18Ni-300 maraging steel produced by the selective laser melting (SLM) process has a unique microstructure that is different from that of the same alloy processed by conventional methods. In this paper, maraging steels were fabricated by the selective laser melting process and their microstructures and mechanical properties were investigated in terms of post heat treatment conditions. Moreover, the effect of different heat treatments on the mechanical anisotropy was studied in detail. The micro Vickers hardness in the as-built state was around 340 Hv and could be increased to approximately 600 Hv by aging heat treatments. It was found that the solution heat treatment was not necessary to obtain a fully hardened state. From tensile tests of the maraging steels heat treated with different conditions, it was found that the highest strength was achieved by aging and solution treatment (ST) temperatures lower than the commonly used temperatures. In the direction parallel to the laser scanning, the highest ultimate tensile strength was obtained when 450 °C aging was done without solution heat treatment. In the other two directions tested, i.e., directions normal to the building and 45 degrees to the laser scanning direction, the highest tensile strength was obtained when aging was done at 450 °C after 750 °C solution treatment.

The present study is to investigate the effect of post heat treatment on the microstructures and mechanical properties of a submerged-arc-welded 304 stainless steel. The base material consisted of austenite and long strips of delta-ferrite surrounded by Cr-carbide, and the welds consisted of delta ferrite and austenite matrix. For the heat treatment at 850 °C or lower, Cr-carbides were precipitated in the weld metal resulting in the reduction of elongation. The strength, however, was slightly reduced despite the presence of Cr-carbides and this could possibly be explained by the relaxation of internal stress and the weakening of particle hardening. In the heat treatment at 1050 °C, the dissolution of Cr-carbide and disappearance of delta ferrite resulted in the lower yield strength and higher elongation partially assisted from deformation-induced martensitic transformation. Consequently, superior property in terms of fracture toughness was achieved by the heat treatment at 1050 °C, suggesting that the mechanical properties of the as-weld metal can be enhanced by controlling the post weld heat treatment.

High-Mn austenitic steels have been recently developed for a storage or transportation application of liquefied natural gas (LNG) in cryogenic fields. Since the structural materials are subjected to extremely low temperature, it requires excellent mechanical properties such as high toughness strength. In case of high-Mn steels, twinning deformation during the cold-working process is known to increase strength yet may cause embrittlement of heavy deformed twin and anisotropic properties. In this study, a recrystallization process through appropriate annealing heat treatments after cold-working was applied to improve the impact toughness for high-Mn austenitic steels. Microstructure and mechanical properties were performed to evaluate the influence of cold-worked and annealed high-Mn austenitic steels. Mechanical properties, such as strength and impact toughness, were investigated by tensile and Charpy impact tests. The relationship between strength and impact toughness was determined by microstructure analysis such as the degree of recrystallization and grain refinement. Consequently, both elongation and toughness were significantly increased after cold-working and subsequent annealing at 1000 °C as compared to the as-received (hot-rolled) specimen. The cold-worked high-Mn steel was completely recrystallized at 1000 °C and showed a homogeneous micro-structure with high-angle grain boundaries.

This study investigated the mechanical properties of steel in flanges, with the goal of obtaining high strength and high toughness. Quenching was applied alone or in combination with tempering at one of nine combinations of three temperatures T_TEM and durations t_TEM. Cooling rates at various flange locations during quenching were first estimated using finite element method simulation, and the three locations were selected for mechanical testing in terms of cooling rate. Microstructures of specimens were observed at each condition. Tensile test and hardness test were performed at room temperature, and a Charpy impact test was performed at −46 °C. All specimens had a multiphase microstructure composed of matrix and secondary phases, which decomposed under the various tempering conditions. Decrease in cooling rate (CR) during quenching caused reduction in hardness and strength but did not affect low-temperature toughness significantly. After tempering, hardness and strength were reduced and low-temperature toughness was increased. Microstructures and mechanical properties under the various tempering conditions and CRs during quenching were discussed. This work was based on the properties directly obtained from flanges under industrial processes and is thus expected to be useful for practical applications.

This study investigated microstructure and mechanical properties of high manganese steel sheet fabricated by gas tungsten arc welding (GTAW). The weld zone showed longitudinal coarse grains due to the coalescence of columnar dendrites grown into the direction of heat source, and the HAZ showed equiaxed coarser grains than the base metal due to the thermal effect of GTAW process. Mn segregation occurred in the inter-dendritic regions of the weld zone and Mn depletion thus occurred in the weld matrix. Although the stacking fault energy is expected to be lowered due to the Mn depletion, no noticeable change in the initial phase and deformation mechanism was found in the weld matrix. Lower hardness and strength were shown in the weld zone than the base metal, which was caused by the coarser grain size. The negative strain rate sensitivity observed in the weld zone and the base metal is considered to have originated from the negative strain rate dependency of twinning nucleation stress.