Acoustic signals are important markers to monitor physiological and pathological conditions, e.g., heart and respiratory sounds. The employment of traditional devices, such as stethoscopes, has been progressively superseded by new miniaturized devices, usually identified as microelectromechanical systems (MEMS). These tools are able to better detect the vibrational content of acoustic signals in order to provide a more reliable description of their features (e.g., amplitude, frequency bandwidth). Starting from the description of the structure and working principles of MEMS, we provide a review of their emerging applications in the healthcare field, discussing the advantages and limitations of each framework. Finally, we deliver a discussion on the lessons learned from the literature, and the open questions and challenges in the field that the scientific community must address in the near future.

In the present study, two commercial typologies of microfibrillated cellulose (MFC) (Exilva and Celish) with 2% wt % were firstly melt-compounded at the laboratory scale into polylactic acid (PLA) by a microcompounder. To reach an MFC proper dispersion and avoid the well-known aglomeration problems, the use of two kinds of biobased plasticisers (poly(ethylene glycol) (PEG) and lactic acid oligomer (OLA)) were investigated. The plasticizers had the dual effect of dispersing the MFC, and at the same time, they counterbalanced the excessive stiffness caused by the addition of MFC to the PLA matrix. Several preliminaries dilution tests, with different aqueous cellulose suspension/plasticizer weight ratios were carried out. These tests were accompanied by SEM observations and IR and mechanical tests on compression-molded films in order to select the best plasticizer content. The best formulation was then scaled up in a semi-industrial twin-screw extruder, feeding the solution by a peristaltic pump, to optimize the industrial-scale production of commercial MFC-based composites with a solvent-free method. From this study, it can be seen that the use of plasticisers as dispersing aids is a biobased and green solution that can be easily used in conventional extrusion techniques.

In an effort to reduce global dependence on fossil-based polymers and advance toward a more sustainable materials industry, research over recent decades has increasingly focused on the development of bio-based polymers and broadening their potential applications. Within this context, the present study investigates nanocomposites based on poly(butylene succinate-co-butylene adipate) (PBSA), reinforced with two types of nanofillers: silicon dioxide nanoparticles (SiO₂ NPs) and cellulose nanofibrils (CNFs). The main objective of this work is to examine how the morphology, geometry, and chemical nature of the nanofillers influence the thermal, mechanical, and barrier properties of PBSA, as well as its biodegradability. For each nanofiller, three formulations were prepared, containing 1, 2, and 5 wt% of filler, respectively. Scanning electron microscopy (SEM) analysis confirmed good dispersion and minimal aggregation in the SiO₂-based systems, whereas marked aggregation was observed in the CNF-based samples. Thermal analysis indicated that the intrinsic thermal properties of neat PBSA were largely preserved. Mechanical testing revealed improvements in both the elastic modulus and elongation at break for most nanocomposite samples. In particular, CNFs provided the most consistent reinforcing effect, with enhancements of approximately 40% in the elastic modulus (495.4 vs. 356.4 GPa in neat PBSA) and 52% in elongation at the break (185.1 vs. 122.0% in neat PBSA) with 5 wt% loading. Additionally, the incorporation of nanofillers did not alter the surface hydrophilicity, but it did improve the oxygen barrier performance and enhanced disintegration under composting conditions. Overall, these findings demonstrate the promising potential of PBSA-based nanocomposites for sustainable rigid packaging applications.