Friction drilling is a widely used process to produce bushings in sheet materials, which are processed further by thread forming to create a connection port. Previous studies focused on the process parameters and did not pay detailed attention to the material flow of the bushing. In order to describe the material behaviour during a friction drilling process realistically, a detailed material characterisation was carried out. Temperature, strain rate, and rolling direction dependent tensile tests were performed. The results were used to parametrise the Johnson–Cook hardening and failure model. With the material data, numerical models of the friction drilling were created using the finite element method in 3D as well as 2D, and the finite volume method in 3D. Furthermore, friction drilling tests were carried out and analysed. The experimental results were compared with the numerical findings to evaluate which modelling method could describe the friction drilling process best. Highest imaging quality to reality was shown by the finite volume method in comparison to the experiments regarding the material flow and the geometry of the bushing.

The process of press hardening is gaining importance in view of the increasing demand for weight reduction combined with higher crash safety in cars. An alternative to the established manganese-boron steel 22MnB5 is hot-formed martensitic chromium steels such as AISI 420C. Strengths of 1850 MPa and elongations of 12% are possible, exceeding those of 22MnB5. In industrial manufacturing, FE-simulation is commonly used in order to design car body parts cost-efficiently. Therefore, the characterization and the modeling of AISI 420C regarding flow stress, phase transformations as well as failure behavior are presented in this paper. Temperature-depended flow curves are determined, showing the low flow stress and hardening behavior at temperatures around 1000 °C. Cooling experiments are carried out, and a continuous cooling diagram is generated. Observed phases are martensite and retained austenite for industrial relevant cooling rates above 10 K/s. In addition, tests to investigate temperature-dependent forming limit curves are performed. As expected, the highest forming limit is reached at 1050 °C and decreases with falling temperature. Finally, a simulation model of a press-hardening process chain is set up based on the material behavior characterized earlier and compared to experimental values. The forming force, phase transformation and forming limit could be calculated with good agreement to the experiment.

As a cost-effective hole production technique, friction drilling is widely used in industrial and automotive manufacturing. Compared with the traditional bolted connection, it enables the fastening of thin metal sheets and thin-walled tubular profiles. Friction drilling results in higher thread length and joint strength, thus better fulfilling the demand for lightweight structures. However, in the numerical simulation of friction drilling, the traditional finite element method encounters difficulties caused by the extreme deformation and complex failure of the material. A large number of elements are usually deleted due to the failure criterion, which significantly reduces the solution accuracy. The development of meshless methods over the past 20 years has alleviated this problem. Especially the Smoothed Particle Galerkin (SPG) method proposed in recent years and incorporating a bond-based failure mechanism has been shown to be advantageous in material separation simulations. It does not require element removal and can continuously evolve each particle's information such as strain and stress after the material failure. Therefore, the SPG method was used in this research for the simulation of frictional drilling of HX220 sheet metal. First the particle distance and the friction coefficient were varied to investigate the applicability of the SPG method to the friction drilling process. Predicted and experimental results were compared and found to be in high agreement. Furthermore, the influence of input parameters, such as sheet thickness, feed rate and rotational speed, on axial force as well as torque of the tool and the surface temperature of the workpiece during friction drilling was investigated numerically.

The increasing global demand for innovative and environmentally friendly lubricants can be met through the use of solid lubricants. By switching from conventional lubricants such as various oils or grease to solid lubricants, new scopes of application can also be opened up. The main requirements for solid lubricants are a reduction in the coefficient of friction (CoF) and an increase in wear resistance. Due to the favourable material properties, molybdenum (Mo) coatings fulfil the tribological requirements and are therefore promising solid lubricants which can be applied via physical vapour deposition (PVD). In this work, the impact of substrate temperature on the hot hardness of deposited Mo coatings was determined. The specimen with the highest hot hardness was then tribologically examined both at the micro and nano level. Through an analysis of the wear tracks by means of nanoindentation and scanning electron microscopy (SEM), it was possible to detect the influence of the tribological load separately from that of the thermal loads. The results showed that the tribological load influenced the Mo coating by significantly increasing its hardness. This was achieved due to the work hardening of the Mo layer leading to an increase in the wear resistance of the coating.