Different mechanical properties characterise the materials of 3D printed components, depending on the specific additive manufacturing (AM) process, its parameters, and the post-treatment adopted. Specifically, stereolithography (SLA) uses a photopolymerisation technique that creates solid components through selective solidification. In this study, 72 specimens were 3D printed using 12 commercial-grade methacrylate resins and tested under uniaxial tensile loads. The resin specimens were evaluated before and after curing. The recommended cure temperature and time were followed for all materials. The stress-strain curves measured during the testing campaign were evaluated in terms of maximum tensile strength, Young’s modulus, ductility, resilience, and toughness. The results reveal that the curing process increases the material stiffness and resistance to tensile loads. However, it was found that the curing process generally reduces the plasticity of the resins, causing a more or less marked brittle behaviour. This represents a potential limitation to the use of SLA 3D printing for structural elements which require some plasticity to avoid dangerous sudden failures.

Objective: This study reports on a new method for the development of multi-color and multi-material realistic Knee Joint anatomical models with unique features. In particular, the design of a fibers matrix structure that mimics the soft tissue anatomy. Methods: Various Computer-Aided Design (CAD) systems and the PolyJet 3D printing were used in the fabrication of three anatomical models wherein fibers matrix structure is mimicked: (i) Anterior cruciate ligament reconstruction (ACL-R) model used in the previous study. (ii) ACL-R model, incorporating orientations, directions, locations, and dimensions of the tunnels, as well as a custom-made surgical guide (SG) for avoiding graft tunnel length mismatch. (iii) Total knee arthroplasty (TKA) model, including custom-made implants. Before models 3D printing, uni-axial tensile tests were conducted to obtain the mechanical behaviors for individual No. 1 (A60-A50), No. 2 (A50-A50), No. 3 (A50-A40), and No. 4 (A70-A60) soft tissue-mimicking polymers. Each material combination represents different shore-hardness values between fiber and matrix respectively. Results: We correlated the pattern of stress-strain curves in the elastic region, stiffness, and elastic modulus of proposed combinations with published literature. Accordingly, material combinations No. 1 and No. 4 with elastic modules of 0.76-1.82 MPa were chosen for the soft tissues 3D printing. Finally, 3D printing Knee Joint models were tested manually simulating 50 flexo-extension cycles without presenting ruptures. Conclusion: The proposed anatomical models offer a diverse range of applications. These may be considered as an alternative to replacing cadaver specimens for medical training, pre-operative planning, research and education purposes, and predictive models validation. The soft tissue anatomy-mimicking materials are strong enough to withstand the stretching during the flexo-extension. The methodology reported for the design of the fiber-matrix structure might be considered as a start to develop new patterns and typologies that may mimic soft tissues.

Present and future anatomical models for biomedical applications will need bio-mimicking three-dimensional (3D)-printed tissues. These would enable, for example, the evaluation of the quality-performance of novel devices at an intermediate step between ex-vivo and in-vivo trials. Nowadays, PolyJet technology produces anatomical models with varying levels of realism and fidelity to replicate organic tissues. These include anatomical presets set with combinations of multiple materials, transitions, and colors that vary in hardness, flexibility, and density. This study aims to mechanically characterize multi-material specimens designed and fabricated to mimic various bio-inspired hierarchical structures targeted to mimic tendons and ligaments. A Stratasys^® J750™ 3D Printer was used, combining the Agilus30™ material at different hardness levels in the bio-mimicking configurations. Then, the mechanical properties of these different options were tested to evaluate their behavior under uni-axial tensile tests. Digital Image Correlation (DIC) was used to accurately quantify the specimens’ large strains in a non-contact fashion. A difference in the mechanical properties according to pattern type, proposed hardness combinations, and matrix-to-fiber ratio were evidenced. The specimens V, J1, A1, and C were selected as the best for every type of pattern. Specimens V were chosen as the leading combination since they exhibited the best balance of mechanical properties with the higher values of Modulus of elasticity (2.21 ± 0.17 MPa), maximum strain (1.86 ± 0.05 mm/mm), and tensile strength at break (2.11 ± 0.13 MPa). The approach demonstrates the versatility of PolyJet technology that enables core materials to be tailored based on specific needs. These findings will allow the development of more accurate and realistic computational and 3D printed soft tissue anatomical solutions mimicking something much closer to real tissues.

Stapling devices have emerged as a widespread and effective option for soft tissue surgery, offering promising outcomes for patients by reducing complication rates and surgery time. This review aims to provide an exhaustive analysis of commercially available alternatives in the market, incorporating insights from market analysis, patent landscape, and the existing literature. The main focus lies in identifying and evaluating the most widely adopted and innovative stapling devices, including linear, linear cutting, circular, and powered staplers. In addition, this review delves into the realm of bioabsorbable staples, exploring the materials utilized and the surgical fields where these advanced staples find applications. To facilitate easy comprehension, the gathered information is presented in tables, highlighting the essential parameters for each stapling device. This comprehensive research about stapling devices is intended to aid healthcare practitioners and researchers in making informed decisions when choosing the most appropriate instrument for specific surgical procedures.

Biocompatible and biodegradable polymers represent the future in the manufacturing of medical implantable solutions. As of today, these are generally manufactured with metallic components which cannot be naturally absorbed within the human body. This requires performing an additional surgical procedure to remove the remnants after complete rehabilitation or to leave the devices in situ indefinitely. Nevertheless, the biomaterials used for this purpose must satisfy well-defined mechanical requirements. These are difficult to ascertain at the design phase since they depend not only on their physicochemical properties but also on the specific manufacturing methods used for the target application. Therefore, this research was focused on establishing the effects of the manufacturing methods on both the mechanical properties and the thermal behavior of a medical-grade copolymer blend. Specifically, Injection and Compression Molding were considered. A Poly(L-lactide-co-D,L-lactide)/Poly(L-lactide-co-ε-caprolactone) blend was considered for this investigation, with a ratio of 50/50 (w/w), aimed at the manufacturing of implantable devices for tendon repair. Interesting results were obtained.

The present study aims to create a patient-specific hand model to simulate the passive rehabilitation on the index finger, quantifying the flexor digitorum profundus (FDP) tendon excursion and the stress experienced during simulated flexion. The computational model used in this analysis was created from an unknown patient dataset available in the Embodi3d online library. The segmentation, three-dimensional reconstruction, and modeling of the structures involved were performed using Materialise Mimics and Rhino3D. The FDP tendon excursion and stress values present in the model were calculated in the ANSYS environment. Based on the finite-element simulation, the FDP tendon presents an excursion of 10.1 mm during passive postoperative flexion. The highest-stress values were observed between the pulleys-FDP tendon contact surfaces. In particular, the pulley A1 exhibited the maximum principal stress of the model with a 58.7 MPa. The pulley A3 showed the same stress distribution pattern that A1 Pulley, but with the lowest values. The FDP Tendon excursion obtained is consistent with the results reported in the literature, which vary from 8 to 11 mm. The stress values found in the model explain the importance of the pulley mechanism keeping the FDP tendon attached to the finger bone during the range of motion experienced. The silico model proposed may potentially be used in the assessment of new medical device proposals in the field of hand reconstructive surgery.