The deep-drawability of a sheet metal blank is strongly influenced by the tribological conditions prevailing in a deep-drawing process. Therefore, new methods to influence the tribology represent an important research topic. In this work, the application of a process-integrated lubrication in a deep-drawing process is investigated. Most promising geometries of the lubrication channels and outlet openings are first identified by means of numerical simulation at the example of a demonstrator process. Cylindrical test specimens with the specified channel geometries are additively manufactured and installed in a strip drawing test stand. Additive manufacturing enables the possibility of manufacturing complex channel geometries which cannot be manufactured by conventional methods. A hydraulic metering device for conveying lubricant is connected to the cylindrical test specimens. Thus, hydraulically lubricated strip drawing tests are performed. The tests are evaluated according to the force curves and the fluid mechanical buildup of pressure cushion. The performance of process-integrated lubrication is thus analyzed and evaluated. By means of a coupled forming and SPH simulation, the lubrication channels could be optimally designed. From the practical tests, it could be achieved that the drawing force decreases up to 27% with pressure cushion build up. In this research, a hydraulic lubrication in the area of highest contact normal stresses is the most optimal process parameter regarding friction reduction.

Friction drilling is a widely used process to produce bushings in sheet materials, which are processed further by thread forming to create a connection port. Previous studies focused on the process parameters and did not pay detailed attention to the material flow of the bushing. In order to describe the material behaviour during a friction drilling process realistically, a detailed material characterisation was carried out. Temperature, strain rate, and rolling direction dependent tensile tests were performed. The results were used to parametrise the Johnson–Cook hardening and failure model. With the material data, numerical models of the friction drilling were created using the finite element method in 3D as well as 2D, and the finite volume method in 3D. Furthermore, friction drilling tests were carried out and analysed. The experimental results were compared with the numerical findings to evaluate which modelling method could describe the friction drilling process best. Highest imaging quality to reality was shown by the finite volume method in comparison to the experiments regarding the material flow and the geometry of the bushing.

Overmoulding of thermoplastic composites combines the steps of thermoforming and injection moulding in an integrated manufacturing process. The combination of continuous fibre-reinforced thermoplastics with overmoulded polymer enables the manufacturing of highly functionally integrated structures with excellent mechanical properties. When performed as a one-shot process, an economically efficient manufacturing of geometrical complex lightweight parts within short cycle times is possible. However, a major challenge in the part and process design of overmoulded thermoplastic composites (OTC) is the assurance of sufficient bond strength between the composite and the overmoulded polymers. Within the framework of a simulation-based approach, this study aims to develop a methodology for predicting the bond strength in OTC using simulation data and a numerical model formulation of the bonding mechanisms. Therefore, a modelling approach for the determination of the bond strength depending on different process parameters is presented. In order to validate the bond strength model, specimens are manufactured with different process settings and mechanical tests are carried out. Overall, the results of the numerical computation are in good agreement with the experimentally determined bond strength. The proposed modelling approach enables the prediction of the local bond strength in OTC, considering the interface conditions and the processing history.

As a result of global economic and environmental change, the demand for innovative, environmentally-friendly technologies is increasing. Employing solid lubricants in rolling contacts can reduce the use of environmentally harmful greases and oils. The aim of the current research was the development of a solid lubricant system with regenerative properties. The layer system consisted of a molybdenum (Mo) reservoir and a top layer of molybdenum trioxide (MoO₃). After surface wear, Mo is supposed to react with atmospheric oxygen and form a new oxide. The determination of the wear volume of thin layers cannot be measured microscopically, which is why the wear behavior is initially determined on the nano level. In this work, single Mo and MoO₃ coatings prepared by physical vapor deposition (PVD) are characterized by nano testing. The main objective was to determine the wear volume of the single coatings using a newly developed method considering the initial topology. For this purpose, nano-wear tests with different wear paths and normal forces were carried out and measured by in situ scanning probe microscopy (SPM). Based on the characteristic values determined, the coefficient of wear was determined for wear modeling according to Sarkar. The validation of the wear model developed was carried out by further wear tests on the respective mono layers.

Increasing product requirements have made numerical simulation into a vital tool for the time- and cost-efficient process design. In order to accurately model hot forging processes with finite, element-based numerical methods, reliable models are required, which take the material behaviour, surface phenomena of die and workpiece, and machine kinematics into account. In hot forging processes, the surface properties are strongly affected by the growth of oxide scale, which influences the material flow, friction, and product quality of the finished component. The influence of different carbon contents on material behaviour is investigated by considering three different steel grades (C15, C45, and C60). For a general description of the material behaviour, an empirical approach is used to implement mathematical functions for expressing the relationship between flow stress and dominant influence variables like alloying elements, initial microstructure, and reheating mode. The deformation behaviour of oxide scale is separately modelled for each component with parameterized flow curves. The main focus of this work lies in the consideration of different materials as well as the calculation and assignment of their material properties in dependence on current process parameters by application of subroutines. The validated model is used to carry out the influence of various oxide scale parameters, like the scale thickness and the composition, on the hot forging process. Therefore, selected parameters have been varied within a numerical sensitivity analysis. The results show a strong influence of oxide scale on the friction behaviour as well as on the material flow during hot forging.

Additive manufacturing with multi-material design offers great possibilities for lightweight and function-integrated components. A process chain was developed in which hybrid steel–steel-components with high fatigue strength were produced. For this, a material combination of stainless powder material Rockit^® (0.52 wt.% C, 0.9% Si, 14% Cr, 0.4% Mo, 1.8% Ni, 1.2% V, bal. Fe) cladded onto ASTM A572 mild steel by plasma arc powder deposition welding was investigated. Extensive material characterization has shown that defect-free claddings can be produced by carefully adjusting the welding process. With a tailored heat treatment strategy and machining of the semi-finished products, bearing washers for a thrust cylindrical roller bearing were produced. These washers showed a longer fatigue life than previously produced bearing washers with AISI 52100 bearing steel as cladding. It was also remarkable that the service life with the Rockit^® cladding material was longer than that of conventional monolithic AISI 52100 washers. This was reached through a favourable microstructure with finely distributed vanadium and chromium carbides in a martensitic matrix as well as the presence of compressive residual stresses, which are largely retained even after testing. The potential for further enhancement of the cladding performance through Tailored Forming was investigated in compression and forging tests and was found to be limited due to low forming capacity of the material.