A co-based porous metal-organic framework (MOF) of zeolitic imidazolate framework-67 (ZIF-67) and carbon nanofibers (CNFs) was utilized to prepare a ZIF-67/CNFs composite via a one-pot synthesis method. Scanning electron microscopy (SEM), energy dispersive X-ray spectroscopy (EDX), and X-ray diffraction (XRD) were employed to investigate the morphology, structure, and composition of the resulting composite. A novel high-performance non-enzymatic electrochemical sensor was constructed based on the ZIF-67/CNFs composite. The ZIF-67/CNFs based sensor exhibited enhanced electrocatalytic activity towards H₂O₂ compared to a pure ZIF-67-based sensor, due to the synergistic effects of ZIF-67 and CNFs. Meanwhile, chronoamperometry was utilized to explore the detection performance of the sensor. Results showed the sensor displayed high-efficiency electrocatalysis towards H₂O₂ with a detection limit of 0.62 μM (S/N = 3), a sensitivity of 323 µA mM⁻¹ cm⁻², a linear range from 0.0025 to 0.19 mM, as well as satisfactory selectivity and long-term stability. Furthermore, the sensor demonstrated its application potential in the detection of H₂O₂ in food.

Sabina chinensis is a valuable reforestation conifer and traditional medicinal plant. In order to retain the physiological and pharmacological activities of the plant and obtain a fibrous material with better antibacterial properties, a mixed solvent of dichloromethane and N,N′-dimethylformamide was used to obtain the leaf extracts, and Sabina chinensis leaf extract (ScLE)-loaded PCL/PVP microfibers were successfully fabricated by electrospinning. The whole preparation process was carried out at room temperature to avoid deterioration of active ingredients. From the antibacterial activity test, it was observed that ScLE-loaded polycaprolactone/polyvinylpyrrolidone (PCL/PVP) microfibers had potential antibacterial activity against both Gram-positive and Gram-negative bacteria stains. The morphological properties of the prepared microfibers were observed by SEM. As the proportion of ScLE increased, the fiber diameter gradually increased and the surface was smooth. The excess ScLE addition caused the formation of beads during electrospinning. Considering different characterization results, 33% (v/v) addition of ScLE to the spinning solution was the optimum ratio. The winding structure obtained by the interaction of components in ScLE with PCL and PVP was confirmed by FTIR, XRD and WCA tests, which indicated that ScLE-loaded microfibers possessed excellent thermal stability, tear resistance and degradation resistance. It is expected that the prepared composite microfibers have potential applications as robust antibacterial meshes and films in the fields of biomedicine and air purification.

Electrospun nanofiber composites derived from polyurethane (PU) or polyethylene oxide (PEO) have demonstrated exceptional chemical and thermal stability.

The treatment of diabetic wounds remains a formidable clinical challenge worldwide. Because of persistent inflammatory reaction, excessive oxidative stress, cell dysfunction, poor blood microcirculation and other microvascular complications, diabetic wounds often fall into inflammatory circulation and are difficult to heal, making patients confront the risk of amputation. In this study, silver complex nanoparticles with Resina Draconis extract and Rhodiola rosea L. extract were loaded in situ onto thermoplastic polyurethane nanofibers to develop a multifunctional electrospun nanofiber wound dressing with excellent mechanical properties, superior water absorption and breathability, good coagulation promoting activity, strong antibacterial performance and antioxidant properties. This wound dressing could effectively enhance the migration and proliferation of fibroblasts, reduce the increased thickness of regenerated epidermis caused by diabetes, and the high expression and high lipid peroxidation levels of IL-1 β, IL-6, TNF α, iNOS and MMP-9, and raise the low expression of VEGF, which shows great potential to accelerate the wound healing of diabetic mouse models. The wound healing rate reached about 87.92%, close to the non-diabetic group. Our findings suggest a breakthrough in diabetic wound care, offering a viable solution to a long-standing medical shackle.

The main core of wound treatment is cell growth and anti-infection. To accelerate the proliferation of fibroblasts in the wound and prevent wound infections, various strategies have been tried. It remains a challenge to obtain good cell proliferation and antibacterial effects. Here, human hair kerateine (HHK)/poly(ethylene oxide) (PEO)/poly(vinyl alcohol) (PVA) nanofibers were prepared using cysteine-rich HHK, and then, silver nanoparticles (AgNPs) were in situ anchored in the sulfur-containing amino acid residues of HHK. After the ultrasonic degradation test, HHK/PEO/PVA nanofibrous mats treated with 0.005-M silver nitrate were selected due to their relatively complete structures. It was observed by TEM-EDS that the sulfur-containing amino acids in HHK were the main anchor points of AgNPs. The results of FTIR, XRD and the thermal analysis suggested that the hydrogen bonds between PEO and PVA were broken by HHK and, further, by AgNPs. AgNPs could act as a catalyst to promote the thermal degradation reaction of PVA, PEO and HHK, which was beneficial for silver recycling and medical waste treatment. The antibacterial properties of AgNP-HHK/PEO/PVA nanofibers were examined by the disk diffusion method, and it was observed that they had potential antibacterial capability against Gram-positive bacteria, Gram-negative bacteria and fungi. In addition, HHK in the nanofibrous mats significantly improved the cell proliferation of NIH3T3 cells. These results illustrated that the AgNP-HHK/PEO/PVA nanofibrous mats exhibited excellent antibacterial activity and the ability to promote the proliferation of fibroblasts, reaching our target applications.