Zinc oxide/reduced graphene oxide nanocomposites (ZnO/rGO) are synthesized via a simple one-pot solvothermal technique. The nanoparticle–nanorod turnability was achieved with the increase in GO additive, which was necessary to control the defect formation. The optimal defect in ZnO/rGO not only increased ZnO/rGO surface and carrier concentration, but also provided the alternative carrier pathway assisted with rGO sheet for electron–hole separation and prolonging carrier recombination. These properties are ideal for photodetection and photocatalytic applications. For photosensing properties, ZnO/rGO shows the improvement of photosensitivity compared with pristine ZnO from 1.51 (ZnO) to 3.94 (ZnO/rGO (20%)). Additionally, applying bending strain on ZnO/rGO enhances its photosensitivity even further, as high as 124% at r = 12.5 mm, due to improved surface area and induced negative piezoelectric charge from piezoelectric effect. Moreover, the photocatalytic activity with methylene blue (MB) was studied. It was observed that the rate of MB degradation was higher in presence of ZnO/rGO than pristine ZnO. Therefore, ZnO/rGO became a promising materials for different applications.

Fabrication of uniform vertically-aligned titanium dioxide nanorods (TiO₂ NRs) was achieved by hydrothermal growth on a fluorine-doped tin oxide (FTO) glass substrate. The substrate was coated by a TiO₂ seed layer composed of titanium (IV) butoxide (TBO) as a precursor in an HCl solution. To reduce the amount of toxic substances used in this work, a minimal amount of HCl was used. On a larger scale, this method would require less precursor and therefore be a cost-savings. The aim of the present work is to achieve high crystalline orientations of TiO₂ NRs for low quantities of both TBO precursor and HCl solutions. Results showed that the 0.7% TBO TiO₂ NRs after 1.5 h of hydrothermal treatment exhibited the optimal crystalline orientation along [001] while the (002) plane is the dominant facet. The results demonstrate high transmittance of visible light and well-formed crystalline structures that offer a fast electron pathway along the length of the TiO₂ NRs with less grain boundaries. Lastly, TiO₂ NRs and their growth mechanism are discussed. This work offers a promising hydrothermal method for growing well-aligned TiO₂ single-crystal NRs that can be employed in solar cell applications.

Cerium-oxide-nanoparticle-decorated zinc oxide was successfully prepared using a simple one-pot hydrothermal technique with different weight% Ce doping. It was found that an increase in Ce doping has an effect on the optical energy band-gap tunability. Ce dopant provides electron trapping on Ce/ZnO nanocomposites and also acts as a surface defect generator during hydrothermal processing. Additionally, a bi-metal oxide heterojunction forms, which acts as a charge separator to obstruct charge recombination and to increase the photodegradation performance. It was found that the methyl orange (MO) degradation performance improved with an increase in Ce doping. The decomposition of MO went from 69.42% (pristine ZnO) to 94.06% (7% Ce/ZnO) after 60 min under fluorescent lamp illumination.

Improving the antibacterial activity of biodegradable materials is crucial for combatting widespread drug-resistant bacteria and plastic pollutants. In this work, we studied polyaniline (PANI)-functionalized zinc oxide nanoparticles (ZnO NPs) to improve surface charges. A PANI-functionalized ZnO NP surface was prepared using a simple impregnation technique. The PANI functionalization of ZnO successfully increased the positive surface charge of the ZnO NPs. In addition, PANI-functionalized ZnO improved mechanical properties and thermal stability. Besides those properties, the water permeability of the bionanocomposite films was decreased due to their increased hydrophobicity. PANI-functionalized ZnO NPs were applied to thermoplastic starch (TPS) films for physical properties and antibacterial studies using Escherichia coli (E. coli) and Staphylococcus aureus (S. aureus). The PANI-functionalized ZnO bionanocomposite films exhibited excellent antibacterial activity for both E. coli (76%) and S. aureus (72%). This result suggests that PANI-functionalized ZnO NPs can improve the antibacterial activity of TPS-based bionanocomposite films.

Graphene quantum dots (GQDs) were synthesized using watermelon rind waste as a photoluminescent (PL) agent for ferric ion (Fe${}^{3+}$) detection and in vitro cellular bio-imaging. A green and simple one-pot hydrothermal technique was employed to prepare the GQDs. Their crystalline structures corresponded to the lattice fringe of graphene, possessing amide, hydroxyl, and carboxyl functional groups. The GQDs exhibited a relatively high quantum yield of approximately 37%. Prominent blue emission under UV excitation and highly selective PL quenching for Fe${}^{3+}$ were observed. Furthermore, Fe${}^{3+}$ could be detected at concentrations as low as 0.28 $\mathsf{\mu }$M (limit of detection), allowing for high sensitivity toward Fe${}^{3+}$ detection in tap and drinking water samples. In the bio-imaging experiment, the GQDs exhibited a low cytotoxicity for the HeLa cells, and they were clearly illuminated at an excitation wavelength of 405 nm. These results can serve as the basis for developing an environment-friendly, simple, and cost-effective approach of using food waste by converting them into photoluminescent nanomaterials for the detection of metal ions in field water samples and biological cellular studies.