A responsible approach towards sustainable development requires the use of environmentally friendly, low-carbon, and energy-intensive materials. One positive way is to use glass waste as a replacement for fine natural aggregate. For this purpose, the effects of adding glass cullet to the mechanical properties of mortar were carried out. The glass aggregate made from recycled post-consumer waste glass (food, medicine, and cosmetics packaging, including mostly bottles), were used. This experimental work included four different contents of fine glass cullet (5, 10, 15, and 20 wt.% of fine aggregate). The compressive, flexural, and split tensile strengths were evaluated. Moreover, the modulus of elasticity and Poisson coefficient were determined. The addition of glass sand aggregate increases the mechanical properties of mortar. When comparing the strength, the obtained improvement in split tensile strength was the least affected. The obtained effect for the increased analysed properties of the glass sand aggregate content has been rarely reported. Moreover, it was determined that by increasing the recycled glass sand aggregate content, the density of mortar decreased. In addition, the relationships between the properties for mortar containing glass sand aggregate were observed.

Foamed concrete shows excellent physical characteristics such as low self weight, relatively high strength and superb thermal and acoustic insulation properties. It allows for minimal consumption of aggregate, and by replacement of a part of cement by fly ash, it contributes to the waste utilization principles. For many years, the application of foamed concrete has been limited to backfill of retaining walls, insulation of foundations and roof tiles sound insulation. However, during the last few years, foamed concrete has become a promising material for structural purposes. A series of tests was carried out to examine mechanical properties of foamed concrete mixes without fly ash and with fly ash content. In addition, the influence of 25 cycles of freezing and thawing on the compressive strength was investigated. The apparent density of hardened foamed concrete is strongly correlated with the foam content in the mix. An increase of the density of foamed concrete results in a decrease of flexural strength. For the same densities, the compressive strength obtained for mixes containing fly ash is approximately 20% lower in comparison to the specimens without fly ash. Specimens subjected to 25 freeze‐thaw cycles show approximately 15% lower compressive strengths compared to the untreated specimens.

High-performance concrete has low tensile strength and brittle failure. In order to improve these properties of unreinforced concrete, the effects of adding recycled polypropylene fibers on the mechanical properties of concrete were investigated. The polypropylene fibers used were made from recycled plastic packaging for environmental reasons (long degradation time). The compressive, flexural and split tensile strengths after 1, 7, 14 and 28 days were tested. Moreover, the initial and final binding times were determined. This experimental work has included three different contents (0.5, 1.0 and 1.5 wt.% of cement) for two types of recycled polypropylene fibers. The addition of fibers improves the properties of concrete. The highest values of mechanical properties were obtained for concrete with 1.0% of polypropylene fibers for each type of fiber. The obtained effect of an increase in mechanical properties with the addition of recycled fibers compared to unreinforced concrete is unexpected and unparalleled for polypropylene fiber-reinforced concrete (69.7% and 39.4% increase in compressive strength for green polypropylene fiber (PPG) and white polypropylene fiber (PPW) respectively, 276.0% and 162.4% increase in flexural strength for PPG and PPW respectively, and 269.4% and 254.2% increase in split tensile strength for PPG and PPW respectively).

The progressive increase in the amount of glass waste produced each year in the world made it necessary to start the search for new recycling methods. This work summarizes the experimental results of the study on mortar samples containing dispersed reinforcement in the form of glass fibers, fully made from melted glass waste (bottles). Mortar mixes were prepared according to a new, laboratory-calculated recipe containing glass fibers, granite as aggregate, polycarboxylate-based deflocculant and Portland cement (52.5 MPa). This experimental work involved three different contents (600, 1200, and 1800 g/m³) of recycled glass fibers. After 28 days, the mechanical properties such as compressive, flexural, and split tensile strength were characterized. Furthermore, the modulus of elasticity and Poisson coefficient were determined. The initial and final setting times, porosity, and pH of the blends were measured. Images of optical microscopy (OM) were taken. The addition of glass fibers improves the properties of mortar. The highest values of mechanical properties were obtained for concrete with the addition of 1800 g/m³ of glass fibers (31.5% increase in compressive strength, 29.9% increase in flexural strength, and 97.6% increase in split tensile strength compared to base sample).

A series of static loading tests was performed to determine the fracture properties of foamed concrete of varying density. Beams with dimensions of 100×100×840 mm with a central notch were tested in three-point bending. Then, remaining halves of the specimens were tested again as un-notched beams in the same set-up with reduced distance between supports. The tests were performed in a hydraulic displacement controlled testing machine with a load capacity of 5 kN. Apart from measuring the loading and mid-span displacement, a crack mouth opening displacement (CMOD) was monitored. Based on the load – displacement curves of notched beams the values of fracture energy and tensile stress at failure were calculated. Subsequently, the flexural tensile strength was obtained on un-notched beams with dimensions of 100×100×420 mm. Moreover, cube specimens 150×150×150 mm were tested in compression to determine the compressive strength

In accordance with the principles of sustainable development, environmentally friendly, low-emission, and energy-intensive materials and technologies, as well as waste management, should be used. Concrete production is responsible for significant energy consumption and CO₂ production; therefore, it is necessary to look for new solutions in which components are replaced by other materials, preferably recycled. A positive way is to use glass waste. In order to determine the effect of a significant glass cullet content on the properties of concrete, glass powder was used as a filler and 100% glass aggregate. The cement–glass composite has low tensile strength and brittle failure. In order to improve tensile strength, the effects of adding polypropylene fibres on the mechanical properties of the composite were investigated. With the addition of 300, 600, 900, 1200, and 1500 g/m³ of fibres, which corresponds to 0.0625%, 0.1250%, 0.1875%, 0.2500%, and 0.3125% of cement mass, respectively, flexural strength increased compared with the base sample by 4.1%, 8.2%, 14.3%, 20.4%, and 26.5%, respectively, while the increase in splitting strength was 35%, 45%, 115%, 135%, and 185%, respectively. Moreover, with the addition of fibres, a decrease in slump by 25.9%, 39.7%, 48.3%, 56.9%, and 65.5%, respectively, compared with the reference specimen was determined.