The aim of this study was to compare the physicochemical properties, filling ability, and antibacterial activity of a premixed calcium silicate-based sealer to those of a powder–liquid bioceramic sealer. Ceraseal (CS) and BioRoot (BR) materials were analyzed using scanning electron microscopy and energy-dispersive X-ray spectroscopy at 7 and 14 d of immersion in distilled water. The filling ability of the two sealers as well as the water contact angle, solubility, flow, roughness, crystalline microstructure, pH, and compressive strength were also evaluated. The antibacterial activity was assessed through an agar diffusion as well as through direct tests. All the results were statistically analyzed using one-way or two-way analysis of variance tests. Statistically significant lower void percentages were observed for CS at 2 and 8 mm from the working length (WL) compared to those for the BR group, whilst no significant difference was observed at 5 mm from the WL. BR sealer showed higher alkaline pH, rougher surface, lower water contact angle values, lower flowability, and higher solubility compared to CS. BR showed globular and needle-like crystalline microstructure, whilst CS had globular and flower-like crystalline microstructure up to 72 h. No statistical difference was found for the compressive strength between the two sealers. BR and CS showed no antibacterial effect against Enterococcus faecalis after 3 h, whilst both sealers showed antibacterial capacity after 24 and 72 h. BR demonstrated higher antibacterial activity after 24 h. In conclusion, the use of bioceramic sealers may play an important role in controlling bacterial growth. Moreover, CS may have superior filling ability and lower solubility than the BioRoot sealer due to its specific chemical composition and mixing method.

(1) Background: This study investigated the effect of the adhesive layer thickness and the length of resin tags on dentin bond strength of five universal adhesives applied in self-etch mode. (2) Methods: One hundred and fifty extracted human third molars were used. Five different universal adhesives were applied in self-etch mode on the dentin surface. Half of the specimens were subjected to an aging procedure for six months. A shear bond strength (SBS) test was performed and the results were statistically analyzed with a t-test and one-way ANOVA test. Scanning electron microscopy (SEM) was executed to measure the adhesive layer thickness and tag depth. (3) Results: No statistical differences were found between the five adhesive systems after a 24 h storage period, regardless of layer thickness and tag depth (p < 0.05). After 6 months of aging in water at 37 °C, Iperbond Max and Scotchbond Universal preserved the bond strength over time (p < 0.05), whilst the SBS of Iperbond Ultra, FuturaBond M+, and Ibond Universal decreased significantly after the aging period. No relation was observed between the adhesive thickness or tags’ length on SBS. (4) Conclusions: Within the limitation of this study, the stability over time of the bond strength of universal adhesives depends on their compositions regardless of the adhesive layer thickness and/or tags’ length.

The purpose of the present study was to evaluate the physicochemical properties and antibacterial activity of three calcium silicate cements. Mineral trioxide aggregate (MTA Biorep “BR”), Biodentine (BD) and Well-Root PT (WR) materials were investigated using scanning electron microscopy (SEM) at 24, 72 and 168 h of immersion in phosphate buffered saline (PBS). The antibacterial activity against Enterococcus faecalis (E. faecalis), the solubility, roughness, pH changes and water contact angle were also analyzed. All results were statistically analyzed using a one-way analysis of variance test. Statistically significant lower pH was detected for BD than WR and BR (p < 0.05). No statistical difference was found among the three materials for the efficacy of kill against E. faecalis (p > 0.05). Good antibacterial activity was observed (kill 50% of bacteria) after 24 h of contact. The wettability and the roughness of BR were higher than for the other cements (p < 0.05). BD was more soluble than WR and BR (p < 0.05). In conclusion, the use of bioceramic cements as retrograde materials may play an important role in controlling bacterial growth and in the development of calcium phosphate surface layer to support healing. Moreover, the premixed cement was easier to use than powder–liquid cement.

The aim of the present in vitro study was to evaluate specific mechanical and physicochemical properties of two calcium silicate based sealers, (AH Plus Bioceramic “AHPB”; Well-Root ST “WRST”), and a conventional resin sealer (AH Plus “AHP”). These aims were accomplished by assessing the porosity, pH, compression strength, roughness, wettability and cell attachment of the tested materials. The results were compared statistically using the one-way ANOVA test. Higher pH values were obtained in both AHPB and WRST compared to AHP at 3, 24 and 72 h (p < 0.05). A greater level of porosity and wettability was detected for both AHPB and WRST compared to the resin sealer AHP (p < 0.05). Evident cell growth characterized by elongated morphology was observed on the surface of AHPB and WRST, while only a thin layer of cells was seen on the surface of AHP. A significant lower compression strength and modulus were obtained in the specimens created using AHPB compared to those made with AHP and WRST (p < 0.05). The removal of calcium silicates may be quite tricky during endodontic retreatment. In conclusion, considering the limitations of the present in vitro study, both calcium silicate sealers demonstrated good physicochemical properties. However, the lower compression strength and modulus of AHPB may facilitate its removal and make the retreatment procedures considerably easier.

This study aimed at evaluating the physicochemical and biological properties of experimental epoxy-resin sealers containing polyphenols such as resveratrol and pyrogallol. A conventional epoxy resin (OB) was modified by adding different concentrations of resveratrol (RS) or pyrogallol (PY) to its composition. Antibacterial and antioxidant activities, mechanical properties, along with wettability and morphological changes were investigated. The results were statistically analyzed using ANOVA and multiple comparison tests (α = 0.05). The incorporation of the tested polyphenols into the epoxy resin enhanced its mechanical properties. PY demonstrated much better antioxidant and antibacterial activities than RS, which were associated with a higher release of PY. In contrast, PY showed a higher cytotoxicity than OB and OB doped with RS. OB containing PY presented a rougher surface and higher water absorption than OB doped with RS. Both tested polyphenols caused no notable changes to the overall porosity of OB. Resveratrol and pyrogallol may not only influence the morphology and mechanical properties of epoxy-resin sealers, but could also enhance antioxidant activity and antibacterial effects against Enterococcus faecalis. Most epoxy-resin sealers currently available in the market can be considered as “passive” materials. Thus, doping their composition with specific polyphenols may be a suitable strategy to confer some antibacterial properties, antioxidant potential, along with improvement of some mechanical properties.

The delayed damage model has been introduced by Allix and Deü [1] as a way to overcome spurious mesh dependency in failure analysis involving damage and dynamic loading. The damage rate is bounded through a time scale which, combined with the wave speed, introduces implicitly a length scale. In this paper, the delayed damage model is analyzed through numerical experiments on three different loading cases of a bar: a slow loading leading to a dynamic failure, pulses and impact. We observe and discuss the load level needed for failure (and the dependence of this load level with respect to the loading rate), as well as the dissipation and extent of the fully damaged zone at failure. Observations lead to the following conclusions. First, the delayed damage model has no regularization effect for a dynamic failure initiating from rest. Second, for pulse loadings, the loading rate has no influence on the minimal load level needed for failure (even though the delayed damage model is a time-dependent model), and beyond this minimal load level for failure, the extent of the fully damage zone rises, proportionally to the length scale. Third, regarding the impact, the velocity needed to reach failure depends only the time-independent parameters of the models, and not the ones linked to the delayed damage.