The enhanced carbon footprint of the construction sector has created the need for CO₂ emission control and mitigation. CO₂ emissions in the construction sector are influenced by a variety of factors, including raw material preparation, cement production, and, most notably, the construction process. Thus, using biobased constituents in cement could reduce CO₂ emissions. However, biobased constituents can degrade and have a negative impact on cement performance. Recently, carbonised biomass known as biochar has been found to be an effective partial replacement for cement. Various studies have reported improved mechanical strength and thermal properties with the inclusion of biochar in concrete. To comprehend the properties of biochar-added cementitious materials, the properties of biochar and their effect on concrete need to be examined. This review provides a critical examination of the mechanical and thermal properties of biochar and biochar-added cementitious materials. The study also covers biochar’s life cycle assessment and economic benefits. Overall, the purpose of this review article is to provide a means for researchers in the relevant field to gain a deeper understanding of the innate properties of biochar imparted into biochar-added cementitious materials for property enhancement and reduction of CO₂ emissions.

The present study is aimed at investigating the effect of hybridisation on Kevlar/E-Glass based epoxy composite laminate structures. Composites with 3 mm thickness and 16 layers of fibre (14 layers of E-glass centred and 2 outer layers of Kevlar) were fabricated using compression moulding technique. The fibre orientation of the Kevlar layers had 3 variations (0, 45 and 60°), whereas the E-glass fibre layers were maintained at 0° orientation. Tensile, flexural, impact (Charpy and Izod), interlaminar shear strength and ballistic impact tests were conducted. The ballistic test was performed using a gas gun with spherical hard body projectiles at the projectile velocity of 170 m/s. The pre- and post-impact velocities of the projectiles were measured using a high-speed camera. The energy absorbed by the composite laminates was further reported during the ballistic test, and a computerised tomographic scan was used to analyse the impact damage. The composites with 45° fibre orientation of Kevlar fibres showed better tensile strength, flexural strength, Charpy impact strength, and energy absorption. The energy absorbed by the composites with 45° fibre orientation was 58.68 J, which was 14% and 22% higher than the 0° and 60° oriented composites.