Municipal solid waste (MSW) contains plastic waste that can be used as a sustainable green substitute to reduce oil footprints, CO₂ emissions, and environmental pollution. This study aims to recycle plastic waste by manufacturing wood-plastic composites and to improve its mechanical properties by using additives, coupling agents, and lubricants. These composites are prepared by mixing 40–70% of wood flour with 20–25% of a polymer matrix. Wood was degraded at 220 °C, and then the composites were processed at 50 °C. The manufacturing process carried out in the study involved wood waste meshing, drying, shredding, drying, trimming, filling, blending, compounding, and extrusion moulding. The compounding of composites was accomplished in twin-screw extruders. Once the mixture was uniformly mixed, its final shape was given by a two-step extrusion moulding. Previously, researchers aimed at enhancing the mechanical properties of the composites, but our research focus was to improve their durability for different industrial applications. The results suggest that the impact strength is 17 MPa with 50% of wood powder ratio while the maximum value for the tensile strength is 32.5 MPa. About 50% of an increase in wood powder resulted in 8.1% bending strength increase from 26.1 to 32.8 MPa. Reducing the plastic matrix and the wood-particles water swelling ratio resulted in better mechanical properties. The wood species also affected the mechanical properties with their excellent dimensional stability and less variability. A high proportion of wood fibre tends to increase its steady-state torque and viscosity. The mechanical properties against different wood-flour proportions indicate that composite materials exhibit superior water swelling behaviour and extrusion quality.

This study investigates the in vitro biocompatibility, corrosion resistance, and adhesion strength of a gas abrasive-treated Ti6Al4V alloy, alongside microplasma-sprayed titanium and tantalum coatings. Employing a novel approach in selecting microplasma spray parameters, this study successfully engineers coatings with tailored porosity, roughness, and over 20% porosity with pore sizes up to 200 μm, aiming to enhance bone in-growth and implant integration. This study introduces an innovative methodology for quantifying surface roughness using laser electron microscopy and scanning electron microscopy, facilitating detailed morphological analysis of both the substrate and coatings. Extensive evaluations, including tests for in vitro biocompatibility, corrosion resistance, and adhesive strength, revealed that all three materials are biocompatible, with tantalum coatings exhibiting superior cell proliferation and osteogenic differentiation, as well as the highest corrosion resistance. Titanium coatings followed closely, demonstrating favorable osteogenic properties and enhanced roughness, which is crucial for cell behavior and attachment. These coatings also displayed superior tensile adhesive strengths (27.6 ± 0.9 MPa for Ti and 28.0 ± 4.9 MPa for Ta), surpassing the ISO 13179-1 standard and indicating a robust bond with the substrate. Our findings offer significant advancements in biomaterials for medical implants, introducing microplasma spraying as a versatile tool for customizing implant coatings, particularly emphasizing the superior performance of tantalum coatings in terms of biocompatibility, osteogenic potential, and corrosion resistance. This suggests that tantalum coatings are a promising alternative for enhancing the performance of metal implants, especially in applications demanding high biocompatibility and corrosion resistance.

This study aims to achieve in situ-formed pure Ti and Ti6Al4V coatings on 316L stainless steel through hot pressing and examine their wear and corrosion properties thoroughly in two simulated body fluids: physiological serum (0.9% NaCl) and Hanks’ solution. The sintering and diffusion bonding process was conducted at 1050 °C under a uniaxial pressure of 40 MPa for 30 min in a vacuum environment of 10⁻⁴ mbar. Following sintering, in situ-formed pure Ti and Ti6Al4V coatings, approximately 1000 µm thick, were produced on 316L substrates approximately 3000 µm in thickness. The mean hardness of 316L substrates, pure Ti, and Ti6Al4V coatings are around 165 HV, 170 HV, and 420 HV, respectively. The interface of the stainless steel substrate and the pure Ti and Ti6Al4V coatings exhibited no microstructural defects, while the interface exhibited significantly higher hardness values (ranging from 600 to 700 HV). The coatings improved corrosion resistance in both electrolytes compared to the 316L substrate. Wet wear tests revealed reduced friction coefficients in 0.9% NaCl relative to Hanks’ solution, highlighting the chemical interactions between the material surface and the electrolyte type and the significance of tribocorrosion in biocoatings.

The high volume production of substrates able to support high density interconnection is becoming increasingly difficult as the pitch of devices continues to decrease. An important issue is the alignment of microvias and pads which is made particularly challenging by the dimensional instability of traditional organic substrates. In this work, glass has been investigated as an alternative substrate material. Glass offers potential advantages including: electrical insulation, dimensional stability, thermal expansion similar to Si and optical transparency. This paper examines manufacturing processes for the preparation of substrates built up from 50 to 100 ¿m thick glass sheets. Excimer laser machining was used to form microvias and tracks in the glass which were metallised using electroless plating methods. Using a photoresist layer during the laser machining process helped to reduce debris on the glass surface and could be used to direct the subsequent deposition of electroless copper or nickel such that circuit patterns could be created. Lamination of the thin glass sheets was investigated using direct glass to glass bonding and through the use of an intermediate layer. A method for the combination of these techniques to create multilayer substrates is proposed.