High-Mn austenitic steels have been recently developed for a storage or transportation application of liquefied natural gas (LNG) in cryogenic fields. Since the structural materials are subjected to extremely low temperature, it requires excellent mechanical properties such as high toughness strength. In case of high-Mn steels, twinning deformation during the cold-working process is known to increase strength yet may cause embrittlement of heavy deformed twin and anisotropic properties. In this study, a recrystallization process through appropriate annealing heat treatments after cold-working was applied to improve the impact toughness for high-Mn austenitic steels. Microstructure and mechanical properties were performed to evaluate the influence of cold-worked and annealed high-Mn austenitic steels. Mechanical properties, such as strength and impact toughness, were investigated by tensile and Charpy impact tests. The relationship between strength and impact toughness was determined by microstructure analysis such as the degree of recrystallization and grain refinement. Consequently, both elongation and toughness were significantly increased after cold-working and subsequent annealing at 1000 °C as compared to the as-received (hot-rolled) specimen. The cold-worked high-Mn steel was completely recrystallized at 1000 °C and showed a homogeneous micro-structure with high-angle grain boundaries.

This study investigated the mechanical properties of steel in flanges, with the goal of obtaining high strength and high toughness. Quenching was applied alone or in combination with tempering at one of nine combinations of three temperatures T_TEM and durations t_TEM. Cooling rates at various flange locations during quenching were first estimated using finite element method simulation, and the three locations were selected for mechanical testing in terms of cooling rate. Microstructures of specimens were observed at each condition. Tensile test and hardness test were performed at room temperature, and a Charpy impact test was performed at −46 °C. All specimens had a multiphase microstructure composed of matrix and secondary phases, which decomposed under the various tempering conditions. Decrease in cooling rate (CR) during quenching caused reduction in hardness and strength but did not affect low-temperature toughness significantly. After tempering, hardness and strength were reduced and low-temperature toughness was increased. Microstructures and mechanical properties under the various tempering conditions and CRs during quenching were discussed. This work was based on the properties directly obtained from flanges under industrial processes and is thus expected to be useful for practical applications.

High-strength steel is widely used in hot forging products for application to the oil and gas industry because it has good mechanical properties under severe environment. In order to apply to the extreme environment industry requiring high temperature and high pressure, heat treatments such as austenitizing, quenching and tempering are required. The microstructure of high-strength steel after heat treatment has various microstructures such as Granular Bainite (GB), Acicular Ferrite (AF), Bainitic Ferrite (BF), and Martensite (M) depending on the heat treatment conditions and cooling rate. Especially in large forged products, the difference in microstructure occurs due to the difference in the forging ratio depending on the location and the temperature gradient according to the thickness during post-heat treatment. Therefore, this study attempted to quantitatively analyze various phases of F70 high-strength steel according to the austenitizing temperature and hot forging ratio using the existing EBSD analysis method. In addition, the correlation between microstructure and mechanical properties was investigated through various phase analysis and fracture behavior of high-strength steel. We found that various microstructures of strength steel depend on the austenitizing temperature and hot forging ratio, and influence the mechanical properties and fracture behavior.