Spinel copper manganese oxide nanoparticles combined with acid-treated multi-walled carbon nanotubes (CuMn₂O₄/MWCNTs) were used in the development of electrodes for pseudocapacitor applications. The CuMn₂O₄/MWCNTs preparation involved initial synthesis of Mn₃O₄ and CuMn₂O₄ precursors followed by an energy efficient reflux growth method for the CuMn₂O₄/MWCNTs. The CuMn₂O₄/MWCNTs in a three-electrode cell assembly and in 3 M LiOH aqueous electrolyte exhibited a specific capacitance of 1652.91 F g⁻¹ at 0.5 A g⁻¹ current load. Similar investigation in 3 M KOH aqueous electrolyte delivered a specific capacitance of 653.41 F g⁻¹ at 0.5 A g⁻¹ current load. Stability studies showed that after 6000 cycles, the CuMn₂O₄/MWCNTs electrode exhibited a higher capacitance retention (88%) in LiOH than in KOH (64%). The higher capacitance retention and cycling stability with a Coulombic efficiency of 99.6% observed in the LiOH is an indication of a better charge storage behaviour in this electrolyte than in the KOH electrolyte with a Coulombic efficiency of 97.3%. This superior performance in the LiOH electrolyte than in the KOH electrolyte is attributed to an intercalation/de-intercalation mechanism which occurs more easily in the LiOH electrolyte than in the KOH electrolyte.

An impedimetric immunosensor for fumonisins was developed based on poly(2,5-dimethoxyaniline)-multi-wall carbon nanotubes doped with palladium telluride quantum dots onto a glassy carbon surface. The composite was assembled by a layer-by-layer method to form a multilayer film of quantum dots (QDs) and poly(2,5-dimethoxyaniline)-multi-wall carbon nanotubes (PDMA-MWCNT). Preparation of the electrochemical immunosensor for fumonisins involved drop-coating of fumonisins antibody onto the composite modified glassy carbon electrode. The electrochemical impedance spectroscopy response of the FB₁ immunosensor (GCE/PT-PDMA-MWCNT/anti-Fms-BSA) gave a linear range of 7 to 49 ng L⁻¹ and the corresponding sensitivity and detection limits were 0.0162 kΩ L ng⁻¹ and 0.46 pg L⁻¹, respectively, hence the limit of detection of the GCE/PT-PDMA-MWCNT immunosensor for fumonisins in corn certified material was calculated to be 0.014 and 0.011 ppm for FB₁, and FB₂ and FB₃, respectively. These results are lower than those obtained by ELISA, a provisional maximum tolerable daily intake (PMTDI) for fumonisins (the sum of FB₁, FB₂, and FB₃) established by the Joint FAO/WHO expert committee on food additives and contaminants of 2 μg kg⁻¹ and the maximum level recommended by the U.S. Food and Drug Administration (FDA) for protection of human consumption (2–4 mg L⁻¹).

Graphene oxide (GO) decorated with silver (Ag), copper (Cu) or platinum (Pt) nanoparticles that are anchored on dodecylbenzene sulfonic acid (DBSA)-doped polyaniline (PANI) were prepared by a simple one-step method and applied as novel materials for high performance supercapacitors. High-resolution transmission electron microscopy (HRTEM) and high-resolution scanning electron microscopy (HRSEM) analyses revealed that a metal-decorated polymer matrix is embedded within the GO sheet. This caused the M/DBSA–PANI (M = Ag, Cu or Pt) particles to adsorb on the surface of the GO sheets, appearing as aggregated dark regions in the HRSEM images. The Fourier transform infrared (FTIR) spectroscopy studies revealed that GO was successfully produced and decorated with Ag, Cu or Pt nanoparticles anchored on DBSA–PANI. This was confirmed by the appearance of the GO signature epoxy C–O vibration band at 1040 cm⁻¹ (which decreased upon the introduction of metal nanoparticle) and the PANI characteristic N–H stretching vibration band at 3144 cm⁻¹ present only in the GO/M/DBSA–PANI systems. The composites were tested for their suitability as supercapacitor materials; and specific capacitance values of 206.4, 192.8 and 227.2 F·g⁻¹ were determined for GO/Ag/DBSA–PANI, GO/Cu/DBSA–PANI and GO/Pt/DBSA–PANI, respectively. The GO/Pt/DBSA–PANI electrode exhibited the best specific capacitance value of the three electrodes and also had twice the specific capacitance value reported for Graphene/MnO₂//ACN (113.5 F·g⁻¹). This makes GO/Pt/DBSA–PANI a very promising organic supercapacitor material.

A generation 1 poly(propylene thiophenoimine)-co-poly(ethylenedioxy thiophene) (G1PPT-co-PEDOT) star copolymer, which exhibits a strong optical absorption over a broad range in the ultraviolet–visible (UV-Vis) region and with good electro/conductive properties, was chemically prepared for the first time. Synthesis of the star copolymer, G1PPT-co-PEDOT was confirmed by spectroscopic studies. Indeed, the disappearance of the very high intensity bands, C–H bending at α-position (687 cm⁻¹), and C=N stretching (1620 cm⁻¹) in the Fourier transform infrared spectroscopy (FTIR) of G1PPT-co-PEDOT, which were initially present in the spectrum of the thiolated starting material, G1PPT, confirmed copolymerization. Furthermore, a large bathochromic shift in the onset wavelength of the UV-Vis absorbance spectra from 367 nm in G1PPT to 674 nm in G1PPT-co-PEDOT further attests of successful copolymerization. The electrochemical analysis of G1PPT-co-PEDOT achieved a highest occupied molecular orbital (HOMO) energy level value of 5.3 eV, which is reminiscent of the value for an ideal electron-donor material. Photoluminescence quenching of up to 82% was observed in solution blends of the G1PPT-co-PEDOT star copolymer and N,N′-diisopropyl naphthalene diimide (NDI). This demonstrates the occurrence of photoinduced intermolecular charge transfer (PICT) from the electron-donating G1PPT-co-PEDOT to the electron accepting NDI, a good property, beneficial for optoelectronic and photovoltaic applications.

In this study, electron-donating semicrystalline generation 1 poly(propylene thiophenoimine)-co-poly(3-hexylthiophene) star copolymer, G1PPT-co-P3HT was chemically prepared for the first time. Copolymerization was achieved with high molecular weight via facile green oxidative reaction. ¹H NMR analyses of the star copolymer demonstrated the presence of 84% regioregular (rr) head-to-tail (HT) P3HT, which accounts for the molecular ordering in some grain regions in the macromolecule’s morphology, as revealed by the high-resolution scanning electron microscopy (HRSEM) and Selected Area Electron Diffraction (SAED) images, and X-ray diffraction spectroscopy (XRD) measurements. The star copolymer also exhibited good absorption properties in the ultraviolet-visible (UV-Vis) and the near infrared (NIR) spectral regions, which give rise to an optical energy bandgap value as low as 1.43 eV. A HOMO energy level at −5.53 eV, which is below the air-oxidation threshold, was obtained by cyclic voltammetry (CV). Electrochemical impedance spectroscopy (EIS) ascertained the semiconducting properties of the macromolecule, which is characterized by a charge transfer resistance, R_ct, value of 3.57 kΩ and a Bode plot-phase angle value of 75°. The combination of the EIS properties of G1PPT-co-P3HT and its highly electron-donating capability in bulk heterojunction (BHJ) active layer containing a perylene derivative, as demonstrated by photoluminescence quenching coupled to the observed Förster Resonance charge transfer, suggests its suitability as an electron-donor material for optoelectronic and photovoltaic devices.