries and supercapacitors. Moreover, the integration of dopants with carbon-based hybrid composites enhances material conductivity and stability by addressing both capacity fading and low electronic conductivity concerns. This review mainly aims to explore the significant relation between fundamental material design principles together with practical uses and provides predictions about future research advancements that aim to enhance the performance of Co₃O₄ NPs in next-generation energy and environmental technology applications.

The synthesis of graphene layers on a nickel substrate in a butane–benzene–oxygen premixed flame at a pressure of 40–100 Torr is studied. It is demonstrated that, the temperature of 900–950°C and...