Recently, new pedicle screw designs have been developed. However, these designs’ performances are still unclear, especially when backed out after insertion. The objective of this study was to investigate the performances of different screw designs when backed out from full insertion. Seven conventional designs of the pedicle screw and one novel design were inserted into polyurethane foam (0.32 g/cm³). All screws were first fully inserted (43 mm) and were backed out 360°. Axial pullout tests were performed and the reaction force was measured. The results showed that the conical screw of type 1 with a small inner diameter provided the highest pullout strength in both full insertion and backed-out insertion (2401.85 and 2169.82 N, respectively). However, this screw’s pullout strength significantly decreased (9.7%) when backed out from full insertion. There was no significant difference between the conical screw of type 1 with a small inner diameter and double duo core screw ( p > 0.01) in backed-out insertion. The cylindrical screw with a small diameter, dual inner core screw and double dual core screw also provided good results in both full insertion (2115.44, 2182.99 and 2226.93 N, respectively) and backed-out conditions (2065.80, 2014.28 and 1941.29 N, respectively). The increased pullout strength of the conical design could be due to the effect of bone compaction. However, the screw exhibited less consistent pullout strength when backed out when compared with the other designs. The conical screw should be inserted to the precise position without turning back, especially in osteoporosis patients. The dual inner core screw and double dual core screw could provide greater stability in both conditions. Care should be taken when using both the cylindrical screw with a small thread depth and the dual outer core screw.

Pyroelectric harvesters convert time-dependent temperature variations into electric current. The appropriate geometry of the pyroelectric cells, coupled with the optimal period of temperature fluctuations, is key to driving the optimal load resistance, which enhances the performance of pyroelectric harvesters. The induced charge increases when the thickness of the pyroelectric cells decreases. Moreover, the induced charge is extremely reduced for the thinner pyroelectric cell when not used for the optimal period. The maximum harvested power is achieved when a 100 μm-thick PZT (Lead zirconate titanate) cell is used to drive the optimal load resistance of about 40 MΩ. Moreover, the harvested power is greatly reduced when the working resistance diverges even slightly from the optimal load resistance. The stored voltage generated from the 75 μm-thick PZT cell is less than that from the 400 μm-thick PZT cell for a period longer than 64 s. Although the thinner PZT cell is advantageous in that it enhances the efficiency of the pyroelectric harvester, the much thinner 75 μm-thick PZT cell and the divergence from the optimal period further diminish the performance of the pyroelectric cell. Therefore, the designers of pyroelectric harvesters need to consider the coupling effect between the geometry of the pyroelectric cells and the optimal period of temperature fluctuations to drive the optimal load resistance.

Pedicle screws are used for treating several types of spinal injuries. Although several commercial versions are presently available, they are mostly either fully cylindrical or fully conical. In this study, the bending strengths of seven types of commercial pedicle screws and a newly designed double dual core screw were evaluated by finite element analyses and biomechanical tests. All the screws had an outer diameter of 7 mm, and the biomechanical test consisted of a cantilever bending test in which a vertical point load was applied using a level arm of 45 mm. The boundary and loading conditions of the biomechanical tests were applied to the model used for the finite element analyses. The results showed that only the conical screws with fixed outer diameter and the new double dual core screw could withstand 1,000,000 cycles of a 50-500 N cyclic load. The new screw, however, exhibited lower stiffness than the conical screw, indicating that it could afford patients more flexible movements. Moreover, the new screw produced a level of stability comparable to that of the conical screw, and it was also significantly stronger than the other screws. The finite element analysis further revealed that the point of maximum tensile stress in the screw model was comparable to the point at which fracture occurred during the fatigue test.

A thermoelastic solution to a coated elliptic hole embedded in an infinite matrix subjected to a remote uniform heat flow is provided in this article. Based on the technique of conformal mapping and the method of analytical continuation in conjunction with the alternating technique, the general expressions of the temperature and stresses in the coated layer and the matrix are derived explicitly in a series form. Some numerical results are provided to investigate the effects of the material combinations and geometric configurations on the interfacial stresses. It is found that a coated layer has a strong effect on thermal stresses of the problem with an elliptic hole embedded in an infinite plate.