Metal chalcogenides such as copper zinc tin sulfide (CZTS) have been intensively studied as potential photovoltaic cell materials, but their viability have been marred by crystal defects and low open circuit potential (V_oc) deficit, which affected their energy conversion efficiency. Strategies to improve on the properties of this material such as alloying with other elements have been explored and have yielded promising results. Here, we report the synthesis of CZTS and the partial substitution of S with Te via anion hot injection synthesis method to form a solid solution of a novel kesterite nanomaterial, namely, copper zinc tin sulfide telluride (CZTSTe). Particle-size analyzed via small angle X-ray scattering spectroscopy (SAXS) confirmed that CZTS and CZTSTe materials are nanostructured. Crystal planes values of 112, 200, 220 and 312 corresponding to the kesterite phase with tetragonal modification were revealed by the X-ray diffraction (XRD) spectroscopic analysis of CZTS and CZTSTe. The Raman spectroscopy confirmed the shifts at 281 cm⁻¹ and 347 cm⁻¹ for CZTS, and 124 cm⁻¹, 149 cm⁻¹ and 318 cm⁻¹ for CZTSTe. High degradation rate and the production of hot electrons are very detrimental to the lifespan of photovoltaic cell (PVC) devices, and thus it is important to have PVC absorber layer materials that are thermally stable. Thermogravimetric analysis (TGA) analysis indicated a 10% improvement in the thermal stability of CZTSTe compared to CZTS at 650 °C. With improved electrical conductivity, low charge transfer resistance (R_ct) and absorption in the visible region with a low bandgap energy (E_g) of 1.54 eV, the novel CZTSTe nanomaterials displayed favorable properties for photovoltaics application.

A generation 1 poly(propylene thiophenoimine)-co-poly(ethylenedioxy thiophene) (G1PPT-co-PEDOT) star copolymer, which exhibits a strong optical absorption over a broad range in the ultraviolet–visible (UV-Vis) region and with good electro/conductive properties, was chemically prepared for the first time. Synthesis of the star copolymer, G1PPT-co-PEDOT was confirmed by spectroscopic studies. Indeed, the disappearance of the very high intensity bands, C–H bending at α-position (687 cm⁻¹), and C=N stretching (1620 cm⁻¹) in the Fourier transform infrared spectroscopy (FTIR) of G1PPT-co-PEDOT, which were initially present in the spectrum of the thiolated starting material, G1PPT, confirmed copolymerization. Furthermore, a large bathochromic shift in the onset wavelength of the UV-Vis absorbance spectra from 367 nm in G1PPT to 674 nm in G1PPT-co-PEDOT further attests of successful copolymerization. The electrochemical analysis of G1PPT-co-PEDOT achieved a highest occupied molecular orbital (HOMO) energy level value of 5.3 eV, which is reminiscent of the value for an ideal electron-donor material. Photoluminescence quenching of up to 82% was observed in solution blends of the G1PPT-co-PEDOT star copolymer and N,N′-diisopropyl naphthalene diimide (NDI). This demonstrates the occurrence of photoinduced intermolecular charge transfer (PICT) from the electron-donating G1PPT-co-PEDOT to the electron accepting NDI, a good property, beneficial for optoelectronic and photovoltaic applications.