High-performance extruded aluminum alloys with complex textures suffer significant dimension variation under environmental temperature fluctuations, dramatically decreasing the precision of navigation systems. This research mainly focuses on the effect of the texture of extruded pure aluminum on its dimensional stability after various annealing processes. The result reveals that a significant increment in the area fraction of recrystallized grains with orientation and a decrement in the area fraction of grains with orientation were found with increasing annealing temperature. Moreover, with the annealing temperature increasing from 150 °C to 400 °C, the residual plastic strain after twelve thermal cycles with a temperature range of 120 °C was changed from −1.6 × 10⁻⁵ to −4.5 × 10⁻⁵. The large amount of equiaxed grains with orientation was formed in the microstructure of the extruded pure aluminum and the average grain size was decreased during thermal cycling. The area fraction of grain with crystallographic orientation of the sample annealed at 400 °C after thermal cycling was 30.9% higher than annealed at 350 °C (23.7%) or at 150 °C (18.7%). It is attributed to the increase in the proportion of recrystallization grains with direction as the annealing temperature increases, provided more nucleation sites for the formation of fine equiaxed grains with orientation. The main orientation of the texture was rotated from parallel to to parallel to after thermal cycling. The change in the orientation of grains contributed to a change in interplanar spacing, which explains the change in the dimension along the extrusion direction during thermal cycling.

Rolling enables the directional alignment of the reinforcements in graphene/Cu composites while achieving uniform graphene dispersion and matrix grain refinement. This is expected to achieve a breakthrough in composite performance. In this paper, the process parameters of rolling are investigated, and the defects, thickness variations of graphene and property changes of the composite under different parameters are analyzed. High-temperature rolling is beneficial to avoid the damage of graphene during rolling, and the prepared composites have higher electrical conductivity. The properties of graphene were investigated. Low-temperature rolling is more favorable to the thinning and dispersion of graphene; meanwhile, the relative density of the composites is higher in the low-temperature rolling process. With the increase of rolling deformation, the graphene defects slightly increased and the number of layers decreased. In this paper, the defect states of graphene and the electrical conductivity with different rolling parameters is comprehensively investigated to provide a reference for the rolling process of graphene/copper composites with different demands.

In this paper, the effects of carbon nanotube defects and a copper surface oxide layer on a carbon nanotube–copper interface were studied via first-principles. A defect-free CNT-Cu interface, Stone–Wales defect CNT-Cu interface, single-hole and double-hole defect CNT-Cu interface, and Cu₂O-Cu interface were simulated and calculated. By simulating the differential charge density, atomic population, bond population and density of states of the interface model, the effects of various defects on the interface bonding and electrical conductivity of the composites during the preparation of the CNT-reinforced copper matrix composites were analyzed, which provided theoretical guidance for the preparation of CNT/Cu composites. After that, copper matrix composites with different CNT defect contents were prepared via different rolling deformation processes. Their hardness and electrical conductivity were tested, and the results were consistent with the results obtained via the first-principles calculations.