A new approach to fabricate TiNi surfaces combining the advantages of both monolithic and porous materials for implants is used in this work. New materials were obtained by depositing a porous TiNi powder onto monolithic TiNi plates followed by sintering at 1200 °C. Then, further modification of the material surface with a high-current-pulsed electron beam (HCPEB) was carried out. Three materials obtained (one after sintering and two after subsequent beam treatment by 30 pulses with different pulse energy) were studied by XRD, SEM, EDX, surface profilometry, and by means of electrochemical measurements, including OCP and EIS. Structural and compositional changes caused by HCPEB treatment were investigated. Surface properties of the samples during their storage in saline for 10 days were studied and a model experiment with cell growth (MCF-7) was carried out for the unmodified sample with an electron beam to detect cell appearance on different surface locations.

Alloys based on TiNi are widely used in various fields of technology and medicine. In the present work, we report on the preparation of TiNi-alloy-based wire with the shape-memory effect, which was used for compression clips for surgery. The composition and structure of the wire and its martensitic and physical–chemical properties were studied using SEM, TEM, optic microscopy, profilometry, mechanical tests, etc. The TiNi alloy was found to consist of B2 and B19′ and secondary-phase particles of Ti₂Ni, TiNi₃ and Ti₃Ni₄. Its matrix was slightly enriched in Ni (50.3 at.% of Ni). A homogeneous grain structure was revealed (an average grain size of 19 ± 0.3 μm) with equal quantities of grain boundaries of special and general types. The surface oxide layer provides improved biocompatibility and promotes the adhesion of protein molecules. Overall, the obtained TiNi wire was concluded to exhibit martensitic, physical and mechanical properties suitable for its use as an implant material. The wire was then used for manufacturing compression clips with the shape-memory effect and applied in surgery. The medical experiment that involved 46 children demonstrated that the use of such clips in children with double-barreled enterostomies permitted improvement in the results of surgical treatment.

The mechanical characteristics of a monolithic (non-porous) crystalline or amorphous material are described by a well-defined set of quantities. It is possible to change the mechanical properties by introducing porosity into this material; as a rule, the strength values decrease with the introduction of porosity. Thus, porosity can be considered an additional degree of freedom that can be used to influence the hardness, strength and plasticity of the material. In the present work, using porous crystalline NiTi as an example, it is shown that the mechanical characteristics such as the Young’s modulus, the yield strength, the ultimate tensile strength, etc., demonstrate a pronounced dependence on the average linear size $\overline{l}$ of the pores. For the first time, an empirical equation is proposed that correctly reproduces the dependence of the mechanical characteristics on the porosity $\varphi$ and on the average linear size $\overline{l}$ of the pores in a wide range of sizes: from nano-sized pores to pores of a few hundred microns in size. This equation correctly takes into account the limit case corresponding to the monolithic material. The obtained results can be used directly to solve applied problems associated with the design of materials with the necessary combination of physical and mechanical characteristics, in particular, porous metallic biomaterials.