Rice hull is a residue from agro-industry that can be used to produce nanocellulose. We produced nanocellulose from rice hulls through bleaching (with a 5% NaOH solution followed by a peracetic acid solution) and acid hydrolysis at a mild temperature (45ºC) followed by ultrasonication. We investigated the microstructure, crystallinity and thermal stability of these materials and studied their effects on the properties of starch films. After bleaching, the compact structure around the cellulosic fibers was removed, and the lignin content of the residue decreased from 7.22 to 4.22%. The obtained nanocellulose presented a higher crystallinity (up 70%), higher thermal stability than the raw material and lignin contents below 0.35%. The nanocellulose formed interconnected webs of tiny fibers (< 100 nm in diameter), which decreased the opacity, water vapor permeability and improved the mechanical properties when added as reinforcement in the starch films.

The aim of this work was to manufacture the biodegradable nanocomposite films by extrusion from different combinations of cassava starch, xanthan gum and nanoclays (sodium montmorillonite - MMT- Na) and to characterize them according to their microstructure, optical, mechanical and barrier properties. Films were manufactured from nine starch/xanthan/nanoclay combinations, containing glycerol as plasticizer. Scanning electron microscopy (SEM) of the starch-xanthan extruded films showed reticulated surface and smooth interior, indicating that the gum was mostly concentrated on the surface of the films, while starch/xanthan/nanoclays films showed a more homogeneous surface, suggesting that the introduction of nanoclays provided a better biopolymeric interaction. In general, nanoclays addition (2.5 - 5.0, w%) generated more transparent and resistant films, with lower water vapor permeabilities and lower water sorption capacities and xanthan gum addition improved the elongation ofa starch films.