Evolution of texture and α*-fiber texture formation mechanism of Fe-0.65%Si non-oriented electrical steel produced by Compact Strip Production (CSP) process during all the thermo-mechanical processing steps were investigated using electron backscatter diffraction (EBSD) and X-ray diffraction (XRD) techniques. Columnar crystal structure of cast slab is fine and well-developed. Textures of the hot-rolled band are quite different in the thickness direction. During annealing of cold-rolled sheet, γ-fiber texture grains would nucleate and grow preferentially, and α*-fiber texture grains mainly nucleate and grow in the shear zone of α-fiber texture of cold-rolled sheet. During the recrystallization process, γ-fiber texture gradually concentrated to {111}, and γ and α*-fiber texture increased significantly. {111} texture priority nucleation at the initial stage of recrystallization. Due to the advantages of nucleation position and quantity, the content of α*-fiber texture is greater than {111} texture in the mid-recrystallization. During grain growth process, {111} oriented grains would grow selectively by virtue of higher mobility, sizes and quantity advantages than that of {411} and {100}, resulting in the gradual increase of γ-fiber texture and the decline of α *-fiber texture.

The effects of cold rolling reduction on the microstructure, recrystallization behavior, and magnetic properties of 3.0%Si-0.8%Al-0.3%Mn steel were studied by X-ray diffraction (XRD) and electron backscatter diffraction (EBSD). With the reduction rates of 78%, 85% and 87% in the cold rolled sheet, the width of the deformation band becomes narrower, the number of intragranular shear bands decreases, and the proportion of grain boundaries increases. The intensity of the α and γ fibers texture in the cold rolled sheet is enhanced, and the annealed sheet is dominated by the γ fibers texture and the content increases from 26.0% to 34.5%. During the recrystallization process, the Goss and γ-grains nucleate first. The λ-grains nucleate mainly at the grain boundaries of the deformed α-grains, and the α-grains ultimately recrystallize. With the increase in the cold rolling reduction rate, the γ-grains develop into the main texture due to a large amount of nucleation at the deformation band and grain boundary. The λ-grains with a high mobility do not have a numerical advantage, and the increase in the texture content is very small. The content of the unfavorable γ fiber texture in the annealed sheet increases, the magnetic induction intensity B50 decreases, Pe and Pt decrease significantly, and the critical grain size with the lowest iron loss decreases from 136.2 to 109.4 μm.

Nitrogen and Sulfur in non-oriented electrical steel would form precipitates, which would severely affect its magnetic properties. Precipitates in compact strip production (CSP) process non-oriented electrical steel were investigated using a transmission electron microscope (TEM) and scanning electron microscopy (SEM). The precipitation mechanism and influence on grain growth were analyzed experimentally and theoretically. The results showed that the main particles in steel were AlN, TiN, MnS, Cu₂S, and fine oxide inclusions. The spherical or quasi-spherical of MnS and Cu₂S were more liable to precipitate along grain boundaries. During the soaking process, the amount of MnS precipitated on the grain boundary was much larger than that of Cu₂S. AlN and TiN in cubic shape precipitated inside grains or grain boundaries. Precipitates preferentially nucleated at grain boundaries, and TiN, MnS mainly precipitated during soaking. In the subsequent processes after soaking, AlN and Cu₂S would precipitate unceasingly with the decrease in the average size. The distribution density, the volume fraction, and the average size of the precipitates in the annealed sheets were 9.08 × 10¹³/cm³, 0.06%, and 54.3 nm, respectively. Precipitates with the grain size of 30–500 nm hindered the grain growth, the grains with 100–300 nm played a major role in inhibiting the grain growth, and the grains with the grain size of 70–100 nm took the second place.

Optimum grain size and effects of crystallographic textures on magnetic properties of Fe-0.65%Si non-oriented electrical steel produced by compact strip production (CSP) process were investigated by optical microscope, electron backscatter diffraction (EBSD), and X-ray diffraction (XRD) techniques. Magnetic induction and core loss show a decreasing trend with the increase of grain size, and grain sizes for optimal magnetic properties are in the range of 26–30 μm. Core loss would be mainly affected by grain size, whereas crystallographic texture would primarily affect magnetic flux density. Magnetic properties increase with increasing of texture factor (volume fraction ratio of {100}/{111}) and magnetic texture factor (volume fraction ratio of /), and increasing with the decrease of A-parameter (minimum angle between magnetization direction and the closest direction) and $A(\overrightarrow{h})$, respectively. Simultaneously, with increasing of A-parameter and $A(\overrightarrow{h})$, a linear decrease of B₅₀ was obtained.

The effects of trace Ce on the microstructure and texture of non-oriented silicon steel during recrystallization and grain growth were examined using X-ray diffraction and electron backscatter diffraction. Additionally, this study focused on investigating the mechanisms by which trace Ce influences the evolution of the {114} and γ-fiber textures. During the recrystallization process, as the recrystallization fraction of annealed sheets increased, the intensity of α-fiber texture decreased, while the intensities of α*-fiber and γ-fiber textures increased. The {111} grains preferentially nucleated in the deformed γ-grains and their grain-boundary regions and tended to form a colony structure with a large amount of nucleation. In addition, the {100} and {114} grains mainly nucleated near the deformed α-grains, which were evenly distributed but found in relatively small quantities. The hindering effect of trace Ce on dislocation motion in cold-rolled sheets results in a 2–7% lower recrystallization ratio for the annealed sheets, compared to conventional annealed sheets. Trace Ce suppresses the nucleation and growth of γ-grains while creating opportunities for α*-grain nucleation. During grain growth, trace Ce reduces γ-grain-boundary migration rate in annealed sheets, providing growth space for {114} grains. Consequently, the content of the corresponding {114} texture increased by 6.4%, while the γ-fiber texture content decreased by 3.6%.

Improving the efficiency of electric vehicle traction motors requires non-oriented silicon steels with low core loss and favorable magnetic induction. This study aims to clarify the influence of annealing temperature on the microstructure, texture, and magnetic properties of a 3.2%Si–0.9%Al steel, providing guidance for process optimization. Optical metallography, X-ray diffraction, and electron backscatter diffraction were employed to characterize the evolution. Recrystallization was completed between 620 °C and 720 °C, during which fine recrystallized grains replaced the deformed structure, accompanied by the nucleation of {111} and {114} grains. With further annealing from 850 °C to 1050 °C, grain growth occurred, resulting in an α*-fiber texture dominated by {114}. The fraction of high-angle {114} grains increased, while low-angle {111} grains decreased. This microstructural evolution significantly influenced the magnetic properties of non-oriented electrical steel. The P_1.5/50 and P_1.0/400 core losses reached minimum values of 2.02 W/kg and 16.48 W/kg at 1010 °C and 930 °C, respectively, while B₅₀ decreased slightly from 1.670 T to 1.652 T. These findings indicate that precise control of the annealing temperature is an effective strategy to tailor microstructure and texture, thereby optimizing the magnetic properties of non-oriented electrical steel.