The waste fly ash (FA) material was subjected to chemical treatment with HCl at elevated temperature for a different time to modify its porosity. Modified FA particles with highest surface area and pore volume were further used as a support for TiO ₂ catalyst during FA/TiO ₂ nanocomposite preparation. The nanocomposite photocatalysts were obtained by in situ sol–gel synthesis of titanium dioxide in the presence of FA particles. To perform accurate characterization of modified FA and FA/TiO ₂ nanocomposite photocatalysts, gas adsorption-desorption analysis, X-ray diffraction, scanning electron microscopy, UV/Vis and Infrared spectroscopy were used. Efficiency evaluation of the synthesized FA/TiO ₂ nanocomposites was performed by following the removal of Reactive Red 45 (RR45) azo dye during photocatalytic treatment under the UV-A irradiation. Photocatalysis has been carried out up to five cycles with the same catalysts to investigate their stability and the possible reuse. The FA/TiO ₂ photocatalyst showed very good photocatalytic activity and stability even after the fifth cycles. The obtained results show that successfully modified waste fly ash can be used as very good TiO ₂ support.

Microplastics (MPs) are detected in the water, sediments, as well as biota, mainly as a consequence of the degradation of plastic products/waste under environmental conditions. Due to their potentially harmful effects on ecosystems and organisms, MPs are regarded as emerging pollutants. The highly problematic aspect of MPs is their interaction with organic and inorganic pollutants; MPs can act as vectors for their further transport in the environment. The objective of this study was to investigate the effects of ageing on the changes in physicochemical properties and size distribution of polyethylene terephthalate (PET), as well as to investigate the adsorption capacity of pristine and aged PET MPs, using pharmaceutical diclofenac (DCF) as a model organic pollutant. An ecotoxicity assessment of such samples was performed. Characterization of the PET samples (bottles and films) was carried out to detect the thermooxidative aging effects. The influence of the temperature and MP dosage on the extent of adsorption of DCF was elucidated by employing an empirical modeling approach using the response surface methodology (RSM). Aquatic toxicity was investigated by examining the green microalgae Pseudokirchneriella subcapitata. It was found that the thermooxidative ageing process resulted in mild surface changes in PET MPs, which were reflected in changes in hydrophobicity, the amount of amorphous phase, and the particle size distribution. The fractions of the particle size distribution in the range 100–500 μm for aged PET are higher due to the increase in amorphous phase. The proposed mechanisms of interactions between DCF and PET MPs are hydrophobic and π–π interactions as well as hydrogen bonding. RSM revealed that the adsorption favors low temperatures and low dosages of MP. The combination of MPs and DCF exhibited higher toxicity than the individual components.

This article reports a study of flame retardancy and thermal and mechanical properties of wood-plastic composites (WPCs) based on high-density polyethylene and pine flour. The study shows that sample composition plays an important role in WPCs' properties. The influence of additives like fillers (SiO₂ or CaCO₃) and flame retardants ammonium polyphosphate (APP) and pentaerythritol (PER) on WPCs' properties has been considered. The best properties are shown in samples using SiO₂ as filler and treated with the intumescent fire retardant APP/PER. Such samples have excellent fire retardancy with V-0 rating (UL-94 test) and imply that APP/PER fire retardant ensures effective fire retardancy for WPCs.

Pyrolysis is gaining more significance as a technology used to produce alternative fuels and chemicals. This study dealt with the catalytic pyrolysis of a realistic waste mixture of multi-layered plastic food packaging. The thermal behavior, kinetic parameters, and kinetic model of multi-layered plastic food packaging pyrolysis were determined to show its potential for process scale-up. In particular, we aimed to evaluate the effect of a ZSM-5 zeolite catalyst, modified with iron(III) oxide. The pyrolysis process on this decagonal structure was investigated using thermogravimetric analysis under nitrogen flow at four heating rates ranging between 40 and 600 °C. The kinetic study was conducted using the model-free isoconversional Friedman method as well as advanced statistical analysis to determine the reaction mechanism of the process. The thermal decomposition occurred in the range of 350–510 °C, with a mass loss greater than 90%. The kinetic study revealed a complex pyrolysis process, which consisted of three decomposition stages, diffusion, and Avrami-Erofeev reaction types. The activation energy values determined by the Friedman method rose with the degree of conversion, from 127 kJ mol⁻¹ at 0.01 to 219 kJ mol⁻¹ at 0.95. The doping of the catalyst lowered the activation energy of the reaction by 44% and 8% in the first and second stages, respectively, and increased the acidity of the zeolites, thus enhancing the reactivity on the surface of the catalysts. Lower activation energy meant less energy was required to heat the pyrolysis reactor since the onset temperature of sample decomposition was reduced.