The utilization of lignocellulosic biomass in various applications has a promising potential as advanced technology progresses due to its renowned advantages as cheap and abundant feedstock. The main drawback in the utilization of this type of biomass is the essential requirement for the pretreatment process. The most common pretreatment process applied is chemical pretreatment. However, it is a non-eco-friendly process. Therefore, this review aims to bring into light several greener pretreatment processes as an alternative approach for the current chemical pretreatment. The main processes for each physical and biological pretreatment process are reviewed and highlighted. Additionally, recent advances in the effect of different non-chemical pretreatment approaches for the natural fibres are also critically discussed with a focus on bioproducts conversion.

The current production method of nanobiochar (NBC), an emerging, environmentally friendly nanocarbon material, is tedious and lengthy. Therefore, in this study we aimed to improve the productivity of NBC via high-energy ball milling by manipulating the grinding media and processing time. The particle size distribution of the resulting NBC measured using dynamic light scattering showed that grinding media with steel balls of different sizes were more effective at producing NBC than small uniform steel balls, which failed to produce NBC even after 90 min of milling. Average NBC particles of around 95 nm were achieved after only 30 min of ball milling, and the size was further reduced to about 30 nm when the milling was prolonged to 150 min. Further prolonging the milling duration led to agglomeration, which increased the size of the biochar nanoparticles. The thermogravimetric analysis (TGA) data showed that the duration of milling and particle size did not cause noticeable differences in the thermal stability of the NBC. Based on the FTIR analysis, the chemical structure of the NBC was not affected by the ball milling. The results showed that 60 min of high-energy ball milling is sufficient to produce NBC particles of 75 nm, with a large surface area and high thermal stability. This could prove beneficial in a myriad of applications, ranging from agriculture to composite fabrication.

Biomimetics is the field of obtaining ideas from nature that can be applied in science, engineering, and medicine. The usefulness of cellulose nanocrystals (CNC) and their excellent characteristics in biomimetic applications are exciting and promising areas of present and future research. CNCs are bio-based nanostructured material that can be isolated from several natural biomasses. The CNCs are one-dimensional with a high aspect ratio. They possess high crystalline order and high chirality when they are allowed to assemble in concentrated dispersions. Recent studies have demonstrated that CNCs possess remarkable optical and chemical properties that can be used to fabricate liquid crystals. Research is present in the early stage to develop CNC-based solvent-free liquid crystals that behave like both crystalline solids and liquids and exhibit the phenomenon of birefringence in anisotropic media. All these characteristics are beneficial for several biomimetic applications. Moreover, the films of CNC show the property of iridescent colors, making it suitable for photonic applications in various devices, such as electro-optical devices and flat panel displays.