This study investigates the in vitro biocompatibility, corrosion resistance, and adhesion strength of a gas abrasive-treated Ti6Al4V alloy, alongside microplasma-sprayed titanium and tantalum coatings. Employing a novel approach in selecting microplasma spray parameters, this study successfully engineers coatings with tailored porosity, roughness, and over 20% porosity with pore sizes up to 200 μm, aiming to enhance bone in-growth and implant integration. This study introduces an innovative methodology for quantifying surface roughness using laser electron microscopy and scanning electron microscopy, facilitating detailed morphological analysis of both the substrate and coatings. Extensive evaluations, including tests for in vitro biocompatibility, corrosion resistance, and adhesive strength, revealed that all three materials are biocompatible, with tantalum coatings exhibiting superior cell proliferation and osteogenic differentiation, as well as the highest corrosion resistance. Titanium coatings followed closely, demonstrating favorable osteogenic properties and enhanced roughness, which is crucial for cell behavior and attachment. These coatings also displayed superior tensile adhesive strengths (27.6 ± 0.9 MPa for Ti and 28.0 ± 4.9 MPa for Ta), surpassing the ISO 13179-1 standard and indicating a robust bond with the substrate. Our findings offer significant advancements in biomaterials for medical implants, introducing microplasma spraying as a versatile tool for customizing implant coatings, particularly emphasizing the superior performance of tantalum coatings in terms of biocompatibility, osteogenic potential, and corrosion resistance. This suggests that tantalum coatings are a promising alternative for enhancing the performance of metal implants, especially in applications demanding high biocompatibility and corrosion resistance.

This study aims to achieve in situ-formed pure Ti and Ti6Al4V coatings on 316L stainless steel through hot pressing and examine their wear and corrosion properties thoroughly in two simulated body fluids: physiological serum (0.9% NaCl) and Hanks’ solution. The sintering and diffusion bonding process was conducted at 1050 °C under a uniaxial pressure of 40 MPa for 30 min in a vacuum environment of 10⁻⁴ mbar. Following sintering, in situ-formed pure Ti and Ti6Al4V coatings, approximately 1000 µm thick, were produced on 316L substrates approximately 3000 µm in thickness. The mean hardness of 316L substrates, pure Ti, and Ti6Al4V coatings are around 165 HV, 170 HV, and 420 HV, respectively. The interface of the stainless steel substrate and the pure Ti and Ti6Al4V coatings exhibited no microstructural defects, while the interface exhibited significantly higher hardness values (ranging from 600 to 700 HV). The coatings improved corrosion resistance in both electrolytes compared to the 316L substrate. Wet wear tests revealed reduced friction coefficients in 0.9% NaCl relative to Hanks’ solution, highlighting the chemical interactions between the material surface and the electrolyte type and the significance of tribocorrosion in biocoatings.