Alloys based on TiNi are widely used in various fields of technology and medicine. In the present work, we report on the preparation of TiNi-alloy-based wire with the shape-memory effect, which was used for compression clips for surgery. The composition and structure of the wire and its martensitic and physical–chemical properties were studied using SEM, TEM, optic microscopy, profilometry, mechanical tests, etc. The TiNi alloy was found to consist of B2 and B19′ and secondary-phase particles of Ti₂Ni, TiNi₃ and Ti₃Ni₄. Its matrix was slightly enriched in Ni (50.3 at.% of Ni). A homogeneous grain structure was revealed (an average grain size of 19 ± 0.3 μm) with equal quantities of grain boundaries of special and general types. The surface oxide layer provides improved biocompatibility and promotes the adhesion of protein molecules. Overall, the obtained TiNi wire was concluded to exhibit martensitic, physical and mechanical properties suitable for its use as an implant material. The wire was then used for manufacturing compression clips with the shape-memory effect and applied in surgery. The medical experiment that involved 46 children demonstrated that the use of such clips in children with double-barreled enterostomies permitted improvement in the results of surgical treatment.

A new approach to fabricate TiNi surfaces combining the advantages of both monolithic and porous materials for implants is used in this work. New materials were obtained by depositing a porous TiNi powder onto monolithic TiNi plates followed by sintering at 1200 °C. Then, further modification of the material surface with a high-current-pulsed electron beam (HCPEB) was carried out. Three materials obtained (one after sintering and two after subsequent beam treatment by 30 pulses with different pulse energy) were studied by XRD, SEM, EDX, surface profilometry, and by means of electrochemical measurements, including OCP and EIS. Structural and compositional changes caused by HCPEB treatment were investigated. Surface properties of the samples during their storage in saline for 10 days were studied and a model experiment with cell growth (MCF-7) was carried out for the unmodified sample with an electron beam to detect cell appearance on different surface locations.

This work is devoted to the physical and mechanical properties of porous alloys based on TiNi alloyed with different amounts of Cu additive. We show that by doping a porous TiNi alloy with copper instead of nickel, it is possible to obtain characteristics acceptable for use in implantology and superior to those of known porous TiNi alloys. Cu addition in the range from 1 to 10 at.% is shown to optimize the properties of tested alloys. There is a decrease in the minimal martensitic transformation stress ${\tau }_{M_s}^{min}$ from 37 to 17 MPa when compared to initial unalloyed TiNi. Alloys with 3 and 6 at.% of Cu are found to be optimal for use in medical practice. Along with a wide temperature range of reversible deformations that cover the range of operating temperatures (273–313 K), such alloys demonstrate their martensitic transformation stress values below 28 MPs. This permits to model implantable structures of complex configuration from such materials under a certain temperature regime.