The effects of cold rolling reduction on the microstructure, recrystallization behavior, and magnetic properties of 3.0%Si-0.8%Al-0.3%Mn steel were studied by X-ray diffraction (XRD) and electron backscatter diffraction (EBSD). With the reduction rates of 78%, 85% and 87% in the cold rolled sheet, the width of the deformation band becomes narrower, the number of intragranular shear bands decreases, and the proportion of grain boundaries increases. The intensity of the α and γ fibers texture in the cold rolled sheet is enhanced, and the annealed sheet is dominated by the γ fibers texture and the content increases from 26.0% to 34.5%. During the recrystallization process, the Goss and γ-grains nucleate first. The λ-grains nucleate mainly at the grain boundaries of the deformed α-grains, and the α-grains ultimately recrystallize. With the increase in the cold rolling reduction rate, the γ-grains develop into the main texture due to a large amount of nucleation at the deformation band and grain boundary. The λ-grains with a high mobility do not have a numerical advantage, and the increase in the texture content is very small. The content of the unfavorable γ fiber texture in the annealed sheet increases, the magnetic induction intensity B50 decreases, Pe and Pt decrease significantly, and the critical grain size with the lowest iron loss decreases from 136.2 to 109.4 μm.

The effects of trace Ce on the microstructure and texture of non-oriented silicon steel during recrystallization and grain growth were examined using X-ray diffraction and electron backscatter diffraction. Additionally, this study focused on investigating the mechanisms by which trace Ce influences the evolution of the {114} and γ-fiber textures. During the recrystallization process, as the recrystallization fraction of annealed sheets increased, the intensity of α-fiber texture decreased, while the intensities of α*-fiber and γ-fiber textures increased. The {111} grains preferentially nucleated in the deformed γ-grains and their grain-boundary regions and tended to form a colony structure with a large amount of nucleation. In addition, the {100} and {114} grains mainly nucleated near the deformed α-grains, which were evenly distributed but found in relatively small quantities. The hindering effect of trace Ce on dislocation motion in cold-rolled sheets results in a 2–7% lower recrystallization ratio for the annealed sheets, compared to conventional annealed sheets. Trace Ce suppresses the nucleation and growth of γ-grains while creating opportunities for α*-grain nucleation. During grain growth, trace Ce reduces γ-grain-boundary migration rate in annealed sheets, providing growth space for {114} grains. Consequently, the content of the corresponding {114} texture increased by 6.4%, while the γ-fiber texture content decreased by 3.6%.

Based on low-temperature high-permeability grain-oriented silicon steel designed with an initial nitrogen content of 0.0055% and produced by the thin slab casting and rolling process, the effect of total nitrogen content and nitriding temperature on primary recrystallization microstructure and texture were studied by optical microscope, scanning electron microscope, transmission electron microscope, and electron backscatter diffraction. The nitriding temperature affects the primary recrystallization behaviors significantly, while the total nitrogen content has a small effect. As the nitriding temperature is 750–850 °C, the average primary grain size and its inhomogeneity factor are about 26.58–26.67 μm and 0.568–0.572, respectively. Moreover, the texture factor is mostly between 0.15 and 0.40. Because of the relatively sufficient inhibition ability of inherent inhibitors in a decarburized sheet, the nitriding temperature (750–850 °C) affects the primary recrystallization microstructure and texture slightly. However, as the nitriding temperature rises to 900–950 °C, the average primary grain size and its inhomogeneity factor increase to 27.75–28.26 μm and 0.575–0.578, respectively. Furthermore, because of the great increase on the area fraction of {112} grains, part of texture factor is increased sharply. Therefore, in order to obtain better primary grain size and homogeneity, better texture composition, and stability of the decarburized sheet, the optimal nitriding temperature is 750–850 °C.

The effects of Cu content on the microstructure, texture, precipitates, and magnetic and mechanical properties of 0.20 mm-thick non-oriented silicon steel (3.0% Si-0.8% Al-0.5% Mn) were systematically investigated using optical microscopy, X-ray diffraction, electron backscatter diffraction, and transmission electron microscopy. The strengthening mechanisms of Cu-bearing high-strength non-oriented silicon steel were further elucidated. Increasing Cu content inhibited grain growth and suppressed the development of the α*-fiber texture in annealed sheets, while promoting the formation of γ-fiber texture. As a result, the P_1.0/400 and B₅₀ values deteriorated. The P_1.0/400 and B₅₀ values of 1.47% Cu non-oriented silicon steel were 13.930 W/kg and 1.614 T, respectively. However, due to the solid solution strengthening effect of 0.5% Cu and partial precipitation strengthening, the R_p0.2 increased by 43 MPa. After aging treatment at 550 °C for 20 min, the P_1.0/400 values of the aged sheets slightly increased, while the B₅₀ values remained almost unchanged. In the aged sheets containing 1.0–1.5% Cu, clustered Cu-rich precipitates with average sizes of 2.71 nm and 13.28 nm were observed. The crystal structure of these precipitates transitioned from the metastable B2-Cu to the stable FCC-Cu. These precipitates enhanced the R_p0.2 of the non-oriented electrical steel to 241 MPa and 269 MPa through cutting and bypass mechanisms, respectively. A high-strength non-oriented silicon steel with balanced magnetic and mechanical properties was developed for driving motors of new energy vehicles by utilizing nanoscale Cu-rich precipitates formed through aging treatment. The optimized steel exhibits a yield strength of 708 MPa, a magnetic induction B₅₀ of 1.639 T, and high-frequency iron loss P_1.0/400 of 14.77 W/kg.