High-Mn austenitic steels have been recently developed for a storage or transportation application of liquefied natural gas (LNG) in cryogenic fields. Since the structural materials are subjected to extremely low temperature, it requires excellent mechanical properties such as high toughness strength. In case of high-Mn steels, twinning deformation during the cold-working process is known to increase strength yet may cause embrittlement of heavy deformed twin and anisotropic properties. In this study, a recrystallization process through appropriate annealing heat treatments after cold-working was applied to improve the impact toughness for high-Mn austenitic steels. Microstructure and mechanical properties were performed to evaluate the influence of cold-worked and annealed high-Mn austenitic steels. Mechanical properties, such as strength and impact toughness, were investigated by tensile and Charpy impact tests. The relationship between strength and impact toughness was determined by microstructure analysis such as the degree of recrystallization and grain refinement. Consequently, both elongation and toughness were significantly increased after cold-working and subsequent annealing at 1000 °C as compared to the as-received (hot-rolled) specimen. The cold-worked high-Mn steel was completely recrystallized at 1000 °C and showed a homogeneous micro-structure with high-angle grain boundaries.

For cryogenic applications, materials must be cautiously selected because of a drastic degradation in the mechanical properties of materials when they are exposed to very low temperatures. We have developed a new technique using a cold-working and surface-cracking process to overcome such degradation of mechanical properties at low temperatures. This technique intentionally induced surface-cracks in cold-worked austenitic stainless steels and resulted in a significant increase in both strength and fracture at low temperatures. According to the microstructure observations, dissipation of the crack propagation energy with surface-cracks enhanced the impact toughness, showing a ductile fracture mode in even the cryogenic temperature region. In particular, we obtained the high strength and toughness materials by a surface-cracking technique at 5% cold-worked specimen with surface-cracks.

High-strength steel is widely used in hot forging products for application to the oil and gas industry because it has good mechanical properties under severe environment. In order to apply to the extreme environment industry requiring high temperature and high pressure, heat treatments such as austenitizing, quenching and tempering are required. The microstructure of high-strength steel after heat treatment has various microstructures such as Granular Bainite (GB), Acicular Ferrite (AF), Bainitic Ferrite (BF), and Martensite (M) depending on the heat treatment conditions and cooling rate. Especially in large forged products, the difference in microstructure occurs due to the difference in the forging ratio depending on the location and the temperature gradient according to the thickness during post-heat treatment. Therefore, this study attempted to quantitatively analyze various phases of F70 high-strength steel according to the austenitizing temperature and hot forging ratio using the existing EBSD analysis method. In addition, the correlation between microstructure and mechanical properties was investigated through various phase analysis and fracture behavior of high-strength steel. We found that various microstructures of strength steel depend on the austenitizing temperature and hot forging ratio, and influence the mechanical properties and fracture behavior.

Functionally graded materials (FGMs) have a characteristic whereby the composition and structure are gradually changed according to the location, and the mechanical properties or chemical properties are gradually changed accordingly. In this study, using a multi-hopper direct energy deposition 3D printer, an FGM material whose composition changes gradually from P21 ferritic steel to stainless steel 316L austenitic steel was fabricated. From optical microscope, scanning electron microscope, and X-ray diffraction analysis, columnar, cell, and point type solidified micro-structure and precipitations were observed depending on the deposited compositions. Electron probe microanalysis and electron backscatter diffraction analysis confirmed the component segregation, ferrite austenite volume fraction and phase distribution behavior according to compositions. In the FGM specimen test, the ultimate tensile strength of STS316L, which was the most fragile, was measured, and the toughness was measured for the notch area, which did not represent the FGM characteristics. Hardness showed changes according to FGM position and was suitable for FGM analysis. The maximum hardness was measured in the FGM duplex area, which was caused by grain refinement, precipitate strengthening, and solid solution strengthening. In nuclear power plant welds high strength can cause adverse effects on stress corrosion cracking, and caution is needed in applying FGM.

High-manganese steel (high-Mn) is valuable for its excellent mechanical properties in cryogenic environments, making it essential to understand its deformation behavior at extremely low temperatures. The deformation behavior of high-Mn steels at extremely low temperatures depends on the stacking fault energy (SFE) that can lead to the formation of deformation twins or transform to ε-martensite or α′-martensite as the temperature decreases. In this study, submerged arc welding (SAW) was applied to fabricate thick pipes for cryogenic industry applications, but it may cause problems such as an uneven distribution of manganese (Mn) and a large weldment. To address these issues, post-weld heat treatment (PWHT) is performed to achieve a homogeneous microstructure, enhance mechanical properties, and reduce residual stress. It was found that the difference in Mn content between the dendrite and interdendritic regions was reduced after PWHT, and the SFE was calculated. At cryogenic temperatures, the SFE decreased below 20 mJ/m², indicating the martensitic transformation region. Furthermore, an examination of the deformation behavior of welded high-Mn steels was conducted. This study revealed that the tensile deformed, as-welded specimens exhibited ε and α′-martensite transformations at cryogenic temperatures. However, the heat-treated specimens did not undergo α′-martensite transformations. Moreover, regardless of whether the specimens were subjected to Charpy impact deformation before or after heat treatment, ε and α′-martensite transformations did not occur.

This study investigated the low-temperature fracture behavior of an 80-mm-thick low-carbon steel plate welded by submerged arc. The relationship between impact absorbed energy and ductility–brittle transition temperature (DBTT) based on the microstructures was evaluated through quantitative analysis on grain size and complex constituent phases using advanced EBSD technique. The microstructure formed differently depending on the heat affections, which determined fracture properties in a low-temperature environment. Among the various microstructures of the heat-affected zone (HAZ), acicular ferrite has the greatest resistance to low-temperature impact due to its fine interlocking formation and its high-angle grain boundaries.