Digital light processing (DLP) is an accurate additive manufacturing (AM) technology suitable for producing micro-parts by photopolymerization. As most AM technologies, anisotropy of parts made by DLP is a key issue to deal with, taking into account that several operational factors modify this characteristic. Design for this technology and photopolymers becomes a challenge because the manufacturing process and post-processing strongly influence the mechanical properties of the part. This paper shows experimental work to demonstrate the particular behavior of parts made using DLP. Being different to any other AM technology, rules for design need to be adapted. Influence of build direction and post-curing process on final mechanical properties and anisotropy are reported and justified based on experimental data and theoretical simulation of bi-material parts formed by fully-cured resin and partially-cured resin. Three photopolymers were tested under different working conditions, concluding that post-curing can, in some cases, correct the anisotropy, mainly depending on the nature of photopolymer.

Natural fibers have been used as an alternative to synthetic ones for their greener character; banana fibers have the advantage of coming from an agricultural residue. Fibers have been extracted by mechanical means from banana tree pseudostems, as a strategy to valorize banana crops residues. To increase the mechanical properties of the composite, technical textiles can be used as reinforcement, instead of short fibers. To do so, fibers must be spun and woven. The aim of this paper is to show the viability of using banana fibers to obtain a yarn suitable to be woven, after an enzymatic treatment, which is more environmentally friendly. Extracted long fibers are cut to 50 mm length and then immersed into an enzymatic bath for their refining. Conditions of enzymatic treatment have been optimized to produce a textile grade of banana fibers, which have then been characterized. The optimum treating conditions were found with the use of Biopectinase K (100% related to fiber weight) at 45 °C, pH 4.5 for 6 h, with bath renewal after three hours. The first spinning trials show that these fibers are suitable to be used for the production of yarns. The next step is the weaving process to obtain a technical fabric for composites production.

Several natural materials and vegetable waste have relevant mechanical properties, mainly in its fiber format. Particularly, banana fiber (BF) provides a close behavior to the widely spread glass fibers, which places it in an advantageous position for use as a reinforcing material in plastic composites. This work characterizes the behavior of acrylonitrile butadiene styrene (ABS), high impact polystyrene (HIPS), and high density polyethylene (HDPE) reinforced with short fibers of bananas from the Canary Islands for its application in molding processes. Several thermal analyses (Thermal Gravimetric Analysis (TGA), Differential Scanning Calorimetry (DSC), and Melt Flow Index (MFI)) and mechanical tests (tensile, flexural, impact, and Dynamic Mechanical Analysis (DMA)) were carried out in composites with different percentages of banana fiber. The thermal results show that the use of banana fiber is viable as a reinforcement in composites for injection molding processes and the mechanical tests indicate an increase in stiffness and an improvement in maximum flexural stress by increasing the fiber content in composites, so the banana fiber turns out to be a natural alternative for the reinforcement of injected plastic components.

The purpose of this paper is to extend existing knowledge of 4D printing, in line with Khoo et al. (2015) who defined the production of 4D printing using a single material, and 4D printing of multiple materials. It is proposed that 4D printing can be achieved through the use of functionally graded materials (FGMs) that involve gradational mixing of materials and are produced using an additive manufacturing (AM) technique to achieve a single component. The latest state-of-the-art literature was extensively reviewed, covering aspects of materials, processes, computer-aided design (CAD), applications and made recommendations for future work. This paper clarifies that functionally graded additive manufacturing (FGAM) is defined as a single AM process that includes the gradational mixing of materials to fabricate freeform geometries with variable properties within one component. The paper also covers aspects of materials, processes, CAD, applications and makes recommendations for future work. This paper examines the relationship between FGAM and 4D printing and defines FGAM as a single AM process involving gradational mixing of materials to fabricate freeform geometries with variable properties within one component. FGAM requires better computational tools for modelling, simulation and fabrication because current CAD systems are incapable of supporting the FGAM workflow. It is also identified that other factors, such as strength, type of materials, etc., must be taken into account when selecting an appropriate process for FGAM. More research needs to be conducted on improving the performance of FGAM processes through extensive characterisation of FGMs to generate a comprehensive database and to develop a predictive model for proper process control. It is expected that future work will focus on both material characterisation as well as seamless FGAM control processes. This paper examines the relationship between FGAM and 4D printing and defines FGAM as a single AM process that includes gradational mixing of materials to fabricate freeform geometries with variable properties within one component.

The influence of manufacturing parameters of filament extrusion and extrusion-based Additive Manufacturing (AM), as well as different post processing techniques, on the electrical conductivity of 3D printed parts of graphene nanoplatelets (GNP)-reinforced acrylonitrile butadiene styrene (ABS) has been analyzed. The key role of the manufacturing parameters to obtain electrically conductive filaments and 3D printed parts has been demonstrated. Results have shown that an increase in extrusion speed, as well as lower land lengths, induces higher extrudate swelling, with the consequent reduction of the electrical conductivity. Additionally, filaments with lower diameter values, which result in a higher surface-to-cross-section ratio, have considerably lower electrical conductivities. These factors tune the values of the volume and surface electrical conductivity between 10⁻⁴–10⁰ S/m and 10⁻⁸–10⁻³ S/sq, respectively. The volume and surface electrical conductivity considerably diminished after 3D printing. They increased when using higher printing layer thickness and width and were ranging between 10⁻⁷–10⁻⁴ S/m and 10⁻⁸–10⁻⁵ S/sq, respectively. This is attributed to the higher cross section area of the individual printed lines. The effect of different post processing (acetone vapor polishing, plasma and neosanding, which is a novel finishing process) on 3D printed parts in morphology and surface electrical conductivity was also analyzed.