Al₂O₃ coatings were applied on the surface of 12Ch18N10T steel by the detonation method at different degrees of filling of the detonation gun. The aim was to study the influence of technological parameters on the formation of the coating’s structure, phase composition and tribological characteristics. The degree of filling the gun with a gas mixture (C₂H₂/O₂) varied from 53% to 68%. X-ray diffraction study showed that the content of α-Al₂O₃ increases depending on the degree of filling. The results showed that the hardness increases with an increase in the α-Al₂O₃ phase. When the gun is 53% filled with gas, the Al₂O₃-based coating has the hardness of 20.56 GPa compared to 58%, 63% and 68% fillings. Tribology tests have shown that the wear rate and friction coefficient of the coating is highly dependent on the degree of filling of the gun.

Arc spraying is one of the most effective and cost-efficient thermal spraying technologies for creating high-quality protective coatings. This paper examines the influence of arc spraying process parameters on the properties of steel coatings. The parameters varied in this study included gas pressure, wire feed rate, and the distance from the spray gun to the substrate (standoff distance). Experimental evaluations focused on surface roughness, thickness, porosity, structure, and hardness of the coatings. The techniques used for these evaluations included profilometry for roughness measurement, scanning electron microscopy (SEM) for structural analysis, Vickers hardness testing, and optical microscopy. The results demonstrate a significant influence of arc spraying parameters on the characteristics of the resulting coatings. The analysis revealed that the coatings produced under different modes exhibit a layered structure and vary in thickness. A detailed examination of the coating structure identified defects such as unmelted particles, voids, and delamination in the interface zone. The study of coating thickness and porosity showed that increasing the wire feed rate and decreasing the standoff distance leads to the formation of thicker and denser coatings. Specifically, increasing the wire feed rate from 2 to 12 cm/s resulted in a decrease in porosity from 12.59% to 4.33% and an increase in coating thickness to 699 μm. The surface analysis highlighted the importance of a comprehensive approach to selecting the optimal roughness. While increasing the wire feed rate up to 12 cm/s can increase the Ra roughness parameter, gas pressure also significantly influences this parameter, reducing roughness from Ra = 18.63 μm at 6 MPa to Ra = 15.95 μm at 8 MPa. Additionally, it was found that varying the arc spraying parameters affects the hardness of the coatings, with all modes resulting in hardness values higher than that of the substrate. Therefore, optimizing these parameters enables the achievement of the best combination of mechanical and structural properties in the coatings. These findings can be valuable for further improvement of arc spraying technologies and the expansion of their application across various industries.

In this work, bioceramic coatings were formed on Ti6Al4V titanium alloy using a combined technique of plasma electrolytic oxidation followed by gas detonation spraying of calcium phosphate ceramics, based on hydroxyapatite. Plasma electrolytic oxidation was carried out in electrolytes with various chemical compositions, and the effect of electrolytes on the macro and microstructure, pore size and phase composition of coatings was estimated. Three types of electrolytes based on sodium compounds were used: phosphate, hydroxide, and silicate. Plasma electrolytic oxidation of the Ti–6Al–4V titanium alloy was carried out at a fixed DC voltage (270 V) for 5 min. The sample morphology and phase composition were studied with a scanning electron microscope and an X-ray diffractometer. According to the results, the most homogeneous structure with lower porousness and many crystalline anatase phases was obtained in the coating prepared in the silicate-based electrolyte. A hydroxyapatite layer was obtained on the surface of the oxide layer using detonation spraying. It was determined that the appearance of α-tricalcium phosphate phases is characteristic for detonation spraying of hydroxyapatite, but the hydroxyapatite phase is retained in the coating composition. Raman spectroscopy results indicate that hydroxyapatite is the main phase in the coatings.

The operation modes of a plasmatron for powder coating spraying have been studied. The plasmatron has a node of annular input and a gasdynamic focusing of the powder, and the outlet holes of the nozzle-anode are made in the form of rectangular narrowing-expanding channels (No.34334 RK: IPC H05H 1/42). The dynamics and trajectories of the powder particles in the plasmatron were investigated. The paper analyzes the influence of plasmatron arc current and working gas flow rate on the structure and properties of the obtained coatings. It is established that the phase composition of the sprayed coatings and the initial powder is the same: the main phase is the compound TiN, in addition, the structure contains the phase TiO₂. The results of tribological tests of the coatings under dry friction conditions according to the ball-on-disk scheme are presented. Within the framework of this study, it can be said, from the point of view of obtaining denser coatings with high performance characteristics, that the optimal modes of plasma spraying of TiN powder are a current of 250 A and the working gas flow rate of argon 34 L/min.

In this paper, Ni–Cr–Al coatings were deposited using the detonation spraying method. The aim was to investigate how technological parameters influence coating structure formation, phase composition and tribological performances. We observed that the degree to which the barrel is filled with an O₂/C₂H₂ gas mixture strongly influences the chemical composition of manufactured coatings. High degrees of barrel filling led to a decrease in aluminum content in the coating. Filling degrees of 40% and 50% produced sprayed coatings in which only Ni–Cr phases could be found. When the filling degree was reduced up to 25%, Ni–Al phases began to form in the sprayed coatings. Gradient Ni–Cr–Al coatings were produced by gradually reducing the filling degree from 50% to 25%. These coatings are characterized by Ni–Cr near the substrate level with Ni–Cr and Ni–Al phases at higher levels. The results obtained confirm that gradient Ni–Cr–Al coatings exhibit high hardness as well as good wear resistance.

In this study, a surface hardening of AISI 52100 bearing steel was performed by ultrasonic nanocrystal surface modification (UNSM), and electrolytic-plasma thermo-cyclic surface modification (EPSM), and their effects on the wear resistance were investigated. To evaluate the impact of these treatments on the wear resistance, the friction tests under dry conditions were conducted using a ball-on-disk tribometer in accordance with ASTM G99. The microstructure of the samples before and after treatment was characterized by scanning electron microscopy. The micro-hardness with respect to the depth from the top surface was measured using a Vickers micro-hardness tester. Microstructural observations showed that EPSM treatment led to the formation of residual austenite in the surface layer, while UNSM treatment led to the formation of a surface severe plastic deformation layer on the surface of the samples. The increase in the micro-hardness of the treated layer was confirmed after UNSM at room temperature and after EPSM at different cycles. The highest increase in wear resistance was observed for the specimen treated by UNSM treatment at 700 °C and five cycles of EPSM treatment. In addition, the wear volume, which has correlation with the friction coefficient and hardness, was determined.