The effect of the addition of bismuth on the dynamic recrystallization (DRX) behavior of the matrix has been investigated by comparing coarse grain pure Mg with the addition of 3 wt.% Bi, using a uniaxial compression test in the temperature range of 473–623 K and the strain rate of 0.01–10 s⁻¹. The constitutive equation, processing map, microstructure, and texture evolution of the Mg-3Bi alloy were systematically investigated. The results showed that the Bi addition could refine the grain size and accelerate the DRX process. The DRX kinetics is discussed in detail, accompanied by extensive characterization employing EBSD analysis. The DRX of the Mg-3Bi alloy depended on the deformation temperature rather than the strain rate. The {10–12} tensile twin appeared at 573 K/0.01–0.1 s⁻¹, and discontinuous DRX (DDRX), continuous DRX (CDRX) as the main mechanism in the case of 573 K/0.01 s⁻¹, while the dominant mechanism was DDRX when deformation temperature and strain rate increased. Particle-stimulated nucleation (PSN) was also involved in the DRX of this new RE-free Mg alloy.

Graphene-reinforced aluminium composites have been widely studied due to their excellent mechanical properties. However, only a few studies have reported their dynamic compression properties. The purpose of this study is to investigate the quasi-static and dynamic compression properties of graphene-reinforced aluminium composites. The addition of graphene improved the compressive stress resistance and energy absorption capacity of the aluminium matrix. An aluminium-0.5 wt.% graphene composite exhibited good compressive properties due to the different interfacial wave impedance generated by the additional grain boundaries or Aluminium-Graphene interfaces.

In this study, we investigated the high strain rate response of Mg-6wt%Er alloys with 1wt%Zn addition by split Hopkinson pressure bar (SHPB) tests in a range of 900–2500 s⁻¹. Their related microstructures were also characterized by optical microscopy (OM), scanning electron microscopy (SEM), electron back-scattering diffraction (EBSD), and transmission electron microscopy (TEM). In particular, the twinning and stacking faults (SFs) in Mg-6Er and Mg-6Er-1Zn alloys are characterized, and the interactions between twin/SFs and dislocations are analyzed in detail. Compared with twins, the dispersed and dense SFs seem to more readily interact with dislocations, resulting in the enhancement of the strength of alloys. Especially at a high strain rate of 1450 s⁻¹, dislocations are prone to tangle around the twins and SFs, forming low-angle grain boundaries (LAGBs). The addition of Zn in Mg-6Er can make LAGBs more easily transform into high-angle grain boundaries (HAGBs) due to the existence of SFs.

In this study, the microstructure and related corrosion behavior of AM60 alloys with/without Ca and Y addition upon gravity casting (GC) and high-pressure die-casting (HPDC) are investigated by means of SEM/EDS characterization, immersion/salt spray test, hydrogen releasing, as well as electrochemistry examination. When utilizing GC, AM60 alloy with Ca and Y addition (named AZXW6000 alloy) has better corrosion resistance compared with AM60 alloy. Thanks to grain refinement and second phase networks introduced in HPDC, the anti-corrosion properties of the AM alloy seem much better than those of the GC counterpart. The corrosion mechanism of both GCed and HPDCed AM60-based alloys is also investigated in detail. The inspiration from present work can provide more thinking for developing high corrosion-resistant Mg alloys using different casting methods.

In this study, an Mg-Bi-RE alloy having a bimodal grain structure was successfully fabricated by a new processing route of combining extrusion and single-pass caliber rolling at room temperature (RT). This novel processing (E-CRed) demonstrates a necklace-like grain structure with ultrafine grains formed around the microscale deformed grains, remarkably different from the uniform