Friction drilling is a widely used process to produce bushings in sheet materials, which are processed further by thread forming to create a connection port. Previous studies focused on the process parameters and did not pay detailed attention to the material flow of the bushing. In order to describe the material behaviour during a friction drilling process realistically, a detailed material characterisation was carried out. Temperature, strain rate, and rolling direction dependent tensile tests were performed. The results were used to parametrise the Johnson–Cook hardening and failure model. With the material data, numerical models of the friction drilling were created using the finite element method in 3D as well as 2D, and the finite volume method in 3D. Furthermore, friction drilling tests were carried out and analysed. The experimental results were compared with the numerical findings to evaluate which modelling method could describe the friction drilling process best. Highest imaging quality to reality was shown by the finite volume method in comparison to the experiments regarding the material flow and the geometry of the bushing.

This study focused on evaluating the mechanical, thermal, and morphological properties of recycled polyethylene terephthalate (RPET) hybrid mineral-filled composites containing fine acicular wollastonite, mica phlogopite, and talc platelets. Depending on the filler content, both single mineral-filled composites as well as hybrid mineral–filler composites were investigated. The maximum nominal filler content was set to 20% by weight with varying ratios for combinations of the wollastonite–mica and wollastonite–talc composites, respectively. Aside from the tensile, compression, and flexural properties, the heat distortion temperature and degree of crystallinity were carried out. Moreover, the dynamical response of the hybrid mineral-filled composites on different frequencies (1 Hz, 2 Hz, 5 Hz, and 10 Hz) was considered. By using scanning electron microscope photography, the fracture surface and the morphology of the composite material were observed. The results demonstrated enhanced stiffness, strengths, and thermal stability for all hybrid mineral-filled composites. In particular, the wollastonite–talc-filled RPET composites revealed a good compatibility and showed the most beneficial results.

The growing demand for individualized products is becoming more and more significant and leads to a reduction in batch sizes. In particular, the production of multi-material components for lightweight design presents new challenges to the manufacturing process. This is evident when it comes to the production of individual parts, as today’s processes are characterized by high tool costs and manual operations. The described challenge can be overcome by a robot-based manufacturing cell allowing the use of a novel, modular process chain in which metal parts are mechanically pre-treated, subsequently completed by additive plastic application, and afterwards finalized in a machining step to achieve the required surface qualities and geometries. In order to realize the novel process chain, robot-based solutions for free-form metal sheet processing, increased interlayer bonding strength of plastic, and multi-material machining with integrated chip extraction have to be found. Therefore, this paper presents the first approach of a robot-guided surface structuring end-effector and a concept for a direct extraction hood, which is able to be adapted specifically to the movement of the robot and the part surface, so free-form surfaces can be machined. Based on this, first experimental studies for increasing the interlayer bonding strength of plastic were carried out using an extruder set up to applicate thermoplastics onto metal at high deposition rates. To define the positioning accuracy for a robot-guided structuring process, different point to point movements have been investigated.