This study presents the investigation of the electromagnetic properties and resistance performance of electrically conductive fabrics coated with composition containing the conjugated polymer system poly(3,4-ethylenedioxythiophene)-polystyrene sulfonate (PEDOT:PSS). The developed fabrics were intended for electromagnetic radiation (EMR) shielding in microwave range and for absorbing microwaves in radar operating range, so as to act as radar absorbing materials (RAM). The measurements of reflection and transmission of the developed fabrics were performed in a frequency range of 2–18 GHz, which covers the defined frequencies relevant to the application. Four types of fabrics with different fiber composition (polyamide; polyamide/cotton; wool and para-aramid/viscose) were selected and coated with conductive paste using screen printing method. It was found that EMR shielding effectiveness (SE) as well as absorption properties depend not only the amount of conductive paste topped on the fabric, but also resides in the construction parameters of fabrics. Depending on such fabric structural parameters as density, mass per unit area, type of weave, a layer of shield (or coating) just sticks on the fabric surface or penetrates into fabric, changing the shield thickness and herewith turning SE results. Meanwhile, the fiber composition of fabrics influences mostly bonding between fibers and polymer coating. To improve the resistance performance of the developed samples, a conventional textile surface modification technique, atmospheric plasma treatment, was applied. Initially, before plasma treatment and after treatment the fabrics were evaluated regarding an aqueous liquid repellency test, measuring the contact angles for the water solvent. The influence of plasma treatment on resistance performance of coated fabrics was evaluated by subjecting the plasma treated samples and untreated samples to abrasion in the Martindale abrasion apparatus and to multiplex washing cycles. These investigations revealed that applied plasma treatment visibly improved abrasion resistance as a result of better adhesion of the coating. However, washing resistance increased not so considerably.

The continuous research and development regarding firefighters’ personal protective equipment (PPE) has led to significant improvements in recent decades. Despite the evolution of firefighters’ PPE, every year an undesirable number of firefighters are seriously burned during firefighting operations, with some of them eventually losing their lives. The protection given by firefighters’ PPE can be further increased with the incorporation of smart textiles in the personal protective equipment, namely, wearable electronics (i.e., integrated sensors to monitor diverse parameters: heart rate, oxygen saturation, carbon dioxide detector, and setting real-time communication with a command post) and advanced materials such as phase change materials (PCMs). The evolution of firefighters’ PPE has been followed by an evolution and update in the international and national standards that specify performance requirements for firefighters’ protective clothing for structural and wildland firefighting as well as technical rescue. This study will focus on the analysis of firefighters protective clothing evolution regarding the use and integration of advanced smart materials, namely, phase change materials, taking into consideration the evolution and requirements of international and European standards as well as national legislation for firefighters’ protective clothing.

Technical clothing with light-responsive features for outdoor sports practiced in environments with low visibility is extremely important for athletes’ safety. Lack of signaling by users and visibility for drivers is one of accidents causes, namely run overs, which can leave serious consequences. The products available on the market lack efficiency and their design is not appealing which makes the development of these new materials a compelling need. Therefore, fluorescent and phosphorescent functional finishings with ability to provide illuminant signalization without compromising the design and/or color of clothing as well as comfort and ergonomics, were developed and applied in the textile structure by knife over roll coating technology. The greatest challenge is to integrate the high visibility materials without compromising the design of the garment and accomplish the European Standard of Protective clothing: Enhanced visibility equipment for medium risk situations and test methods and requirements—EN 17353 (that supersedes EN1150:1999 and allows more freedom in the design of the apparel) published in 2020. Phosphorescent materials were evaluated by luminance decay according to DIN 67510, before and after fastness to wash tests. Results obtained regarding high visibility functional finishings and the integration of the materials developed in the final sports collection will be presented.

Considering the high level of heat and flame exposure firefighters encounter while performing their work activities, personal protective equipment (PPE) is of the utmost importance to enhance their safety. Phase change materials (PCMs) are known as advanced materials able to absorb high amounts of thermal energy, with the potential to increase the thermal performance of protective clothing. In this work, a PCM-vest was developed for the first time, and its thermal performance was evaluated. A three-stage approach was followed: (1) at a small scale in the laboratory, the effect of different encapsulated PCMs on a multilayer assembly performance was evaluated; (2) in the laboratory, the essential requirements of heat and flame tests were assessed; and (3) in a simulated urban fire, the thermal performance of three different PCM-vests (different textiles and designs) was studied. As the main conclusions, the PCMs significantly affected the heating rate of the multilayer assembly, particularly when a PCM with higher latent heat was used. In some cases, the heat transfer index (HTI) doubled by comparison with the sample without PCMs. As a drawback and as expected, the cooling time was increased. The PCM-vest sample ensured the requirements of the heat and flame tests. Through this study, the positive impact of using PCMs to enhance the heat protection of conventional PPE can be highlighted.

The widespread use of wireless technologies raises concerns about health effects and electromagnetic interference (EMI). This study aims to investigate the EMI-shielding properties of functional textiles using modified multi-walled carbon nanotubes (MWCNT) dispersed in different polymeric matrices as coating inks. Poly(3,4-ethylenedioxythiophene):polystyrene sulfonate (PEDOT:PSS) combined with MWCNT showed promise. For instance, a textile coated with a PEDOT:PSS-based ink containing 5 wt.% of N-doped MWCNT with a thickness of 140 µm achieved a shielding effectiveness (SE) of 31.0 dB (221 dB µm⁻¹) in the 5.85–18 GHz range. This fabric is classified as ‘excellent’ for general use and may be suitable for EMI-protective clothing. Some tests using silicone as a polymer matrix demonstrated improved SE through resonance phenomena.

Nowadays, despite the evolution of personal protective equipment (PPE), the number of firefighters injured and burned during fire extinguishing operations is still very high, leading in some cases to loss of life. Therefore, the research and development of new solutions to minimize firefighters’ heat load and skin burns, with consecutive improvements of commercial firefighters’ suits, is of extreme importance. The integration of phase change materials (PCMs) in a protective clothing system has been used to significantly reduce the incoming heat flux from the fire environment. This study consists in the development of a protective clothing system composed by a vest, specially designed to protect the torso (back, chest and abdomen) with a layer of PCM pouches, to be worn over a fire-resistant jacket – selection and design based on numerical models’ predictions. Therefore, several mockups were made, varying the number of PCM pouches and their distribution in the vest, allowing the creation of air ducts to increase the breathability of the vest. The most promising solutions are being evaluated in a real controlled environment, at a Portuguese National School of Firefighters (ENB) simulation site, using a fire manikin and thermocouples to monitor vest temperature during heat and flame exposure, and consequently to verify PCMs influence in heat protection. Results regarding the development of a PCM vest will be presented, focusing on the integration of PCM pouches and the thermal performance of the most promising solutions.