The significant rise in the use of clear aligners for orthodontic treatment is attributed to their aesthetic appeal, enhancing patient appearance and self-confidence. The aim of this study is to evaluate the aligners’ response to common staining agents (coffee, black tea, Coca-Cola, and Red Bull) in color and chemical stability. Polyurethane-based thermoformed and 3D-printed aligners from four brands were exposed to common beverages to assess color change using a VITA Easyshade compact colorimeter after 24 h, 48 h, 72 h, and 7 days, as well as chemical stability using ATR-FTIR spectroscopy. The brand, beverage, and manufacturing method significantly influence color stability. ATR-FTIR analysis revealed compositional differences, with variations in response to beverage exposure affecting the integrity of polymer bonds. Color change analysis showed coffee as the most potent staining agent, particularly affecting Tera Harz TC85 aligners, while ClearCorrect aligners exhibited the least susceptibility. 3D-printed aligners showed a greater color change compared to thermoformed ones. Aligners with a PETG outer layer are more resistant to stains and chemical alterations than those made of polyurethane. Additionally, 3D-printed polyurethane aligners stain more than thermoformed ones. Therefore, PETG-layered aligners are a more reliable choice for maintaining the aesthetic integrity of aligners.

Over the past few decades, adhesive dentistry has advanced significantly. In light of minimal-invasive dentistry, this novel technique advocates a more conservative cavity design that relies on the efficiency of present enamel-dentine adhesives. The study aimed to address the scientific deficit in understanding the long-term bonding performance of universal adhesives and to provide a new clinical solution with desirable bond strength to dentin. The dentin bond strength of three bonding agents, G2-Bond Universal (GC), Clearfil SE Bond (Kuraray), and Scotchbond Universal Plus (3M ESPE), was evaluated following various storage and etching modes. The UltraTester (Ultradent) bond strength testing machine was used to assess shear bond strength. The results showed that thermal cycling and the choice of adhesive system significantly affected the shear bond strength (p = 0.018 and p = 0.001, respectively). Among the three adhesives, Scotchbond Universal Plus had the lowest bond strength value (mean value = 24.78 MPa), while G2-Bond Universal was found to have desirable shear bond strength to dentin compared to the other adhesives, even after one year in the oral environment (mean value = 35.15 MPa). These findings imply that the HEMA-free universal adhesive G2-Bond Universal is the most effective universal adhesive for clinical practices, particularly when applied in the self-etch mode.

Objective: The objective of this study is to evaluate clinical and patient reported outcomes of different bleaching products. Materials and methods: Thirty participants were randomly divided into three bleaching groups (n = 10). Bleaching was performed with high concentrations of hydrogen peroxide (HP) – Boost (40%) and Dash (30%), and with prefabricated splints Bite&White (6% HP). Tooth colour was measured before, immediately after, and 1 and 6 months after the bleaching by using classical shade guide and spectrophotometer. Tooth hypersensitivity was self-rated by patients on the Wong-Baker’s face scale. Patient satisfaction was evaluated on a 7-point Likert-type scales that measured perceived performance and importance of different characteristics of bleaching treatment. Results: All products were effective in teeth colour change (ΔE > 3.3), which was significantly higher for Boost (p = .016) and Dash (p = .024) than Bite&White treatment. Perception of hypersensitivity was the highest in Boost group, followed by Dash and Bite&White treatment. Most of the patients were satisfied with final tooth colour, length and comfort during treatment, but were dissatisfied with the stability of bleached tooth colour. Conclusion: Materials with the higher concentrations of bleaching agent demonstrated greater bleaching effectiveness than at-home bleaching product, but also a greater hypersensitivity. Lengthening the treatment process, but achieving a more stable tooth colour may improve the perceived value of a bleaching service.

To compare short-term release of fluoride ions from ion-releasing dental restorative materials. Seven experimental groups were prepared using the following six different materials: alkasite (Cention Forte), resin-modified glass ionomer cement (Fuji II LC), bioactive composite (ACTIVA BioACTIVE-RESTORATIVE), fluoride-containing nano-hybrid composite (Luminos UN), coat-free glass hybrid (EQUIA Forte HT), coat-applied glass hybrid (EQUIA Forte HT), and glass ionomer cement (Fuji IX). A total of 40 samples for each group (n=40) were prepared in Teflon molds (8 mm x 2 mm) and placed in polyethylene vials with 5 ml of deionized water. Fluoride release was measured after 6, 24, 48 hours, and for 5 weeks using an ion-selective electrode. The results were expressed in mg/l and the data were statistically analyzed using ANOVA. Significant differences in fluoride release were observed within the first 6 hours (ANOVA p<0.001). EQUIA Forte HT had the highest release, while the other materials showed no significant differences. After 24 hours, EQUIA Forte HT (p<0.001) and Luminos UN (p<0.05) exhibited significantly higher releases, compared to other tested materials. EQUIA Forte HT maintained the highest release at 48 hours (p<0.001), followed by Cention Forte (p<0.05) and Luminos UN (p<0.05). All material pairs showed significant differences in fluoride release at 5 weeks (p<0.001). Coat-free EQUIA Forte HT had the overall highest fluoride release, while Cention Forte demonstrated the greatest increase over time. ACTIVA BioACTIVE-RESTORATIVE exhibited the lowest fluoride release in this study.