New experimental results have been obtained on the behavior of arsenic and other associated metals (Re and others) under conditions of oxidative and reductive sintering. It has been established that the extraction of arsenic strongly depends on the process temperature during oxidative sintering. The extraction of arsenic into dust media at 873 K is 50% and rhenium is 88–90%. The effect of excess air on the extraction of arsenic and rhenium into dust was studied: the higher the excess air coefficient, the more complete the extraction of arsenic and rhenium into the dust. The obtained data indicate that achieving a high level of arsenic extraction from the initial product is not possible during oxidative sintering. The best arsenic removal results were reached under the conditions of reductive sintering of initial material by natural gas. The extraction of arsenic into dust at 823 K was 88%, and at 1373 K arsenic is almost completely converted into dust. Obtained new experimental results have a fundamental importance for the selection and organization of a comprehensive technology for the processing complex in composition refractory gold-copper-arsenic-bearing products.

Dross from hot-dip galvanizing is an important source of pure zinc ingots and zinc oxide for use as mineral additives in animal and poultry feed. Thermodynamic calculations have shown the possibility of solving the issue of dross processing by roasting using CaCl₂ and NH₄Cl. The influence of the consumption of chlorinating reagents, the roasting temperature on the degree of sublimation of Pb, Fe, Ni, Cu and Cd has been investigated. It has been shown that the best results are achieved when roasting the dross with the simultaneous use of CaCl₂ and NH₄Cl in amounts of 6 and 15% by weight of the feed material. The optimal roasting parameters were established: T = 1000 °C, duration—60 min, air flow—0.1 L/min. Recovered pure zinc oxide composition (%) was: 0.05 Pb, 0.15 Fe, 0.06 Ni, 0.003 Cu and 0.001 Cd. The degree of sublimation of copper, nickel and iron chlorides was ~75%, with lead and cadmium at 90–98% of their initial amount in the dross.

Attention focuses on the highly efficient heat and mass transfer in the counterflow of batch and hot reducing gases, which determines the duration of the blast-furnace process and increases the unit...