This work focuses on research on obtaining and characterizing Al₂O₃/ZrO₂ materials formed via slip casting method. The main emphasis in the research was placed on environmental aspects and those related to the practical use of ceramic materials. The goal was to analyze the environmental loads associated with the manufacturing of Al₂O₃/ZrO₂ composites, as well as to determine the coefficient of thermal expansion of the obtained materials, classified as technical ceramics. This parameter is crucial in terms of their practical applications in high-temperature working conditions, e.g., as parts of industrial machines. The study reports on the four series of Al₂O₃/ZrO₂ materials differing in the volume content of ZrO₂. The sintering process was preceded by thermogravimetric measurements. The fabricated and sintered materials were characterized by dilatometric study, scanning electron microscopy, X-ray diffraction, and stereological analysis. Further, life cycle assessment was supplied. Based on dilatometric tests, it was observed that Al₂O₃/ZrO₂ composites show a higher coefficient of thermal expansion than that resulting from the content of individual phases. The results of the life cycle analysis showed that the environmental loads (carbon footprint) resulting from the acquisition and processing of raw materials necessary for the production of sinters from Al₂O₃ and ZrO₂ are comparable to those associated with the production of plastic products such as polypropylene or polyvinyl chloride.

This paper focuses on the possibility of adapting the centrifugal slip casting method to obtain zirconia–alumina composite materials in the form of finished tube-shaped products. These types of products, due to their unique properties, can be utilised, for example, in the transport of aggressive substances, even in extreme temperatures or corrosive conditions. The study reports on the two series of zirconia–alumina composites differing in the content of ZrO₂—2.5 and 25 vol%. The fabricated and sintered materials were characterised using scanning electron microscopy (SEM), X-ray diffraction (XRD) and stereological analysis. Moreover, a life cycle assessment (LCA) was provided in accordance with the requirements of the ISO 14044 and EN 15805 standards. The obtained data clearly show that the centrifugal slip casting method allows obtaining samples with high density and extremely uniform distribution of the ZrO₂ phase in the alumina matrix. The stereological analysis results proved also that the addition of ZrO₂ is effective in reducing the growth of Al₂O₃ grains during the sintering process. The phase analysis carried out by means of XRD showed that during the sintering process, in the case of composites with a lower ZrO₂ content (2.5 vol%), the monoclinic to tetragonal transformation of ZrO₂ was total, while for samples containing 25 vol% ZrO₂, the monoclinic phase remained in a small amount in the final product.

The present work deals with the evaluation of the effect of ZrO₂ on the structure and selected properties of shapes obtained using the centrifugal slip casting method. The samples were made of alumina and zirconia. The applied technology made it possible to produce tubes with a high density reaching 99–100% after sintering. Very good bonding was obtained at the Al₂O₃/ZrO₂ interphase boundaries with no discernible delamination or cracks, which was confirmed by STEM observations. In the case of Al₂O₃/ZrO₂ composites containing 5 vol.% and 10 vol.% ZrO₂, the presence of equiaxial ZrO₂ grains with an average size of 0.25 µm was observed, which are distributed along the grain boundaries of Al₂O₃. At the same time, the composites exhibited a very high hardness of 22–23 GPa. Moreover, the environmental influences accompanying the sintering process were quantified. The impacts were determined using the life cycle analysis method, in the phase related to the extraction and processing of raw materials and the process of producing Al₂O₃/ZrO₂ composites. The results obtained show that the production of 1 kg of sintered composite results in greenhouse gas emissions of 2.24–2.9 kg CO₂ eq. which is comparable to the amount of emissions accompanying the production of 1 kg of Polyvinyl Chloride (PVC), Polypropylene (PP), or hot-rolled steel products.

This paper focuses on the verifying the possibility of producing Al₂O₃-ZrO₂ composite pipes with a gradient structure using centrifugal slip casting method. The aim of the research is to define the correlation between the rheological properties of aqueous suspensions of ceramic powders with different solid loading and obtaining the ZrO₂ phase gradient in the Al₂O₃ matrix. Such products, due to their unique properties, can be utilized in the transport of aggressive substances, even in extreme temperature or corrosive conditions. The suspensions and the sintered samples were characterized by: broad rheological analysis, scanning electron microscopy, X-ray diffraction, stereological analysis and Vickers hardness tests. The study reports on a series of samples produced of ceramic suspensions (70 vol.% Al₂O₃–30 vol.% ZrO₂) differing in the total solid loading in the range of 30–55 vol.%. The results clearly indicate that obtaining the gradient structure of ceramic-ceramic composite pipes is closely related to the rheological properties of the suspensions from which the samples are cast. The phase gradient is obtainable from suspensions 30–40 vol.%, in which the possibility of moving ZrO₂ particles relative to the Al₂O₃ is quite high—these suspensions are characterized by low viscosity and the dominance of viscous over elastic properties (G′ > G″).