Sustainability has become of paramount importance, as evidenced by the increasing number of norms and regulations concerning various sectors. Due to its intrinsic trans-sectorial nature, tribology has drawn the attention of the supporters of sustainability. This discipline allows the environmental, economic, and social impacts to be decreased in a wide range of applications following the same strategies. In 2010, Nosonovsky and Bhushan drew up 12 approaches based on the 12 principles of green chemistry and the 12 principles of green engineering, defining the “12 principles of green tribology.” This review exploits the 12 principles of green tribology to fathom the developed research related to sustainability and tribology. Different approaches and innovative studies have been proposed in this short selection as references to consider for further development, pursuing the efforts of the scientific community for a sustainable future through the contribution also of tribosystems. The manuscript aims to provide practical examples of materials, lubricants, strategies, and technologies that have contributed to the overall progress of tribology, decreasing wear and friction and increasing efficiency, and at the same time promoting sustainable development, lowering toxicity, waste production, and loss of energy and resources.

Friction and wear are responsible for around 23% of the energy consumption in transportation, manufacturing, power generation, and residential sectors. Employed components are exposed to a wide range of operational conditions, therefore a suitable material design is fundamental to decreasing tribological issues, energy consumption, costs, and environmental impact. This study aims to analyze the effect of different solid lubricants on the suitability of copper matrix composites (CuMCs) as a potential solution to reduce the depletion of sliding electrical contacts working under extreme conditions. CuMCs samples are produced by cold-pressing and sintering to merge a high electrical conductivity with the lubricant effect supplied by different species, namely tungsten disulfide micro-powder (WS₂), inorganic fullerene-like (IF) tungsten disulfide nanoparticles, and graphene nanoplatelets (GNP). The crystalline structure of the pristine and composite materials is characterized via XRD. The electrical tests show a small decrease of conductivity compared to pure copper, due to the insulating effect of WS₂; however, the measured values are still adequate for conduction purposes. Micro-scratch and wear tests highlight the positive effect of the combination of WS₂ structures and GNP. The friction coefficient reduction leads to the possibility of extending the lifetime of the components.

Innovative nanostructured materials offer the possibility of enhancing the tribological performance of traditional materials like graphite and molybdenum disulfide (MoS₂). In this study, the scratch resistance of two different copper powders, dendritic and spherical, and their composites with traditional MoS₂, nanometric MoS₂, and graphene nanoplatelets was investigated. Metal powder metallurgy was employed to produce composite materials with 5 wt% and 10 wt% of each solid lubricant. A ball milling step was employed to grind and mix the matrix copper powder with the lubricants. The use of a cold press combined with the sintering in inert atmosphere at 550 °C limited the oxidation of the copper and the degradation of the solid lubricants. The so-produced materials were characterized through a variety of techniques such as micro-indentation hardness, electrical resistivity, contact angle wettability, X-ray diffraction, Raman scattering, and scanning electron microscopy. Moreover, micro-scratch tests were performed on both pure copper and composite materials for comparing the apparent scratch hardness and friction coefficients. The scratches were examined with confocal laser scanning microscopy (CLSM), to identify the evolution of the damage mechanisms during the formation of the groove. The results highlighted the important difference between the dendritic and spherical copper powders and demonstrated a way to improve wear behavior thanks to the use of nanometric powders as solid lubricants.

Metal matrix self-lubricating composites exhibit outstanding performance in various environments, reaching the required properties by modifying the reinforcement–matrix ratio and the production method. The present research investigated the effects on tribological performance and electrical properties of different pressure loads, maintaining pressing time, and sintering temperatures during the production of copper–10 wt% tungsten disulfide (Cu–WS₂) composite via powder metallurgy. Moreover, additional thermo-mechanical treatments were evaluated, namely second pressing and second sintering steps. The density and the hardness of the produced composites were measured, as well as the electrical resistivity, considering sliding electrical contacts as possible employment. The outputs of the wear tests were considered together with the analysis of the wear track via scanning electron microscopy and confocal laser scanning microscopy to understand wear mechanisms. Different production routes were compared in terms of electrical resistivity, wear coefficient, and specific wear rate, calculated by the confocal laser scanning microscopy, and friction coefficient, measured during the wear test. The main results highlighted that the increase in sintering temperature was detrimental to the hardness and tribological properties; higher load and additional pressing step determined a general improvement in the tested properties.

Ball milling is a fundamental step of powder metallurgy widely employed for composite manufacturing. This work focuses on the influence of ball milling time on the morphological, electrical, and tribological properties of self-lubricating copper-tungsten disulfide (Cu-WS₂) composites. The study investigates ball milling times between 1 and 24 h to guarantee different degrees of incorporation of WS₂ in the copper matrix. Micro-scratch and wear tests are performed to evaluate the tribological behavior. Optical, scanning electron, and confocal laser scanning microscopy analyze the scratch and wear tracks. The results show the reliability of the production process and a general improvement of the composites' mechanical properties compared to pure copper. The addition of WS ₂ enhances the tribo-mechanical properties, increasing hardness and wear resistance and decreasing the friction coefficient. Shorter ball milling times result in larger WS₂ flakes distributed in the copper matrix, while longer ball milling times result in smaller and more dispersed particles. This homogeneous fine dispersion determines a difference in the composites' electrical conductivity and tribological performance, with shorter ball milling times (i.e., between 2 and 4 h) offering the best trade-off between wear behavior and electrical properties.