The potential-induced degradation (PID) mechanism in Cu(In,Ga)(Se,S)₂ (CIGS) thin-film solar cells, which are alternative energy sources with a high efficiency (>23%) and upscaling possibilities, remains unclear. Therefore, the cause of PID in CIGS solar cells was investigated in this study at the cell level. First, an appropriate PID experiment structure at the cell level was determined. Subsequently, PID and recovery tests were conducted to confirm the PID phenomenon. Light current–voltage (I–V), dark I–V, and external quantum efficiency (EQE) analyses were conducted to determine changes in the cell characteristics. In addition, capacitance–voltage (C–V) measurements were carried out to determine the doping concentration and width of the space charge region (SCR). Based on the results, the causes of PID and recovery of CIGS solar cells were explored, and it was found that PID occurs due to changes in the bulk doping concentration and built-in potential at the junction. Furthermore, by distinguishing the effects of temperature and voltage, it was found that PID phenomena occurred when potential difference was involved.

As we move towards the commercialization and upscaling of perovskite solar cells, it is essential to fabricate them in ambient environment rather than in the conventional glove box environment. The efficiency of ambient-processed perovskite solar cells lags behind those fabricated in controlled environments, primarily owing to external environmental factors such as humidity and temperature. In the case of device fabrication in ambient environments, relying solely on a single parameter, such as temperature or humidity, is insufficient for accurately characterizing environmental conditions. Therefore, the dew point is introduced as a parameter which accounts for both temperature and humidity. In this study, a machine learning model was developed to predict the efficiency of ambient-processed perovskite solar cells based on meteorological data, particularly the dew point. A total of 238 perovskite solar cells were fabricated, and their photovoltaic parameters and dew points were collected from March to December 2023. The collected data were used to train various tree-based machine learning models, with the random forest model achieving the highest accuracy. The efficiencies of the perovskite solar cells fabricated in January and February 2024 were predicted with a MAPE of 4.44%. An additional Shapley Additive exPlanations analysis confirmed the significance of the dew point in the performance of perovskite solar cells.

Photovoltaic (PV) installations have traditionally relied on a conventional south-facing orientation, which maximizes energy production at noon but has lower energy generation in the morning and afternoon. Vertical photovoltaic (VPV) systems have emerged as promising alternatives to address this inconsistency. Vertical photovoltaic systems can enhance energy generation by facing east in the morning and west in the afternoon. We compared the performance of n-tunnel oxide passivated contact (n-TOPCon) and p-passivated emitter and rear contact (p-PERC) cells in vertical photovoltaic systems to determine whether the optimal installation direction of bifacial vertical photovoltaics is east or west. Our findings indicated that n-TOPCon cells exhibited higher energy yields than p-PERC cells, with a difference of approximately 8%, attributed to the superior bifaciality and lower temperature coefficient of power of n-TOPCon. Additionally, the energy yield was higher for n-TOPCon modules when the front faced east, whereas the PERC modules performed better with a west-facing front. This contributes to the knowledge of the factors for energy production in vertical photovoltaic systems and the optimization of installation configurations.

In this work, nickel silicide was applied to tandem solar cells as an interlayer. By the process of thermal evaporation, a layer of NiO_x, hole transport layer (HTL) was deposited on n⁺ poly-Si layer directly. Nickel silicide was simultaneously formed by nickel diffusion from NiO_x to n⁺ poly-Si layer during the deposition and annealing process. The I–V characteristics of NiO_x/n⁺ poly-Si contact with nickel silicide showed ohmic contact and low contact resistivity. This structure is expected to be more advantageous for electrical connection between perovskite top cell and TOPCon bottom cell compared to the NiO_x/TCO/n⁺ poly-Si structure showing Schottky contact. Furthermore, nickel silicide and Ni-deficient NiO_x thin film formed by diffusion of nickel can improve the fill factor of the two sub cells. These results imply the potential of a NiO_x/nickel silicide/n⁺ poly-Si structure as a perovskite/silicon tandem solar cell interlayer.

This study investigated the integration of perovskite solar cells (PSCs) on stainless steel (SS) substrates for application in building-integrated photovoltaics (BIPV). Using advanced atomic force microscopy measurements, we confirmed that enhanced substrate roughness increased the reflectance along an interface. Consequently, a remarkable final efficiency of 11.9% was achieved. Notably, PSCs, known for their exceptional efficiency of 26.1%, can overcome the inherent efficiency limitations of SS-based thin-film solar cells. In this study, a PSC with an efficiency of 14% was fabricated on a flexible SS substrate. This study is a significant step towards advancing sustainable energy solutions for BIPV applications. The global shift towards renewable energy sources has catalyzed intensive research and development efforts, rendering the exploration of alternative materials and manufacturing processes a priority. The success of PSCs on SS substrates underscores their promise to achieve a balance between efficiency and versatility in BIPV solutions. Moreover, our findings reveal that controlling the substrate surface characteristics can significantly enhance the performance of PSCs, offering a pathway toward greater energy efficiency and sustainability in the construction industry.